A kind of microwave radiation melt method chlorination production method of chlorinated polyvinyl chloride cpvc resin

A technology of CPVC resin and chlorinated polyvinyl chloride, applied in the field of new technology and new polymer materials, can solve the problems of high chlorine content, short chlorination reaction time and high utilization rate of liquid chlorine

Inactive Publication Date: 2017-06-30
深圳兰品科技有限公司
View PDF20 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] The advantages of the present invention are: melt method, microwave accelerated chlorination, chlorination process, and equipment have no special requirements for raw material polyvinyl chloride PVC resin, and can meet the chlorination and chlorination reaction of domestic polyvinyl chloride PVC resin in the international market. The time is short (from the conventional 4 hours to 5-10 minutes), there is basically no degradation and no branching in the chlorination process, and the chlorine content of chlorinated polyvinyl chloride CPVC products is high and the chlorine content is easy to use with screw speed and feeding Quantity control and adjustment, high utilization rate of liquid chlorine, high mechanical properties, high flame retardancy, continuous production, closed system production safety and environmental protection, no similar chlorination production method reported in the world, advanced technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of microwave radiation melt method chlorination production method of chlorinated polyvinyl chloride cpvc resin
  • A kind of microwave radiation melt method chlorination production method of chlorinated polyvinyl chloride cpvc resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Embodiment 1: Feed 8 kg / min SG8 type polyvinyl chloride PVC resin quantitatively and uniformly in a twin-screw extruder with a diameter of 62, an aspect ratio L / D=64, a set temperature of 110° C., and a rotating speed of 500 rpm. After the material is discharged, use a liquid chlorine booster pump to inject 1 kg / min (a total of 2 kg / min) of liquid chlorine into the 6th and 11th sections of the two main inlets. The extruded product is a white resin, and the measured chlorine content is 60.6 %, the measured viscosity converted into a degree of polymerization is 700;

Embodiment 2

[0037] Embodiment 2: Feed 8 kg / min SG8 type polyvinyl chloride PVC resin quantitatively and uniformly in a twin-screw extruder with a diameter of 62, an aspect ratio L / D=64, a set temperature of 110° C., and a rotating speed of 500 rpm. After the material is discharged, use the liquid chlorine booster pump to inject 1 kg / min (2 kg / min in total) of liquid chlorine into the 6th and 11th sections of the two main inlets, and turn on the microwave radiation at the same time. The power of each magnetron is 1000W. , the power distributed to each waveguide branch is about 200W, the extruded product is a white resin, the measured chlorine content is 73.1%, and the measured viscosity is converted into a degree of polymerization of 710;

Embodiment 3

[0038] Embodiment 3: Feed 8 kg / min SG8 type polyvinyl chloride PVC resin quantitatively and uniformly in a twin-screw extruder with a diameter of 62, an aspect ratio L / D=64, a set temperature of 110° C., and a rotating speed of 600 rpm. After the material is discharged, use the liquid chlorine booster pump to inject 1 kg / min (2 kg / min in total) of liquid chlorine into the 6th and 11th sections of the two main inlets, and turn on the microwave radiation at the same time. The power of each magnetron is 1000W. , the power distributed to each waveguide branch tube is about 200W, the extruded product is a white resin, the measured chlorine content is 68.8%, and the measured viscosity converted into a degree of polymerization is 708;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
wavelengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a chlorination production method of chlorinated polyvinyl chloride CPVC resin by microwave radiation melt method, which comprises feeding liquid chlorine into molten polyvinyl chloride PVC under high pressure in a twin-screw extruder reactor and simultaneously feeding microwave Auxiliary chlorination of molten polyvinyl chloride PVC resin to achieve high quality, high chlorine content, low cost, fast, environmentally friendly and continuous production of chlorinated polyvinyl chloride CPVC resin Compared with polyvinyl chloride PVC resin, microwave accelerated chlorination in molten state, chlorination process has no special requirements for raw material polyvinyl chloride PVC resin, chlorination reaction is uniform, and molecular chain is basically free from degradation and branching in the chlorination process. The product has the advantages of high chlorine content and easy control and adjustment of chlorine content, fast chlorination speed, complete reaction, high mechanical strength of the product, high utilization rate of chlorine gas, precise temperature control, green production process, and easy large-scale production.

Description

technical field [0001] The present invention relates to the technical field of new polymer materials and new techniques, and in particular to a unique production method of chlorinated polyvinyl chloride CPVC resin, that is, the twin-screw extruder is fed with microwaves and simultaneously injected with liquid chlorine to rapidly chlorinate polychlorinated polyvinyl chloride. Melt chlorination method of ethylene PVC resin. Background technique [0002] Polyvinyl chloride (English Poly Vinyl Chloride referred to as PVC) is an important general-purpose thermoplastic resin polymerized from vinyl chloride VCM monomer. From the discovery of vinyl chloride by Regnauk in France in 1835 to the realization of emulsion polymerization by Bitterfeld in 1935 and the creation of suspension polymerization by Goodrich in 1940, the industrial production of polyvinyl chloride began to develop rapidly. At present, the consumption of PVC in the world is second only to polyethylene PE. For quite ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F14/06C08F8/20C08L27/24
Inventor 肖金亭任广鸿
Owner 深圳兰品科技有限公司