Bismuth tungstate modified magnetic separation hollow composite photocatalyst and preparation method thereof

A technology of magnetic separation and bismuth tungstate, applied in chemical instruments and methods, physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, etc., can solve the problems of unsatisfactory catalytic effects of photocatalysts, and achieve Effects of promoting application potential, high preparation efficiency, and mild reaction conditions

Active Publication Date: 2016-08-17
陕西万华环境工程有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a bismuth tungstate-modified magnetic separation hollow composite photocatalyst, which solves the problem that the catalytic effect of the existing two-phase composite heterojunction photocatalyst is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bismuth tungstate modified magnetic separation hollow composite photocatalyst and preparation method thereof
  • Bismuth tungstate modified magnetic separation hollow composite photocatalyst and preparation method thereof
  • Bismuth tungstate modified magnetic separation hollow composite photocatalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The preparation method of the above bismuth tungstate modified magnetic separation hollow composite photocatalyst, the specific preparation steps are as follows:

[0032] Step 1, adopting traditional hydrothermal reaction to prepare phenolic resin microspheres;

[0033] The preparation volume ratio is 1:(10~100):(59~179) ammoniacal liquor, the mixed solution of ethanol and water, wherein the concentration of ammoniacal liquor is 25%; Resorcinol and concentration are 37% formalin solution Add the above mixed solution, place it in a water bath at 10-60°C and stir for 10 hours, wherein the mass volume ratio of resorcinol and mixed solution is 1: (70-280) g / ml, formalin solution and mixed solution The volume ratio of the solution is 1: (50-200); transfer the solution to a hydrothermal kettle, and keep it at 100°C for 24h; after natural cooling, wash it with absolute ethanol and deionized water three times, and then dry it at 50°C for 24h , to obtain phenolic resin microsph...

Embodiment 1

[0038] Step 1, mix 59mL of deionized water, 10mL of ethanol and 1mL of 25% ammonia solution, place in a water bath at 15°C, then add 0.25g of resorcinol and 0.35mL of formaldehyde solution, stir in the water bath for 10h, then put The solution was transferred to a hydrothermal kettle and kept at 100°C for 24 hours; after natural cooling, it was rinsed three times with absolute ethanol and deionized water, and then dried at 50°C for 24 hours to obtain phenolic resin microspheres;

[0039] Step 2, mix 10mL of zinc nitrate solution with a concentration of 0.01mol / L and 21mL of ferric nitrate solution with a concentration of 0.01mol / L to form a mixed solution A, disperse 0.155g of phenolic resin microspheres into the mixed solution A, and process 15min, after aging for 3 hours, washed with water and centrifuged for 3 times, then dried in a vacuum oven at 50°C for 24h, and the obtained product was 2 Calcined in medium, slowly heated to 350 °C and kept for 1 h, then cooled naturally...

Embodiment 2

[0042] Step 1, mix 179mL of deionized water, 100mL of ethanol and 1mL of 25% aqueous ammonia solution, place in a water bath at 60°C, then add 4g of resorcinol and 5.6mL of formaldehyde solution, stir in the water bath for 10h, and then mix the The solution was transferred to a hydrothermal kettle and kept at 100°C for 24 hours; after natural cooling, it was rinsed three times with absolute ethanol and deionized water, and then dried at 50°C for 24 hours to obtain phenolic resin microspheres;

[0043] Step 2: Mix 10mL of zinc chloride solution with a concentration of 4mol / L and 40mL of ferric chloride solution with a concentration of 4mol / L to form a mixed solution A, disperse 5g of phenolic resin microspheres into the mixed solution A, and ultrasonically treat for 15min , aged for 3 hours, washed with water and centrifuged for 3 times, then dried in a vacuum oven at 50°C for 24 hours, and the obtained product was placed in N 2 Calcined in medium, slowly heated to 1000 °C and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a bismuth tungstate modified magnetic separation hollow composite photocatalyst, which is composed of ZnFe 2 o 4 , Fe 2 o 3 and Bi 2 WO 6 Composite; the particle size of the hollow microspheres is 50-1000nm, and the thickness of the hollow shell is 1-100nm. The invention also discloses its preparation method: preparing phenolic resin microspheres by hydrothermal reaction; adding them into the mixed solution of iron salt and zinc salt for ultrasonication, aging and calcining to obtain C@ZnFe 2 o 4 ‑Fe 2 o 3 microspheres; the C@ZnFe 2 o 4 ‑Fe 2 o 3 Microspheres soaked in Bi(NO 3 ) 3 and Na 2 WO 4 It can be obtained by ultrasonication, aging and calcination in mixed ethylene glycol solution. The photocatalyst of the present invention can efficiently photocatalyze and degrade toxic and harmful substances under sunlight and ultraviolet light, and the degradation rate is close to 100%, and ZnFe 2 o 4 It has magnetism, is easy to separate and recover, and has a simple preparation method.

Description

technical field [0001] The invention belongs to the technical field of photocatalysts, and in particular relates to a bismuth tungstate modified magnetic separation hollow composite photocatalyst, and also relates to a preparation method of the composite photocatalyst. Background technique [0002] The treatment of environmental pollution is one of the major problems that human beings are facing urgently today. The purification of environmental pollution by photocatalytic oxidation has attracted much attention due to its advantages of low energy consumption, mild purification conditions, no secondary pollution, and deep oxidation. Among them, the composition and morphology design of photocatalysts are at the core of this technology and the key to the efficiency of photocatalytic oxidation. Compared with traditional powder photocatalysts, hollow nano photocatalysts have small size, large surface volume fraction, different chemical bond states and electronic states on the surf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/888
Inventor 李军奇刘振兴刘辉何选盟朱振峰
Owner 陕西万华环境工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com