Preparation method of illite-smectite clay intercalated silica dual composite natural rubber

A technology of silica and natural rubber, which is applied in the field of preparation of multiphase composite natural rubber, can solve the problems of lower performance such as inferior carbon black, tear strength and elasticity, and low tensile strength of filled rubber, so as to reduce production capacity consumption effect

Inactive Publication Date: 2014-08-20
陈雄
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Moreover, when its microscopic polycrystalline silicate sheet is combined with rubber, it can bring certain reinforcing properties to the mixed colloid, but if Imon clay is used alone, the effect of reinforcing rubber is not as good as that of carbon black and white carbon. Black, and after the filling number of Emon clay in the rubber syst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] Recipe Components:

[0065] Component

Mass content%

natural rubber

73.5

Silica

22.1

Emon Clay

3.7

Intercalant

0.4

Emulsifier

0.1

stabilizer

0.2

[0066] The present invention adopts the fresh latex harvested in the forest on the same day.

[0067] Preparation of Imon clay slurry

[0068] Weigh 200g of Yimeng clay raw ore, manually crush it to a powder material with a diameter of less than or equal to 3mm, put it into 800ml tap water and soak for 16 hours, until the Yimeng clay ore is completely dissolved, stir it evenly by mechanical stirring, and Complete the 325# sieve filtration, and the filtrate is controlled to have a solid content of 15% by adjusting the moisture content. After the filtrate was allowed to stand for 10 minutes, the supernatant suspension was taken out, and after adjusting the concentration to 5%, 200ml was weighed into a beaker, 1g of dimethylformamide was add...

Embodiment 2

[0078] Recipe Components:

[0079] Component

Mass content%

natural rubber

56.7

Silica

34.0

Emon Clay

8.5

Intercalant

0.3

Emulsifier

0.2

stabilizer

0.3

[0080] The present invention adopts the fresh latex harvested in the forest on the same day.

[0081] Preparation of Imon clay slurry

[0082] Weigh 200g of Yimeng clay raw ore, manually crush it to a powder material with a diameter of less than or equal to 3mm, put it into 800ml tap water and soak for 16 hours, until the Yimeng clay ore is completely dissolved, stir it evenly by mechanical stirring, and Complete the 325# sieve filtration, and the filtrate is 15% by adjusting the moisture control solid content. After the filtrate was allowed to stand for 10 minutes, the supernatant suspension was taken out, and after adjusting the concentration to 5%, 200ml was weighed into a beaker, 1g of dimethylformamide was added and stirred at 70°C f...

Embodiment 3

[0094] Recipe Components:

[0095] Component

Mass content%

natural rubber

67.2

Silica

28.9

Emon Clay

3.4

Intercalant

0.2

Emulsifier

0.1

stabilizer

0.2

[0096] The present invention adopts the fresh latex harvested in the forest on the same day.

[0097] Preparation of Imon clay slurry

[0098] Weigh 200g of Yimeng clay raw ore, manually crush it to a powder material with a diameter of less than or equal to 3mm, put it into 800ml tap water and soak for 16 hours, and wait until the Yimeng clay ore is completely dissolved, stir it evenly by mechanical stirring, and Complete the 325# sieve filtration, and the filtrate is 15% by adjusting the moisture control solid content. After the filtrate was allowed to stand for 10 minutes, the supernatant suspension was taken out, and after the concentration was adjusted to 5%, 200ml was weighed into a beaker, 0.5g of dimethylformamide was added and sti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method for preparing dual composite natural rubber from illite-smectite clay intercalated silica. The method mainly comprises the steps of processing a nano-scale illite-smectite clay material by adopting an intercalating agent, further damaging a close and ordered packed structure of laminar silicate to form layered basic units by peeling, then mixing and melting with a suspension mixed with natural latex and silica, uniformly dispersing in a polymer matrix, finally realizing intercalation composition of a natural rubber high polymer, silica and layered silicate lamellae on nano scale and completing the manufacturing of a finished product through continuous production.

Description

technical field [0001] The invention relates to a method for preparing multiphase composite natural rubber in the field of rubber, in particular to a method for intercalation modification of Imon clay and double compound filling of natural rubber with inorganic filler. Background technique [0002] Natural rubber is a rubber strain widely used in the rubber field. It is different from the downstream products of petroleum refining such as butadiene rubber and styrene-butadiene rubber. Natural rubber comes from natural plant extraction. It has the advantages of green resources. When natural rubber is applied in downstream product enterprises (such as tire industry, etc.), it is necessary to add reinforcing materials such as carbon black and white carbon black to improve the strength of rubber products and reduce costs. Among them, white carbon with silica as the main component After being filled with rubber, black has the functions of reducing tire rolling resistance, heat ge...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/02C08K9/04C08K3/34C08K3/36
Inventor 陈雄
Owner 陈雄
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap