Ceramic brick with color-changing enamel layer, green body structure and production method of ceramic brick

A production method and technology for ceramic tiles, applied in building construction, covering/lining, construction, etc., can solve problems such as unrealism and lingering effects, and achieve the effects of easier cleaning, brighter colors, and good practicability

Active Publication Date: 2015-07-08
FOSHAN SANSHUI NEW PEARL CONSTR CERAMICS IND +2
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limitation of production technology, the tiles with color-changing glaze layer in the past were all realized through printing and mold effects. It feels unreal, but the three-dimensional color-changing glaze buried in the middle of the glaze layer has not been able to make a breakthrough in technology.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic brick with color-changing enamel layer, green body structure and production method of ceramic brick
  • Ceramic brick with color-changing enamel layer, green body structure and production method of ceramic brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] As shown in the accompanying drawings, a production method for ceramic tiles with changing glaze layers, the structure of the green ceramic tiles is composed of a bottom body 1, a bottom glaze 2, a colored particle layer 3 and a transparent surface glaze layer 4.

[0046] The colored granules in the colored granule layer are pre-calcined from regenerated raw ore, and the particle size is preferably between 12 mesh and 40 mesh sieve. The weight ratio of raw materials is: 20% potassium feldspar; 10% quartz; 10% zinc oxide; 5% lithium carbonate; 2% chromium carbonate; 10% titanium oxide; 1% manganese oxide; 20% kaolin; 17% barium carbonate; Copper acetate 5%.

[0047] The water content of the bottom body powder accounts for 6.5% of the mass of the body powder, and the fineness of the body powder is 1.0% over a 250-mesh sieve; the fineness of the transparent glaze slurry in the transparent surface glaze layer is 0.6% over a 325-mesh sieve .

[0048] The powder of the bott...

Embodiment 2

[0050] As shown in the accompanying drawing, a production method of ceramic tiles with changing color glaze layer, the structure of the green ceramic tile is composed of bottom body 1, bottom glaze 2, colored particle layer 3 and transparent surface glaze layer 4.

[0051]The colored granules in the colored granule layer are pre-calcined from regenerated raw ore, and the particle size is preferably between 12 mesh and 40 mesh sieve. The weight ratio of raw materials is: potassium feldspar 15%; quartz 15%; zinc oxide 10%; lithium carbonate 4%; chromium carbonate 2%; titanium oxide 11%; manganese oxide 3%; kaolin 20%; barium carbonate 17%; Copper acetate 3%.

[0052] The water content of the bottom body powder accounts for 8.5% of the mass of the body powder, and the fineness of the body powder is 0.8% over a 250-mesh sieve; the fineness of the transparent glaze slurry in the transparent surface glaze layer is 0.4% over a 325-mesh sieve %.

[0053] The powder of the bottom bla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a ceramic brick with a color-changing enamel layer, a green body structure and a production method of the ceramic brick. A decorative layer is arranged above a bottom blank and comprises a transparent cover coat, a ground coat and colored burst particles which are fused together. The transparent cover coat, the ground coat and the colored burst particles are mingled and permeated to each other. The colored burst particles are below the transparent cover coat, the ground coat permeates upwards from the bottom among gaps of the colored burst particles, the topmost of the decorative layer is the transparent cover coat, the bottom of the decorative layer is the ground coat, and the ground coat is connected with the bottom blank. The outer surface of the transparent cover coat above the ceramic brick is an uneven structure with a sharp corner angle and is a structure with a concave-convex structure and smooth handfeel.

Description

technical field [0001] The invention relates to a building ceramic decoration material and a production method thereof. Background technique [0002] With the improvement of people's living standards, architectural decoration pays more and more attention to personalization. The glaze layer with changing colors has become a decorative material admired by people because of its luxurious decorative effect. It has long been the core subject of research in the ceramic industry. However, due to the limitation of production technology, the tiles with color-changing glaze layer in the past were all realized through printing and mold effects. It feels unreal, but the three-dimensional color-changing glaze buried in the middle of the glaze layer has not been able to make a breakthrough in technology. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a ceramic tile with a color-changing glaze layer, a green body structure a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/89C04B41/86E04F13/077
Inventor 叶德林韦前黄春林朱光耀
Owner FOSHAN SANSHUI NEW PEARL CONSTR CERAMICS IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com