Environment-friendly water-based paint and preparation method thereof

A water-based paint and environmentally friendly technology, applied in the field of coatings, can solve the problems of complex preparation process of nano-mixtures and inability to release negative ions

Active Publication Date: 2015-05-06
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF5 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The Chinese patent document with the application number 201310738713.3 discloses a formaldehyde-removing nano-mixture and its preparation method. The nano-mixture is mainly composed of photocatalyst-composite titanium dioxide, superabsorbent graphene, nano-anion tourmaline, and biological polyphenols. It can absorb a certain amount of formaldehyde and PM2.5 particles, but the preparation process of the nano-mixture is complicated and cannot release negative ions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly water-based paint and preparation method thereof
  • Environment-friendly water-based paint and preparation method thereof
  • Environment-friendly water-based paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] Correspondingly, the present invention also provides a preparation method of an environmentally friendly water-based paint, comprising the following steps: step a) mixing 0.5 to 5 parts by weight of a defoamer, 1 to 20 parts by weight of a thickener, 1 to 10 parts by weight of a dispersant and Put 0-200 parts by weight of water into the mixer, add 50-150 parts by weight of composite anion powder and 40-100 parts by weight of anion additive after the dispersion is complete, and stir evenly. The speed of the mixer is 600-2500 rpm. It is composed of crystal salt, nano-silica, nano-phosphate titanium dioxide and nano-zinc dioxide; step b) reduce the speed of the mixer to 400-800 rpm, mix 700-900 parts by weight of water-based resin dispersion, 10-100 parts by weight The film-forming aid, 0.5-5 parts by weight of the defoamer and 0.1-1 part by weight of the pH regulator are put into the mixer, and stirred for 30-50 minutes to obtain an environmentally friendly water-based pai...

Embodiment 1

[0062] The described water-based paint capable of releasing negative ions comprises the following components, and the parts by weight of each component are:

[0063]

[0064] Wherein, the parts by weight of each component in the composite anion powder are respectively:

[0065]

[0066] Wherein, the parts by weight of each component in the negative ion additive are respectively:

[0067]

[0068] The preparation process steps of the water-based paint capable of releasing negative ions are as follows:

[0069] 1) Prepare raw materials according to the set weight percentage, put water, thickener, dispersant and 50% defoamer into the high-speed mixer, and after the dispersion is complete, slowly add composite anion powder and anion additive, Until the desired fineness is achieved, the speed of the high-speed stirrer is 1600 revolutions per minute.

[0070] 2), reduce the rotating speed of the agitator to 600 revolutions per minute. According to the set weight percenta...

Embodiment 2

[0072] The described water-based paint capable of releasing negative ions comprises the following components, and the parts by weight of each component are:

[0073]

[0074] Wherein, the parts by weight of each component in the composite anion powder are respectively:

[0075]

[0076] Wherein, the parts by weight of each component in the negative ion additive are respectively:

[0077]

[0078] The preparation process steps of the water-based paint capable of releasing negative ions are as follows:

[0079] 1) Prepare raw materials according to the set weight percentage, put water, thickener, dispersant and 50% defoamer into the high-speed mixer, and after the dispersion is complete, slowly add composite anion powder and anion additive, until the desired fineness is achieved. The speed of the high-speed stirrer was 1500 revolutions per minute.

[0080] 2), reduce the rotating speed of the agitator to 600 revolutions per minute. According to the set weight percen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides environment-friendly water-based paint and a preparation method thereof. The environment-friendly water-based paint comprises water-based resin dispersion, water, compound anion powder, an anion additive, a coalescing agent, a deforming agent, a thickening agent, a dispersing agent and a pH regulator. Crystal salt can undergo water loss after absorbing water molecules from air and the process is carried out alternately to continuously generate anions, so that the redundant cations in the air can be effectively neutralized, the floating dust and particles in the air are adsorbed and the air is purified. Nano silicon dioxide, nano phosphate titanium dioxide and nano zinc dioxide are used as photocatalyst materials which can be used for effectively degrading the harmful gases such as formaldehyde in the air under illumination so as to generate superoxide anion free radicals and accompany negative oxygen ions. Under the combined action of the crystal salt and the photocatalyst, the prepared environment-friendly water-based paint has the advantages of forming high-concentration negative oxygen ion environment which can be kept and sufficiently absorbing the harmful gases and particles such as dust so as to effectively improve the indoor air quality.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an environmentally friendly water-based paint and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, the requirements for the living environment are getting higher and higher, and more attention is paid to the impact of the environment on human health. Furniture is an essential item in the living environment, which is closely related to the living environment of modern people, and paint is an indispensable material in furniture production. At present, there are many functional coatings on the market, such as coatings with functions such as heat preservation, heat insulation, flame retardancy, and sound insulation, but they cannot really improve the impact of the coating itself on the human body. [0003] Negative ions are the protectors of the environment. Negative ion air is called "longevity element" or "air vitamin"...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/04C09D4/02C09D4/06C09D5/14C09D7/12
CPCC08K2201/011C09D5/14C09D7/61C09D175/04C08L83/12C08K13/02C08K3/36C08K2003/2237C08K2003/2296C08K3/38C08K3/04C08K3/346
Inventor 陈宗宗
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com