Ultraviolet curing anti-anodic oxidation shielding protection printing ink

A technology for protecting ink and ultraviolet light, applied in ink, household utensils, applications, etc., can solve the problems of low film protection process efficiency, low product yield, and incompetence, and achieve excellent film release performance, fast curing speed, and attached Good effect

A technology for protecting ink and ultraviolet light, applied in ink, household utensils, applications, etc., can solve the problems of low film protection process efficiency, low product yield, and incompetence, and achieve excellent film release performance, fast curing speed, and attached Good effect

CN104817880AInactive Publication Date: 2015-08-05VITAYON FINE CHEM SCI & TECH CO LTD SHENZHEN
2 Cites 13 Cited by

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultraviolet curing anti-anodic oxidation shielding protection printing ink
  • Ultraviolet curing anti-anodic oxidation shielding protection printing ink
  • Ultraviolet curing anti-anodic oxidation shielding protection printing ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] Raw materials: based on the total weight of the ink, anhydride-modified epoxy acrylate 15%; aliphatic urethane acrylate 30%; aromatic urethane acrylate 25%; hydroxyethyl acrylate 10%; 1-hydroxy-cyclohexyl benzophenone 3%; 2,4,6-trimethylbenzoyl-diphenylphosphine oxide 1.5%; talc 15%; phthalocyanine blue 0.5%; polyether modified polydimethylsiloxane 0.3%.

[0061] Preparation method: Step 1: Stir the raw materials in the above ratio with a disperser for 1.5 hours to dissolve the initiator and mix the materials evenly; Step 2: Filter the product obtained in Step 1 to obtain the finished product.

[0062] The product hardness HB was measured, and the adhesion force was 5B. The test performance is shown in Table 1.

Embodiment 2

[0064] Raw materials: based on the total weight of the ink, 20% of anhydride-modified epoxy acrylate; 50% of aliphatic urethane acrylate derived from caprolactone long-chain polyol; 5% of aromatic urethane acrylate; 5% of isobornyl acrylate; Acrylate Phosphate 0.5%; 1-Hydroxy-Cyclohexylbenzophenone 3%; 2,4,6-Trimethylbenzoyl-Diphenylphosphine Oxide 1%; Talc 15%; Phthalocyanine Blue 0.5% ; Polyether modified polydimethylsiloxane 0.3%.

[0065] Step 1: Stir the raw materials in the above ratio with a disperser for 1.5 hours to dissolve the initiator and mix the materials evenly; Step 2: Filter the product obtained in Step 1 to obtain the finished product.

[0066] The product hardness HB was measured, and the adhesion force was 5B. The test performance is shown in Table 1.

Embodiment 3

[0068] Raw materials: 40% aliphatic urethane acrylate derived from tetrahydrofuran long-chain polyols; 20% anhydride-modified epoxy acrylate; 15% isobornyl acrylate; 1-hydroxy-cyclohexylbenzophenone, based on the total weight of the ink 2%; 2,4,6-trimethylbenzoyl-diphenylphosphine oxide 1.5%; talc 20%; phthalocyanine blue 0.5%; aminomethoxysilane 1%; base siloxane 0.3%.

[0069] Step 1: Stir the raw materials in the above ratio with a disperser for 1.5 hours to dissolve the initiator and mix the materials evenly; Step 2: Filter the product obtained in Step 1 to obtain the finished product.

[0070] The product hardness HB was measured, and the adhesion force was 5B. The test performance is shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Functional group degreeaaaaaaaaaa
adhesivityaaaaaaaaaa
Login to View More

Abstract

The invention provides an ultraviolet curing anti-anodic oxidation shielding protection printing ink, by taking total weight of a printing ink composition as a reference, the ultraviolet curing anti-anodic oxidation shielding protection printing ink comprises the following components by weight percentage: 55-80% of low polymer, 5-15% of active monomer, 3-8 parts of initiator and 15-25% of filling material; wherein the low polymer is one or two selected from aliphatic polyurethane acrylate and acid anhydride-modified epoxy acrylate. The ultraviolet curing anti-anodic oxidation shielding protection printing ink has the advantages of fast solidification speed, better adhesive force, CNC resistance, scratch resistance, immersion resistance by various cutting fluids, anodic oxidation resistance, easy stripping, no residues after film-stripping, and no base material corrosion; is suitable for aluminum material or aluminum alloy base material and plastic cement base material, and is especially suitable for an aluminum material and plastic cement-embedded composite base material.

Description

technical field [0001] The invention relates to the technical field of surface protection ink products, in particular to an ultraviolet light-cured anti-anode shielding protection ink, which is especially suitable for composite substrates inlaid with aluminum and plastic. Background technique [0002] Ultraviolet light curing ink, also known as UV ink, is a rapidly developing green and environmentally friendly ink. Compared with traditional inks, it has instant curing, no volatile organic solvents, high production efficiency, strong film forming hardness, and solvent resistance. Good, less environmental pollution, energy saving, etc., because of its incomparable advantages over traditional solvent-based inks, it has been widely used in many fields such as cigarette packs, wine packs, cosmetic packaging, pharmaceutical packaging, and self-adhesive trademarks. [0003] Today, more and more products (such as mobile phone casings, tablet computers, etc.) are designed with metal,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
05 Aug 2015
Publication
CN104817880A
IPC
C09D11/101; C09D11/102; C09D11/107; C09D11/03
CPC
C09D11/03; C09D11/101; C09D11/102; C09D11/107
Inventors
朱婉平