Aluminum alloy material and quenching treatment process thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of aluminum alloy materials and processing technology, which is applied in the processing field of metal materials and metal materials, can solve the problems of high material cost, impossibility of wide application, limited application range, etc., achieve high surface quality, good heat treatment ability, improve The effect of tensile strength
Inactive Publication Date: 2015-02-18
WUXI LEHUA AUTOMATION TECH
View PDF9 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the material cost of this patent is high, and the application range is limited due to the high price, so it is impossible to be widely used
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0049] The aluminum alloy material is mainly composed of aluminum, and the aluminum alloy material includes the following components: cadmium, germanium, magnesium, copper, iron, silicon, manganese, nickel and titanium, and is characterized in that the weight percentages of the components are respectively:
[0052] The aluminum alloy material is mainly composed of aluminum, and the aluminum alloy material includes the following components: cadmium, germanium, magnesium, copper, iron, silicon, manganese, nickel and titanium, and is characterized in that the weight percentages of the components are respectively:
[0055] The aluminum alloy material is mainly composed of aluminum, and the aluminum alloy material includes the following components: cadmium, germanium, magnesium, copper, iron, silicon, manganese, nickel and titanium, and is characterized in that the weight percentages of the components are respectively:
[0057] The aluminum alloy material also includes beryllium, and the weight percentage of the beryllium is 0.002%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
Diameter
aaaaa
aaaaa
Login to View More
Abstract
The invention relates to an aluminum alloy material and a quenching treatment process thereof. The aluminum alloy material comprises the following components: cadmium, germanium, magnesium, copper, iron, silicon, manganese, nickel, titanium, beryllium and molybdenum. The quenching treatment process comprises the following steps: (1) making the aluminum alloy material into a cable shape with the diameter of not more than 45 mm; (2) heating the aluminum alloy material to 450 DEG C in a quenching furnace; (3) forcedly and quickly cooling the aluminum alloy material in a quenching groove to finish the quenching process of the aluminum alloy material. According to the aluminum alloy material and the quenching treatment process, the properties of the aluminum alloy material are comprehensively improved, the mechanical strength and tensile property of aluminum alloy are improved, and the tensile strength, yield limit and heat resistance of the aluminum alloy material are improved; the quenching treatment process is convenient to control and realize, the aluminum alloy material is completely quenched, and stable and uniform component connection stress distribution of stable internal structure of the aluminum alloy material is achieved.
Description
technical field [0001] The invention relates to an aluminum alloy material and a quenching process thereof, and belongs to the technical field of processingmetal materials and metal materials. Background technique [0002] Aluminum is a pure white lightmetal with ductility, and its products are often made into rods, sheets, foils, powders, ribbons and filaments. In humid air, an oxide film can be formed to prevent metal corrosion. Aluminum powder and foil burn violently when heated in the air, emitting a blinding white flame. Soluble in dilute sulfuric acid, nitric acid, hydrochloric acid, sodiumhydroxide and potassiumhydroxide solution, insoluble in water. The content of aluminum in the earth's crust is second only to oxygen and silicon, ranking third, and is the most abundant metal element in the earth's crust. The development of the three important industries of aviation, construction, and automobile requires that the material properties have the unique properti...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More