Lithium ion battery electrolyte solution
A lithium-ion battery, electrolyte technology, applied in secondary batteries, organic electrolytes, non-aqueous electrolytes, etc., can solve the problems of low temperature performance of lithium batteries, and achieve high voltage resistance performance, high thermal decomposition temperature, and electrical conductivity. high effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0023] Example 1
[0024] The production of lithium ion battery positive sheet: the active material lithium nickel cobalt manganese oxide LiNi 0.5 Co 0.2 Mn 0.3 O 2 , Conductive agent Super-P and binder PVDF are dispersed into N-methyl-2-pyrrolidone in a mass ratio of 92:4:4, and stirred evenly to obtain positive electrode slurry. The slurry is evenly coated on both sides of the current collector aluminum foil, dried, cold pressed, striped, then vacuum dried, and the tabs are welded to form a lithium ion battery positive sheet that meets the requirements.
[0025] Production of lithium ion battery negative sheet:
[0026] Add the active material natural graphite, the conductive agent Super-P, the binder styrene butadiene rubber SBR, and the binder sodium carboxymethyl cellulose CMC into the solvent deionized water at a mass ratio of 96:1.5:1.5:1, and stir evenly to obtain Negative slurry. The slurry is evenly coated on both sides of the current collector copper foil, dried, cold pr...
Example Embodiment
[0031] Example 2
[0032] A lithium ion battery made by the same method as in Example 1. The solvent in the electrolyte is ethylene carbonate (EC), γ-butyrolactone (GBL), and ethyl methyl carbonate (EMC) in a mass ratio of 1:1:3. The lithium salt is lithium difluorooxalate (LiDFOB), The concentration is 0,9mol / L.
Example Embodiment
[0033] Example 3
[0034] A lithium ion battery made by the same method as in Example 1. The solvent in the electrolyte is ethylene carbonate (EC), gamma-butyrolactone (GBL), dimethyl carbonate (DMC), ethyl methyl carbonate (EMC) mixed in a mass ratio of 1:1:1.5:1.5, lithium salt It is lithium difluorooxalate borate (LiDFOB) with a concentration of 1mol / L.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap