Anti-abrasion and flame-retardant modified natural rubber

A natural rubber and modified technology, applied in the rubber field to achieve the effect of promoting the degree of cross-linking, improving the vulcanization efficiency, and enhancing the wear resistance and elasticity

Inactive Publication Date: 2014-12-10
ANHUI ELECTRIC GRP SHARES
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In production, the modified method is generally used to further process natural rubber to make up for the shortcomings of high cost and poor physical and mechanical properties of natural rubber; at the same time, due

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A kind of wear-resisting flame-retardant modified natural rubber that the present invention proposes, its raw material comprises by weight: 78 parts of natural rubber, 30 parts of butyl rubber, 12 parts of acrylonitrile-butadiene-styrene copolymer ABS, jute fiber 10 parts, 2 parts of 1,1-bis(di-tert-butylperoxy)-3,3,5-trimethylcyclohexane, 0.8 parts of sulfur powder, 1.1 parts of zinc acrylate, 17 parts of modified graphene, 26 parts of talcum powder, 30 parts of diatomaceous earth, 5 parts of high wear-resistant carbon black, 35 parts of flame retardant system, 6 parts of trioctyl trimellitate TOTM, 9 parts of epoxy cocklebur oleate, antioxidant 22641.8 1.8 parts, anti-aging agent MBZ 1.8 parts, wherein the flame retardant system is composed of 55wt% magnesium hydroxide, 15wt% melamine cyanurate and 30wt% microencapsulated red phosphorus, propylene in acrylonitrile-butadiene-styrene copolymer ABS The weight percent of nitrile is 25wt%, the weight percent of butadiene i...

Embodiment 2

[0016] A kind of wear-resisting flame-retardant modified natural rubber that the present invention proposes, its raw material comprises by weight: 80 parts of natural rubber, 27 parts of butyl rubber, 14 parts of acrylonitrile-butadiene-styrene copolymer ABS, jute fiber 8 parts, 2.6 parts of 1,1-bis(di-tert-butylperoxy)-3,3,5-trimethylcyclohexane, 0.6 parts of sulfur powder, 1.3 parts of zinc acrylate, 15 parts of modified graphene, 28 parts of talcum powder, 28 parts of diatomaceous earth, 7 parts of high wear-resistant carbon black, 33 parts of flame retardant system, 7.2 parts of trioctyl trimellitate TOTM, 7 parts of epoxy cocklebur oleate, antioxidant 22642.3 1.5 parts, anti-aging agent MBZ 1.5 parts, wherein the flame retardant system is composed of 62wt% magnesium hydroxide, 12wt% melamine cyanurate and 26wt% microencapsulated red phosphorus, propylene in acrylonitrile-butadiene-styrene copolymer ABS The weight percent of nitrile is 26wt%, and the weight percent of buta...

Embodiment 3

[0019] A kind of wear-resisting and flame-retardant modified natural rubber proposed by the present invention, its raw material comprises by weight: 82 parts of natural rubber, 26 parts of butyl rubber, 15 parts of acrylonitrile-butadiene-styrene copolymer ABS, jute fiber 7 parts, 3 parts of 1,1-bis(di-tert-butylperoxy)-3,3,5-trimethylcyclohexane, 0.5 parts of sulfur powder, 1.4 parts of zinc acrylate, 14 parts of modified graphene, 29 parts of talcum powder, 27 parts of diatomaceous earth, 8 parts of high wear-resistant carbon black, 32 parts of flame retardant system, 8 parts of trioctyl trimellitate TOTM, 6 parts of epoxy cocklebur oleate, antioxidant 22642.5 1.2 parts, anti-aging agent MBZ 1.2 parts, wherein the flame retardant system is composed of 65wt% magnesium hydroxide, 10wt% melamine cyanurate and 25wt% microencapsulated red phosphorus, propylene in acrylonitrile-butadiene-styrene copolymer ABS The weight percent of nitrile is 27wt%, the weight percent of butadiene ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses anti-abrasion and flame-retardant modified natural rubber which comprises the raw materials in parts by weight: 78-82 parts of natural rubber, 26-30 parts of butyl rubber, 12-15 parts of acrylonitrile-butadiene-styrene copolymer, 7-10 parts of jute fibers, 2-3 parts of 1,1-di(di-tert-peroxo)-3,3,5-trimethyl-cyclohexane, 0.5-0.8 part of sulfur, 1.1-1.4 parts of zinc acrylate copolymer, 14-17 parts of modified graphene, 26-29 parts of talcum powder, 27-30 parts of kieselguhr, 5-8 parts of high-abrasion-resistance carbon black, 32-35 parts of a flame-retardant system, 6-8 parts of trioctyl trimellitate TOTM, 6-9 parts of epoxy siberian cocklebur butyl oleate, 1.8-2.5 parts of an anti-ageing agent 2264 and 1.2-1.8 parts of an anti-ageing agent MBZ. The anti-abrasion and flame-retardant modified natural rubber is excellent in abrasion resistance, tearing resistance and flame retardancy, and is perfect in elasticity, ageing resistance and heat resistance performance.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to a wear-resistant and flame-retardant modified natural rubber. Background technique [0002] Natural rubber is obtained from the white latex of specific plants in tropical climate areas. It is an important industrial material and is widely used in transportation, industrial equipment, medical equipment, construction and other fields. In production, natural rubber is generally further processed by modified methods to make up for the shortcomings of high cost and poor physical and mechanical properties of natural rubber; at the same time, due to the rapid development of industry, the flame retardancy and wear resistance of rubber materials are required. Therefore, it is imperative to develop a rubber material with good wear resistance and flame retardancy. Contents of the invention [0003] The technical problems in the basic background technology, the present invention proposes a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/00C08L23/22C08L55/02C08L97/02C08K13/06C08K9/04C08K3/04C08K5/14C08K3/06C08K5/098C08K3/34C08K5/12C08K9/10C08K3/02
Inventor 郑有松黄海琴朱家俊吴松如徐国锋
Owner ANHUI ELECTRIC GRP SHARES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap