Repeelable water-dispersible acrylic pressure-sensitive adhesive composition and pressure-sensitive adhesive sheet

一种丙烯酸、分散型的技术，应用在酸性共聚物粘合剂、非高分子粘合剂添加剂、粘合剂类型等方向，能够解决易造成污染等问题，达到低污染性优良、优良再剥离性的效果

Inactive Publication Date: 2016-11-09
NITTO DENKO CORP
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Especially for water-dispersed acrylic adhesives, the emulsifier, which is one of the components, tends to segregate to the interface in the adhesive layer, so there is a problem that it transfers to the surface of the adherend and easily causes contamination.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Repeelable water-dispersible acrylic pressure-sensitive adhesive composition and pressure-sensitive adhesive sheet
  • Repeelable water-dispersible acrylic pressure-sensitive adhesive composition and pressure-sensitive adhesive sheet
  • Repeelable water-dispersible acrylic pressure-sensitive adhesive composition and pressure-sensitive adhesive sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0223] (Preparation of Acrylic Emulsion Polymer (A))

[0224] Mix 90 parts by weight of water and raw material monomers and reactive surfactants (reactive surfactants that do not contain oxyalkylene groups) in the amount shown in Table 1 in the container, then stir and mix with a high-speed mixer, Prepare monomer emulsion.

[0225] Then, 50 parts by weight of water, 0.01 part by weight of a polymerization initiator (ammonium persulfate) and 10 wt. amount, emulsion polymerization was carried out at 75° C. for 1 hour while stirring. Then, 0.07 parts by weight of a polymerization initiator (ammonium persulfate) was further added, and the remaining whole monomer emulsion (an amount corresponding to 90% by weight) was added over 3 hours while stirring, and reacted at 75° C. for 3 hours. Then, it was cooled to 30° C., and adjusted to pH 8 by adding ammonia water at a concentration of 10% by weight to prepare an aqueous dispersion of an acrylic emulsion polymer (concentration of th...

Embodiment 2～20、 comparative example 1～8

[0231] As shown in Tables 1, 2, and 3, by changing the type and compounding amount of the raw material monomers, reactive surfactants, and the compounding amount of the surfactant (D), the re-peeling water-dispersible acrylic acid was obtained in the same manner as in Example 1. Adhesive-like composition and adhesive sheet.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface tensionaaaaaaaaaa
surface tensionaaaaaaaaaa
roughnessaaaaaaaaaa
Login to View More

Abstract

The present invention provides an acrylic water-dispersible pressure-sensitive adhesive composition that can prepare a removable adhesive layer having low contamination of an adherent. The acrylic water-dispersible pressure-sensitive removable adhesive composition according to the present invention comprises an acrylic emulsion polymer (A) comprising an alkyl (meth)acrylate ester and a carboxyl group-containing unsaturated monomer as essential raw material constitutive monomers and prepared by polymerization with a reactive surfactant containing no oxyalkylene group.

Description

technical field [0001] The present invention relates to a water-dispersible acrylic adhesive composition capable of forming a repeelable adhesive layer. Moreover, this invention relates to the PSA sheet which has the PSA layer formed from this PSA composition. Background technique [0002] In the manufacturing and processing of optical members (optical materials) such as polarizing plates, retardation plates, and anti-reflection films, for the purpose of preventing surface scratches and stains, improving cutting processability, and suppressing cracks, etc., A surface protection film is pasted on the surface of the optical member (see Patent Documents 1 and 2). As these surface protection films, a re-peelable pressure-sensitive adhesive sheet provided with a re-peelable pressure-sensitive adhesive layer on the surface of a plastic film substrate is generally used. [0003] Conventionally, solvent-based acrylic adhesives have been used as adhesives for these surface protecti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J133/06C09J7/02C09J11/06C09J133/02
CPCC08L2201/54C08L2312/00C09J7/385C09J133/02C09J133/08Y10T428/2848Y10T428/2891C08F220/1808C08F220/14C08F220/06B32B27/30C09J11/02C09J11/06C09J133/06
Inventor 高岛杏子三井数马森本有天野立巳米崎幸介
Owner NITTO DENKO CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com