Novel high-softness polylactic acid fiber composite material and preparation method thereof

A polylactic acid fiber and composite material technology, which is applied in the directions of fiber processing, fiber chemical characteristics, and conjugated synthetic polymer rayon, etc., to achieve the effects of improved processing performance, improved elongation at break, and improved softness

Active Publication Date: 2015-06-10
HEFEI GENIUS NEW MATERIALS
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, no special research on the softness of polyester modified PLA fibers has been reported, and the present invention has important research significance and application value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 80 parts of polylactic acid (PLA), 20 parts of polytrimethylene adipate (PPA), 0.5 parts of polycarbodiimide (PCDI), and 0.5 parts of tetrabutyl titanate.

[0027] (1) The blend modified polylactic acid fiber was prepared by the following method: 40 parts of PLA resin was vacuum-dried at 60°C for 24 hours, and then PLA (40 parts) / PPA (20 parts) / PCDI (0.5 parts ) / TT-01 (0.5 parts) were uniformly mixed, added to a twin-screw extruder for melt blending to prepare spinning chips, and the extrusion temperature was 160°C;

[0028] (2) Preparation of polylactic acid and its blended fibers: 40 parts of PLA and PLA (40 parts) / PPA (20 parts) / PCDI (0.5 parts) / TT-01 (0.5 parts) prepared in step (1) were combined The mixed slices were dried in a vacuum oven at 90 °C for 48 h, and then fibers were prepared by a two-step melt spinning-drawing method. Among them, the spinneret has 24 holes, the hole diameter is 0.3 mm, and the spinneret hole length-to-diameter ratio (L / D) is 3. Then ...

Embodiment 2

[0031] 70 parts of polylactic acid (PLA), 30 parts of polytrimethylene adipate (PPA), 0.1 part of polycarbodiimide (PCDI), 0.1 part of tetrabutyl titanate.

[0032] (1) The blend modified polylactic acid fiber was prepared by the following method: 35 parts of PLA resin was vacuum-dried at 60°C for 24 hours, and then PLA (35 parts) / PPA (30 parts) / PCDI (0.1 part ) / TT-01 (0.1 parts) were uniformly mixed, added to a twin-screw extruder for melt blending to prepare spinning chips, and the extrusion temperature was 150°C;

[0033] (2) Preparation of polylactic acid and its blended fibers: 35 parts of PLA and PLA (35 parts) / PPA (30 parts) / PCDI (0.1 parts) / TT-01 (0.1 parts) prepared in step (1) were combined The mixed slices were dried in a vacuum oven at 90 °C for 48 h, and then fibers were prepared by a two-step melt spinning-drawing method. Among them, the spinneret has 24 holes, the hole diameter is 0.3 mm, and the spinneret hole length-to-diameter ratio (L / D) is 3. Then spin th...

Embodiment 3

[0035] 90 parts of polylactic acid (PLA), 10 parts of polytrimethylene adipate (PPA), 1 part of polycarbodiimide (PCDI), 1 part of tetrabutyl titanate.

[0036] (1) The blend modified polylactic acid fiber was prepared by the following method: 45 parts of PLA resin was vacuum-dried at 60°C for 24 hours, and then PLA (45 parts) / PPA (10 parts) / PCDI (1 part ) / TT-01 (1 part) mixed evenly, added to a twin-screw extruder for melt blending to prepare spinning chips, and the extrusion temperature was 180°C;

[0037] (2) Preparation of polylactic acid and its blended fibers: 45 parts of PLA and PLA (45 parts) / PPA (10 parts) / PCDI (1 part) / TT-01 (1 part) prepared in step (1) were combined The mixed slices were dried in a vacuum oven at 90 °C for 48 h, and then fibers were prepared by a two-step melt spinning-drawing method. Among them, the spinneret has 24 holes, the hole diameter is 0.3 mm, and the spinneret hole length-to-diameter ratio (L / D) is 3. Then spin through a spinning machin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Apertureaaaaaaaaaa
Weight average molecular weightaaaaaaaaaa
Weight average molecular weightaaaaaaaaaa
Login to View More

Abstract

The invention relates to a novel high-softness polylactic acid fiber composite material and a preparation method thereof. The composite material comprises the following components in parts by weight: 70-90 parts of polylactic acid (PLA), 1-3 parts of poly(1,2-propylene glycol adipate) (PPA), 0.1-1 part of polycarbodiimide (PCDI), and 0.1-1 part of tetrabutyl titanate. The PLA / PPA blend is modified by taking multifunctional PCDI and TT-01 as reactive compatibilizers, the high-temperature stability and compatibility of the material can be well improved by PCDI, and the processing performance is better. After PCDI is added, the breaking strength and elastic modulus of the PLA / PPA blend fiber are reduced, the breaking elongation is obviously improved, and the softness is improved. The transesterification reaction between PLA and PPA can be promoted through the addition of TT-01, so that the stability and compatibility of the product are further improved.

Description

technical field [0001] The invention relates to the technical field of biodegradable polymer materials, in particular to a novel polylactic acid fiber composite material with high flexibility and a preparation method thereof. Background technique [0002] As a new type of environmentally friendly fiber, polylactic acid / polypropylene adipate (PLA / PPA) fiber has the advantages of good mechanical properties, degradability, good biocompatibility and low production energy consumption, but in a certain In fields such as medicine, packaging and cable coating, due to the poor compatibility of PLA / PPA, some properties of the material, especially the flexibility, cannot meet the requirements of the parts. Aiming at these problems, this paper innovatively uses multifunctional polycarbodiimide as a reactive compatibilizer to further modify PLA / PPA blends. The addition of polycarbodiimide (PCDI) can improve the blend The high temperature stability and compatibility of the material, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F8/14D01F1/10D01D5/08D01D5/30D01D5/12D01D10/02
Inventor 杨桂生刘凯
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More