Nano fire-resistant paint, and preparation method and application thereof

A fire retardant coating and nanotechnology, applied in fire retardant coatings, antifouling/underwater coatings, coatings, etc., can solve the problems of impact resistance, poor artificial aging resistance, poor adhesion, affecting service life, and poor antibacterial effect. Achieve long-lasting antibacterial effect, strong adhesion, excellent fireproof effect

Inactive Publication Date: 2014-12-10
SUZHOU CHENGSHENG INFORMATION TECH
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing fireproof coatings generally have excellent fireproof effects, but other effects, such as impact resistance, artificial aging resistance, adhesion, etc., are poor, which affects their service life, and are easy to fall off due to long time, and the antibacterial effect is not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano fire-resistant paint, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of nano fireproof coating, its component is made up of following composition by weight percentage: 80% A component and 20% B component; Described A component comprises following component by weight: 30 parts of ethylene-acetic acid Vinyl ester copolymer, 25 parts of nano silicon dioxide, 1 part of auxiliary agent, 0.4 part of mixed solvent; auxiliary agent includes wetting agent, anti-settling agent and defoamer; said mixed solvent includes propylene glycol and butyl acetate; Group B Parts by weight include the following components: 15 parts of cobalt naphthenate, 10 parts of melamine pyrophosphate, 20 parts of propylene glycol, and 15 parts of talcum powder. Additives include wetting agent, anti-settling agent and defoamer in a weight ratio of 1:4:1. The volume ratio of propylene glycol to butyl acetate in the mixed solvent is 1:2. The average particle diameter of nano silicon dioxide is 25nm.

[0018] The preparation method of nano fireproof coating, comprise...

Embodiment 2

[0024] A kind of fireproof coating, its component is made up of following composition by weight percentage: 90% of A component and 10% of B component; Described A component comprises following component by weight: 50 parts of ethylene-vinyl acetate Ester copolymer, 20 parts of nano silicon dioxide, 8 parts of auxiliary agent, 0.6 part of mixed solvent; auxiliary agent includes wetting agent, anti-sedimentation agent and defoamer; mixed solvent includes propylene glycol and butyl acetate; the B component It comprises the following components in parts by weight: 20 parts of cobalt naphthenate, 20 parts of melamine pyrophosphate, 30 parts of propylene glycol, and 20 parts of talcum powder. Additives include wetting agent, anti-settling agent and defoamer in a weight ratio of 1:4:1. The volume ratio of propylene glycol to butyl acetate in the mixed solvent is 1:2. The average particle diameter of nano silicon dioxide is 35nm.

[0025] The preparation method of fireproof coating ...

Embodiment 3

[0030] A kind of fireproof coating, its component is made up of following composition by weight percentage: 85% of A component and 15% of B component; Said A component comprises following component by weight: 40 parts of ethylene-vinyl acetate Ester copolymer, 22 parts of nano-silica, 5 parts of auxiliary agent, 0.5 part of mixed solvent; auxiliary agent includes wetting agent, anti-settling agent and defoamer; mixed solvent includes propylene glycol and butyl acetate; B component by weight The parts include the following components: 17 parts of cobalt naphthenate, 15 parts of melamine pyrophosphate, 25 parts of propylene glycol, and 17 parts of talcum powder. Additives include wetting agent, anti-settling agent and defoamer in a weight ratio of 1:4:1. The volume ratio of propylene glycol to butyl acetate in the mixed solvent is 1:2. The average particle diameter of nano silicon dioxide is 30nm.

[0031] The preparation method of fireproof coating comprises the following ste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano fire-resistant paint which is composed of the following components in percentage by weight: 80-90% of component A and 10-20% of component B. The component A comprises the following components in parts by weight: 30-50 parts of ethylene-vinyl acetate copolymer, 20-25 parts of nano silicon dioxide, 1-8 parts of assistant and 0.4-0.6 part of mixed solvent. The assistant comprises a wetting agent, an anti-settling agent and a defoaming agent. The mixed solvent comprises propanediol and butyl acetate. The component B comprises the following components in parts by weight: 15-20 parts of cobalt naphthenate, 10-20 parts of melamine pyrophosphate, 20-30 parts of propanediol and 15-20 parts of talcum powder. The invention also discloses a preparation method and application of the fire-resistant paint. The nano fire-resistant paint has the advantages of stable quality, favorable use effect, higher adhesive force and more durable antimicrobial effect.

Description

technical field [0001] The invention relates to a paint, in particular to a nano fireproof paint and its preparation method and application. Background technique [0002] Fireproof coating is a special coating used on the surface of flammable substrates, which can reduce the flammability of the surface of the coated material, retard the rapid spread of fire, and improve the fire resistance limit of the coated material. [0003] Existing fireproof coatings generally have excellent fireproof effects, but other effects, such as impact resistance, artificial aging resistance, adhesion, etc., are poor, thereby affecting their service life. Contents of the invention [0004] Purpose of the invention: In order to overcome the deficiencies in the prior art, the first purpose of the present invention is to provide a kind of nano fireproof coating. The second object of the present invention is to provide the preparation method of above-mentioned nano fireproof coating. The third ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/08C09D131/04C09D5/18C09D5/14C09D7/12
Inventor 夏建
Owner SUZHOU CHENGSHENG INFORMATION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com