Red-spot crystalline glaze and preparation method of ceramic adopting same
A technology for preparing ceramics and crystallizing glaze, applied in the field of glaze formulation, can solve the problems of poor product repeatability, economic loss of enterprises, difficult firing, etc., and achieve the effect of increasing the variety of ceramics, delicate luster, and enriching market demand.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022] The method for preparing ceramics using the red spot crystal glaze according to any one of the above claims of the present invention includes the following steps:
[0023] (1) Weigh the raw materials according to the glaze formula and put them into a ball mill for wet grinding. The weight ratio of material:ball:water during wet grinding is 1:2:0.6-1, and the glaze slurry obtained by grinding has a fineness of 200-300 mesh. The sieve residue is less than 1%, and the moisture content of the glaze slurry is 45-48%. It can be used after aging; the fineness of the glaze and the thickness of the glaze have a greater impact on the red spot crystal flower art glaze products. Only a few crystal flowers are scattered on the glaze surface after finishing. If the glaze is too thin, the crystal flower will appear small, and it will not grow up to form the required crystal flower size, which will affect the artistic effect of the crystal flower.
[0024] (2) Apply glaze on the biscuit, w...
Example Embodiment
[0028] Example 1
[0029] Glaze recipe:
[0030] 20 parts of albite, 10 parts of quartz, 10 parts of burnt talc, 1 part of calcite, 10 parts of ashes, 1 part of glass powder, 5 parts of barium carbonate, 5 parts of iron oxide, 0.5 parts of high-dielectric earth, 0.3 parts of fluorite powder.
[0031] Preparation:
[0032] (1) Weigh the raw materials according to the glaze formula and put them into a ball mill for wet grinding. The weight ratio of material:ball:water during wet grinding is 1:2:0.6, and the glaze slurry obtained by grinding has a fineness of 200-300 mesh sieve. The remainder is less than 1%, the moisture content of the glaze slurry is 45~48%, and it is used after aging;
[0033] (2) Apply glaze on the biscuit, with a thickness of 0.8mm, and dry after glazing;
[0034] (3) Put the dried body into a kiln. When firing, it takes 90 minutes from room temperature to 500°C, 60 minutes from 500°C to 950°C, 10 minutes from 950°C to 1100°C, and from 1100°C It takes 10 minutes to r...
Example Embodiment
[0035] Example 2
[0036] Glaze recipe:
[0037] 25 parts of albite, 10 parts of quartz, 10 parts of burnt talc, 2 parts of calcite, 12 parts of ashes, 2 parts of glass powder, 8 parts of barium carbonate, 10 parts of iron oxide, 0.8 parts of high-dielectric earth, 0.5 parts of fluorite powder.
[0038] Preparation:
[0039] (1) Weigh the raw materials according to the glaze formula and put them into a ball mill for wet grinding. The weight ratio of material:ball:water during wet grinding is 1:2:0.6, and the glaze slurry obtained by grinding has a fineness of 200-300 mesh sieve. The remainder is less than 1%, the moisture content of the glaze slurry is 45~48%, and it is used after aging;
[0040] (2) Apply glaze on the biscuit, with a thickness of 0.8mm, and dry after glazing;
[0041] (3) Put the dried body into a kiln for firing. When firing, it takes 100 minutes from room temperature to 500°C, 75 minutes from 500°C to 950°C, 15 minutes from 950°C to 1100°C, and from 1100°C It takes ...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap