Wear-resisting emulsion paint

A technology of latex paint and styrene-acrylic emulsion, applied in the field of wear-resistant latex paint, can solve the problems of affecting appearance and other properties, poor stain resistance, easy to produce scratches, etc. Effects without toxic side effects

Inactive Publication Date: 2015-04-29
QINGDAO JIASHANG CREATIVE CULTURE
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main manifestations are: 1. Poor stain resistance, which seriously affects the appearance and other properties; 2. Poor wear resistance, prone to scratches, etc.; 3. Poor adhesion, easy to fall off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1, a kind of wear-resisting latex paint, is made of the following raw materials in parts by weight: 6 parts of sodium lauryl sulfate, 20 parts of styrene-acrylic emulsion, 4 parts of sodium hexametaphosphate, 11 parts of ammonium tungstate, poly 9 parts of vinyl alcohol, 5 parts of n-butanol, 20 parts of deionized water, 4 parts of polyaluminium chloride, 8 parts of ethyl orthosilicate, 10 parts of perfluorooctyl-triethoxysilane, 7 parts of nano titanium dioxide, 6 parts of wollastonite, 5 parts of butyl acrylate, 3 parts of mica powder, and 5 parts of kaolin.

Embodiment 2

[0011] Embodiment 2, a kind of wear-resisting latex paint, is made of the following raw materials in parts by weight: 10 parts of sodium lauryl sulfate, 25 parts of styrene-acrylic emulsion, 6 parts of sodium hexametaphosphate, 18 parts of ammonium tungstate, poly 13 parts of vinyl alcohol, 10 parts of n-butanol, 35 parts of deionized water, 8 parts of polyaluminum chloride, 15 parts of ethyl orthosilicate, 13 parts of perfluorooctyl-triethoxysilane, 12 parts of nano titanium dioxide, 10 parts of wollastonite, 10 parts of butyl acrylate, 8 parts of mica powder, and 10 parts of kaolin.

Embodiment 3

[0012] Embodiment 3, a kind of wear-resisting latex paint, is made of the following raw materials in parts by weight: 12 parts of sodium lauryl sulfate, 30 parts of styrene-acrylic emulsion, 8 parts of sodium hexametaphosphate, 22 parts of ammonium tungstate, poly 14 parts of vinyl alcohol, 15 parts of n-butanol, 50 parts of deionized water, 12 parts of polyaluminum chloride, 17 parts of ethyl orthosilicate, 15 parts of perfluorooctyl-triethoxysilane, 14 parts of nano titanium dioxide, 12 parts of wollastonite, 15 parts of butyl acrylate, 11 parts of mica powder, and 15 parts of kaolin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses wear-resisting emulsion paint. The wear-resisting emulsion paint is prepared from the following raw materials in parts by weight: 6-12 parts of lauryl sodium sulfate, 20-30 parts of styrene-acrylic emulsion, 4-8 parts of sodium hexametaphosphate, 11-22 parts of ammonium tungstate, 9-14 parts of polyvinyl alcohol, 5-15 parts of n-butyl alcohol, 20-50 parts of deionized water, 4-12 parts of aluminum polychloride, 8-17 parts of tetraethoxysilane, 10-15 parts of perfluorooctyl triethoxysilane, 7-14 parts of nanometer titanium dioxide, 6-12 parts of wollastonite, 5-15 parts of butyl acrylate, 3-11 parts of mica powder, and 5-15 parts of kaolin. The wear-resisting emulsion paint provided by the invention is non-toxic, environment-friendly, high in caking capability, free of toxic and side effects, high in abrasion resistance, capable of preventing sun burning and corrosion, and long-lasting in use.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a wear-resistant latex paint. Background technique [0002] With people's awareness of health, they are more and more aware of the importance of environmental protection. The high-grade, functional and environmental protection of coatings are gradually accepted by the market. However, the competition in the coatings market has always been fierce. With the change of consumption structure, functions and Environmentally friendly coatings are on the horizon and are hot spots in the market; as we all know, people spend 70% of their time indoors, so the cleanliness of indoor air will directly affect people's health. Faced with this market situation, the vast majority of consumers still find it difficult to accept expensive products, while some latex rubbers with relatively low prices often have technical problems such as poor raw material quality and excessive formaldehyde c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/06C09D4/02C09D7/12C09D5/02C09D5/08
Inventor 范开娟李文勇李长敏
Owner QINGDAO JIASHANG CREATIVE CULTURE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com