A kind of preparation method of graphene-polypropylene carbonate green composite material

A polypropylene carbonate and composite material technology, which is applied in the field of composite film preparation, can solve the problems of poor solvent resistance, oxygen barrier, thermal stability, poor mechanical wear resistance, and low glass transition temperature, and achieves easy operation. , good solvent resistance, excellent biodegradability effect

Active Publication Date: 2016-08-24
广东顺德伟德创通智能科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Polypropylene carbonate is a completely degradable green and environmentally friendly material synthesized from propylene oxide and carbon dioxide. It is considered to be one of the most pro

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0017] Example 1: A preparation method of graphene-polypropylene carbonate green composite material, specifically:

[0018] Weighing of raw materials: 1 part of graphene, 60 parts of polypropylene carbonate, and 70 parts of polyvinyl alcohol are weighed by weight.

[0019] Preparation method: graphene surface pretreatment; high-speed mixing treatment of graphene and sodium dodecylbenzene sulfonate, high-speed mixing of the processed graphene mixture with silane coupling agent KH560 for secondary surface treatment; Graphene, polypropylene carbonate and polyvinyl alcohol are uniformly mixed at high speed in a high-speed mixing hopper; the mixed materials are put into a twin-screw extruder with a preset temperature of 130°C and a screw speed of 150r / min for vacuum extrusion The composite material is obtained by cutting pellets.

Example Embodiment

[0020] Embodiment 2: A preparation method of graphene-polypropylene carbonate green composite material, specifically:

[0021] Weighing of raw materials: 6 parts by weight of graphene, 90 parts of polypropylene carbonate, and 80 parts of polyvinyl alcohol.

[0022] Preparation method: graphene surface pretreatment; high-speed mixing treatment of graphene and sodium dodecylbenzene sulfonate, high-speed mixing of the processed graphene mixture with silane coupling agent KH560 for secondary surface treatment; Graphene, polypropylene carbonate and polyvinyl alcohol are uniformly mixed at high speed in a high-speed mixing hopper; the mixed materials are put into a twin-screw extruder with a preset temperature of 170°C and a screw speed of 250r / min for vacuum extrusion The composite material is obtained by cutting pellets.

Example Embodiment

[0023] Embodiment 3: A preparation method of graphene-polypropylene carbonate green composite material, specifically:

[0024] Weighing of raw materials: 3 parts by weight of graphene, 75 parts of polypropylene carbonate, and 75 parts of polyvinyl alcohol.

[0025] Preparation method: graphene surface pretreatment; high-speed mixing treatment of graphene and sodium dodecylbenzene sulfonate, high-speed mixing of the processed graphene mixture with silane coupling agent KH560 for secondary surface treatment; Graphene, polypropylene carbonate and polyvinyl alcohol are uniformly mixed at high speed in a high-speed mixing hopper; the mixed materials are put into a twin-screw extruder with a preset temperature of 155°C and a screw speed of 200r / min for vacuum extrusion The composite material is obtained by cutting pellets.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of a green graphene-poly(propylene carbonate) composite material. The method comprises the following steps: pretreating the surface of graphene, carrying out high-speed mixing treatment on pretreated graphene as well as poly(propylene carbonate) and polyvinyl alcohol, and carrying out extrusion, vacuumizing and granulation. The composite film prepared by the method has excellent degradable quality of poly(propylene carbonate) and also has better solvent resistance, oxygen isolation property, thermal stability and mechanical wear resistance.

Description

technical field [0001] The invention relates to the field of preparation of composite films, in particular to a method for preparing a graphene-polypropylene carbonate green composite material. Background technique [0002] Graphene oxide is a functionalized graphene with a quasi-two-dimensional layered molecular structure, containing many functional groups such as hydroxyl, carboxyl, carbonyl and epoxy, and has a high specific surface energy and good hydrophilicity and Mechanical properties, and good dispersion in polar solvents, this new type of functional nanomaterials has attracted more and more attention from scientists, and has become a research hotspot for scholars from all over the world. Graphene oxide is not only the starting point for large-scale synthesis of graphene, but also one of the most effective ways to realize the functionalization of graphene. By using graphene oxide as a new functional modifier to prepare or optimize various composite materials, it has ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L29/04C08L69/00C08K9/06C08K9/04C08K3/04
Inventor 王强
Owner 广东顺德伟德创通智能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap