Prefabrication method of temperature-changed-shrinkage resistant inner partition plate for building

A technology for interior partition walls and buildings, which is applied in the field of prefabrication of interior partition panels for buildings. It can solve problems such as cracking, affecting the apparent quality of buildings, and rising, so as to reduce the drop rate, improve the apparent quality, and reduce temperature fluctuations. small effect

Inactive Publication Date: 2015-04-29
吉林森煌建筑材料集团有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] When the outdoor ambient temperature changes, the indoor ambient temperature will also change accordingly, and the temperature of the inner partition wall board as an indoor space partition will also increase or decrease accordingly, and the resulting temperature difference stress fluctuation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A method for prefabricating an inner partition wall panel that resists temperature change and shrinkage for buildings, comprising the following prefabrication steps:

[0016] 1. Material preparation: Take 230 kg of Portland cement; 80 kg of commercial concrete grade fly ash; 780 kg of sand and gravel particles with a particle diameter ≤ 5mm used as aggregate; the model produced by Jilin Dehong Chemical Building Materials Co., Ltd. is DH -1 40 kilograms of acetophenone phase-change material microspheres; 1 kilogram of rosin soap cement foaming agent; 200 kilograms of water stand-by;

[0017] 2. The first mixing: Put Portland cement, commercial concrete grade fly ash, sand and gravel particles and water into the mixer for mixing. After mixing evenly, the first mixture is obtained;

[0018] 3. Stir for the second time: add DH-1 acetophenone phase change material microspheres in the first mixture, continue to stir with a mixer, after stirring evenly, obtain the second mixtu...

Embodiment 2

[0027] A method for prefabricating an inner partition wall panel that resists temperature change and shrinkage for buildings, comprising the following prefabrication steps:

[0028] 1. Material preparation: Take 320 kg of sulphoaluminate cement; 170 kg of commercial concrete grade fly ash; 820 kg of sand and gravel particles with a particle diameter ≤ 5mm used as aggregate; the model produced by Jilin Dehong Chemical Building Materials Co., Ltd. is 80 kg of acetophenone phase change material microspheres of DH-1; 1.2 kg of animal protein cement foaming agent; 240 kg of water for use;

[0029] 2. The first mixing: send sulphoaluminate cement, commercial concrete grade fly ash, sand and gravel particles and water into the mixer for mixing, and after mixing evenly, obtain the first mixture;

[0030] 3. Stir for the second time: add DH-1 acetophenone phase change material microspheres in the first mixture, continue to stir with a mixer, after stirring evenly, obtain the second mix...

Embodiment 3

[0039] A method for prefabricating an inner partition wall panel that resists temperature change and shrinkage for buildings, comprising the following prefabrication steps:

[0040] 1. Material preparation: take 275 kg of slag cement; 125 kg of commercial concrete grade fly ash; 800 kg of sand and gravel particles with a particle diameter ≤ 5mm used as aggregate; the model produced by Jilin Dehong Chemical Building Materials Co., Ltd. is DH-1 60 kg of acetophenone phase change material microspheres; 1.1 kg of plant tea saponin cement foaming agent; 220 kg of water for use;

[0041] 2. Stir for the first time: send slag cement, commercial concrete grade fly ash, sand and gravel particles and water into the mixer for mixing, and after mixing evenly, obtain the first mixture;

[0042] 3. Stir for the second time: add DH-1 acetophenone phase change material microspheres in the first mixture, continue to stir with a mixer, after stirring evenly, obtain the second mixture;

[0043]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a prefabrication method of a temperature-changed-shrinkage resistant inner partition plate for a building. The method comprises the following steps: firstly, preparing concrete, coal ashes for commercial concrete, sand and gravel particles, acetophenone phase-change material microspheres, water and a concrete foaming agent; respectively stirring the materials evenly for three times; pouring a mold, hardening and conserving; and evenly and effectively distributing the acetophenone phase-change material microspheres and foam into a wall body of the inner partition wall plate. The inner partition plate obtained by the prefabrication method disclosed by the invention has the performance of resisting temperature-changed shrinkage, and is small in deformation in use; and the indoor apparent quality of the building can be improved.

Description

technical field [0001] The invention relates to the field of prefabrication of inner partition wall boards for buildings, and in particular provides a prefabrication method for inner partition wall boards of anti-temperature change and shrinkage for buildings. Background technique [0002] When the outdoor ambient temperature changes, the indoor ambient temperature will also change accordingly, and the temperature of the inner partition wall board as an indoor space partition will also increase or decrease accordingly, and the resulting temperature difference stress fluctuation will cause the inner partition wall board to shrink and deform , resulting in cracking at the connection between the inner partition wall panel and the main structure of the building or at the joint between the inner partition wall panel and the inner partition wall panel, which affects the apparent quality of the building. Contents of the invention [0003] The object of the present invention is to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/02C04B28/00
Inventor 董宏伟苗春生董亮
Owner 吉林森煌建筑材料集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap