Method for preparing nano-titanium dioxide modified color fixing agent emulsion

A nano-titanium dioxide and color-fixing agent technology, applied in dyeing, textile and papermaking, etc., can solve the problems of strong hydrophilicity and reduce the color-fixing effect, and achieve the effects of strong softness, simple process and simple control.

Active Publication Date: 2015-07-01
ZHEJIANG IND POLYTECHNIC COLLEGE
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this type of color-fixing agent containing cationic groups reduces its color-fixing effect due to its strong hydrophilicity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Nano-titanium dioxide modified color-fixing agent emulsion is made from modified nano-titanium dioxide dispersion liquid, cationic monomer, organosilicon monomer, initiator, emulsifier, and deionized water, and is prepared by core-shell emulsion polymerization. Parts by mass are: 15 parts of modified nano-titanium dioxide dispersion liquid, 29 parts of cationic monomer, 13 parts of organosilicon monomer, 18 parts of emulsifier, 2 parts of initiator, and 820 parts of deionized water.

[0032] The preparation method of nano-titanium dioxide modified color-fixing agent emulsion comprises the steps:

[0033] Step 1. Add modified nano-titanium dioxide dispersion liquid, 2 / 3 emulsifier, 1 / 3 cationic monomer, 1 / 3 organosilicon monomer, 2 / 3 deionized water into the reaction kettle, heat to 55°C, stir for 30 Minutes, form emulsion; Initiator is dissolved in 30 parts of deionized water and forms aqueous solution, stand-by;

[0034] Step 2. Put 1 / 3 emulsifier, 1 / 3 cationic monome...

Embodiment 2

[0044] Nano-titanium dioxide modified color-fixing agent emulsion is made from modified nano-titanium dioxide dispersion liquid, cationic monomer, organosilicon monomer, initiator, emulsifier, and deionized water, and is prepared by core-shell emulsion polymerization. Parts by mass are: 12 parts of modified nano-titanium dioxide dispersion liquid, 36 parts of cationic monomer, 15 parts of organosilicon monomer, 22 parts of emulsifier, 1 part of initiator, and 750 parts of deionized water.

[0045] The preparation method of nano-titanium dioxide modified color-fixing agent emulsion comprises the steps:

[0046]Step 1. Add modified nano-titanium dioxide dispersion, 2 / 3 emulsifier, 1 / 3 cationic monomer, 1 / 3 organosilicon monomer, 2 / 3 deionized water into the reaction kettle, heat to 57°C, stir for 30 Minutes, form emulsion; Initiator is dissolved in 30 parts of deionized water and forms aqueous solution, stand-by;

[0047] Step 2. Put 1 / 3 emulsifier, 1 / 3 cationic monomer, 1 / 3 or...

Embodiment 3

[0057] Nano-titanium dioxide modified color-fixing agent emulsion is made from modified nano-titanium dioxide dispersion liquid, cationic monomer, organosilicon monomer, initiator, emulsifier, and deionized water, and is prepared by core-shell emulsion polymerization. Parts by mass are: 20 parts of modified nano-titanium dioxide dispersion liquid, 23 parts of cationic monomer, 11 parts of organosilicon monomer, 16 parts of emulsifier, 1.5 parts of initiator, and 600 parts of deionized water.

[0058] The preparation method of nano-titanium dioxide modified color-fixing agent emulsion comprises the steps:

[0059] Step 1. Add modified nano-titanium dioxide dispersion liquid, 2 / 3 emulsifier, 1 / 3 cationic monomer, 1 / 3 organosilicon monomer, 2 / 3 deionized water into the reaction kettle, heat to 58°C, stir for 30 Minutes, form emulsion; Initiator is dissolved in 30 parts of deionized water and forms aqueous solution, stand-by;

[0060] Step 2. Put 1 / 3 emulsifier, 1 / 3 cationic mono...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing nano-titanium dioxide modified color fixing agent emulsion and aims to overcome the defect that color fixing emulsion is poor in ultraviolet resistance. According to the method, the nano-titanium dioxide modified color fixing agent emulsion is prepared from modified nano-titanium dioxide dispersion liquid, a cationic monomer, an organic silicon monomer, an emulsifier, an initiator and deionized water in a nuclear-shell emulsion polymerization mode. The method is simple and convenient in process, simple to control and stable in polymerization system, and by adjusting the proportions of monomer components of a core layer and a shell layer, nano-titanium dioxide, the cationic monomer and the organic silicon monomer are differently distributed, and thus a purpose of modifying the color fixing agent emulsion is achieved.

Description

technical field [0001] The invention relates to a preparation method of nano-titanium dioxide-modified color-fixing agent emulsion, and belongs to the field of polymer preparation. Background technique [0002] Although some dyes can dye brighter colors, due to the water-soluble groups on the dyes, the wet fastness is not good, and the fading and staining are serious. If it is stained on white or other colored fibers, it will cause staining and color matching, such as direct dyes and acid dyes, which are prone to such problems. In addition, although reactive dyes can form covalent bonds with cellulose fibers, if there are hydrolyzed dyes or insufficient soaping of unbonded dyes during dyeing, the wet fastness will also be reduced; Reactive dyes that have formed covalent bonds may also break bonds and decompose under acidic or alkaline conditions, as well as problems such as insufficient color fastness to chlorine, perspiration fastness, and light fastness. In order to impr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/12C08F226/02C08F222/22C08F2/28C08F2/30C08K9/04C08K3/22D06P5/08D06P5/10
Inventor 张奇鹏
Owner ZHEJIANG IND POLYTECHNIC COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap