Polypyrrole-PEDOT/Fe3O4 compound and preparation method thereof

A technology of dioxyethylene thiophene and composites, applied in the direction of ferrous oxide, iron oxide/iron hydroxide, etc., can solve the problems of uneven dispersion and complexity of magnetic particles

Inactive Publication Date: 2014-11-12
OCEAN UNIV OF CHINA
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the two-step synthesis method adopted by Xiong Dongbai et al. is relatively complicated, and the magnetic particles are not uniformly dispersed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypyrrole-PEDOT/Fe3O4 compound and preparation method thereof
  • Polypyrrole-PEDOT/Fe3O4 compound and preparation method thereof
  • Polypyrrole-PEDOT/Fe3O4 compound and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0073] Embodiment 1: poly(pyrrole-dioxyethylenethiophene) / Fe of the present invention 3 o 4 Preparation of complex

[0074] The implementation steps of this embodiment are as follows:

[0075] A. Preparation of white emulsion

[0076] According to the molar ratio of pyrrole and dioxyethylene thiophene 1:1.2, add pyrrole and dioxyethylene thiophene to 80ml of ammonia solution with a concentration of 1.4mol / L, mix well, and use ultrasound The ultrasonic equipment sold by the cleaning machine, the obtained mixture is subjected to ultrasonic treatment for 3 minutes under the conditions of 20KHz. and power 80w, and a white emulsion is obtained;

[0077] B. Add ferrous chloride

[0078] At a temperature of 32°C, according to FeCl 2 4H 2 The molar ratio of O to pyrrole is 1:2.0, add 1.0mol / LFeCl to the white emulsion obtained in step A 2 4H 2 O aqueous solution, obtains the solution containing ferrous chloride;

[0079] C. Add ferric chloride

[0080] According to FeCl 2 ....

Embodiment 2

[0088] Embodiment 2: poly(pyrrole-dioxyethylenethiophene) / Fe of the present invention 3 o 4 Preparation of complex

[0089] The implementation steps of this embodiment are as follows:

[0090] A. Preparation of white emulsion

[0091] According to the molar ratio of pyrrole and dioxyethylene thiophene 1:0.4, add pyrrole and dioxyethylene thiophene to 100ml of ammonia solution with a concentration of 1.0mol / L, mix well, and use Gowell Technology Co., Ltd. to use ultrasonic cleaning under the trade name Ultrasonic equipment sold by the machine, the obtained mixture was subjected to ultrasonic treatment for 2 minutes under the conditions of 25KHz and power 120w, and a white emulsion was obtained;

[0092] B. Add ferrous chloride

[0093] At a temperature of 20°C, according to FeCl 2 4H 2 The molar ratio of O to pyrrole is 1:1.3, add 0.3mol / LFeCl to the white emulsion obtained in step A 2 4H 2 O aqueous solution, obtains the solution containing ferrous chloride;

[0094] ...

Embodiment 3

[0099] Embodiment 3: Poly(pyrrole-dioxyethylenethiophene) / Fe of the present invention 3 o 4 Preparation of complex

[0100] The implementation steps of this embodiment are as follows:

[0101] A. Preparation of white emulsion

[0102] According to the molar ratio of pyrrole and dioxyethylene thiophene 1:0.8, add pyrrole and dioxyethylene thiophene to 90ml of ammonia solution with a concentration of 1.2mol / L, mix well, and use ultrasonic The ultrasonic equipment sold by the cleaning machine, the obtained mixture is subjected to ultrasonic treatment for 3 minutes under the condition of 30KHz. and power 120w, and a white emulsion is obtained;

[0103] B. Add ferrous chloride

[0104] At a temperature of 28°C, according to FeCl 2 4H 2 The molar ratio of O to pyrrole is 1:1.5, add 0.8mol / LFeCl to the white emulsion obtained in step A 2 4H 2 O aqueous solution, obtains the solution containing ferrous chloride;

[0105] C. Add ferric chloride

[0106] According to FeCl 2 ....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a Polypyrrole-PEDOT / Fe3O4 compound with the characteristic of microwave absorption and a preparation method of the Polypyrrole-PEDOT / Fe3O4 compound. The preparation method includes the steps of preparing white emulsion, adding ferrous chloride, adding ferric chloride, carrying out washing and drying, and the like. The absorption frequency band of the compound prepared according to the method can be adjusted by changing the thickness of the compound, the microwave absorption frequency band is obviously broadened, and good wave absorption performance is achieved. In the preparation process, electromagnetic parameters can be adjusted by changing temperature and the use number of oxidizing agents, and the method is of great significance in broadening the microwave absorption frequency band of the compound and preparing novel wave absorption materials.

Description

【Technical field】 [0001] The invention belongs to the technical field of novel wave-absorbing materials. More specifically, the present invention relates to a poly(pyrrole-dioxyethylenethiophene) / Fe 3 o 4 complexes, also involving poly(pyrrole-dioxyethylenethiophene) / Fe 3 o 4 Method for the preparation of the complex. 【Background technique】 [0002] Microwave material refers to a material that can absorb and attenuate incident electromagnetic waves, and convert its electromagnetic energy into heat energy to dissipate or make electromagnetic waves disappear due to interference. Absorbing materials were first used for military purposes and were called "stealth materials". Research on microwave materials in civilian applications such as television broadcasting, electronic devices, and microwave radiation protection has also received increasing attention. Absorbing materials are divided into traditional absorbing materials and new absorbing materials. New absorbing materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L65/00C08K3/22C08G61/12C08G73/06C01G49/08
Inventor 张志明于甜甜于良民姜晓辉赵海洲李昌诚闫雪峰李霞董磊
Owner OCEAN UNIV OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap