Abrasion-resistant paint and preparation method thereof

A technology of wear-resistant coatings and component A, applied in the field of coatings, can solve the problems of easy wear of coatings, general wear resistance, wear and other problems, and achieve the effect of strong adhesion, strong wear resistance and simple process

Inactive Publication Date: 2014-12-24
JIANGSU MARINE VICTORY COATING
View PDF2 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, the wear resistance of the existing coatings is average, and the coatings are often subject to friction in some exposed parts, and the coatings are easy to wear. In the prior art, the coatings commonly used increase the wear resistance of equipment parts, but at 600 ° C There are many deficiencies in the wear resistance, gloss, adhesion and other propert

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] This embodiment provides a wear-resistant coating, including two components, A and B, and A and B are a two-component composition composed of components A and B mixed in a ratio of A:B=1:1.5, and A and B are measured in parts by mass. Contains the following components:

[0039] The A component in the A component comprises the following components in parts by mass:

[0040] E-20 epoxy resin with an epoxy equivalent of 450g / eq: 10 parts, black silicon carbide with a particle size of 6 μm: 25 parts, graphite fluoride with a particle size of 7 μm: 17 parts; γ-aminopropyltriethoxysilane : 20 copies;

[0041] The B component in the A component comprises the following components in parts by mass:

[0042] Methyl methacrylate: 43 parts, butyl acrylate: 25 parts, aluminum isopropoxide: 10 parts, vinyltriethoxysilane: 10 parts; xylene: 20 parts;

[0043] Component B includes the following components in parts by mass:

[0044] m-phenylenediamine: 42 parts, silicone: 5 parts, p...

Embodiment 2

[0055] This embodiment provides a wear-resistant coating, including two components, A and B, and A and B are a two-component composition composed of components A and B mixed in a ratio of A:B=1:1.5, and A and B are measured in parts by mass. Contains the following components:

[0056] The A component in the A component comprises the following components in parts by mass:

[0057] E-20 epoxy resin with an epoxy equivalent of 500g / eq: 14 parts, black silicon carbide with a particle size of 6 μm: 15 parts, fluorinated graphite with a particle size of 10 μm: 20 parts; 3-methacryloxypropyl Trimethoxysilane: 25 parts;

[0058] The B component in the A component comprises the following components in parts by mass:

[0059] Methyl methacrylate: 45 parts, butyl acrylate: 25 parts, aluminum isopropoxide: 5 parts, vinyltriethoxysilane: 13 parts; n-butanol: 23 parts;

[0060] Component B includes the following components in parts by mass:

[0061] Diethylene triamine: 35 parts, simeth...

Embodiment 3

[0072] This embodiment provides a wear-resistant coating, including two components, A and B, and A and B are a two-component composition composed of components A and B mixed in a ratio of A:B=1:1.5, and A and B are measured in parts by mass. Contains the following components:

[0073] The A component in the A component comprises the following components in parts by mass:

[0074] E-20 epoxy resin with an epoxy equivalent of 480g / eq: 15 parts, black silicon carbide with a particle size of 6 μm: 22 parts, graphite fluoride with a particle size of 5 μm: 15 parts; γ-(2,3 glycidyl oxide Base) propyltrimethoxysilane: 22 parts;

[0075] The B component in the A component comprises the following components in parts by mass:

[0076] Methyl methacrylate: 40 parts, butyl acrylate: 30 parts, aluminum isopropoxide: 6 parts, vinyltriethoxysilane: 15 parts; ethyl acetate: 20 parts;

[0077] Component B includes the following components in parts by mass:

[0078] Polyamide: 50 parts, pol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses abrasion-resistant paint and a preparation method thereof. The paint comprises a first component and a second component, wherein the first component is double-component composition formed by mixing of a component A and a component B in a ratio of 1:1, the component A in the first component comprises components as follows: E-20 epoxy resin, silicon carbide micro powder, carbon monofluoride and a coupling agent; the component B in the first component comprises components as follows: methyl methacrylate, butyl acrylate, aluminum isopropoxide, triethoxy vinyl silane and 20-25 parts of a solvent; the second component comprises components as follows: a curing agent, an antifoaming agent, a leveling agent and a solvent. The components A and B in the first component are prepared separately and then mixed, and finally, the first and second components are cured to obtain the abrasion-resistant paint.

Description

Technical field [0001] The invention is a coating technology field, which involves a wear -resistant coating and its preparation methods. Background technique [0002] With the advancement and development of science and technology, new materials, as one of the three major industries of the 21st century, are obviously particularly important. To a certain extent, it also represents the country's industrial progress and development.one. [0003] The coating is a type of liquid or solid material that is coated on the surface of the object to form a film to protect, decorate, or other special functions, such as insulation, rust, mold, heat resistance, etc.There are many types of coatings, and the special features that can be achieved by different formulas are different. [0004] At present, the wear -resistant coatings on the market are mainly used in the steel industry and the machinery industry. Wearing is often encountered in high -speed operations. The equipment will fail, damage,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/12C09D163/00C09D7/12C08F220/14C08F220/18C08F230/08
Inventor 郑化陈廷生刘小林
Owner JIANGSU MARINE VICTORY COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap