Metal antirust paint

A metal antirust and coating technology, applied in the field of coatings, can solve problems such as general corrosion resistance, easy corrosion, and aesthetic impact, and achieve the effects of chemical resistance, high stability, good corrosion resistance, and good waterproof effect

Active Publication Date: 2015-08-19
湖州大周高分子材料有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing metal materials are prone to corrosion, and the surface is easily stained, which affects the appearance; coating protection is required, and the corrosion resistance of existing metal coatings is average, which cannot meet the market demand for metal coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The metal antirust coating described is made of the following materials in parts by weight: 40 parts of water-based acrylic modified epoxy resin, 5 parts of benzotriazole, 4 parts of polyorganosiloxane, ferricyanic acid 5 parts of salt, 6 parts of styrene, 8 parts of aluminum powder, 0.5 parts of nano-silver with a particle size of 20nm, 30 parts of nano-eggshell powder with a particle size of 30nm, 6 parts of aluminum tripolyphosphate, 2 parts of tetraethylamine tetrafluoroborate 3 parts of talcum powder, 5 parts of iron oxide pigment slurry, and 20 parts of water; the above-mentioned components are put into a high-speed mixing tank according to the ratio and mixed at high speed, and then extruded by a screw extruder to obtain an antibacterial powder coating.

Embodiment 2

[0020] The metal antirust coating described above is made of the following materials in parts by weight: 42 parts of water-based acrylic modified epoxy resin, 6 parts of benzotriazole, 5 parts of polyorganosiloxane, ferricyanate 6 parts, 7 parts of styrene, 9 parts of aluminum powder, 0.6 parts of nano-silver with a particle size of 25nm, 32 parts of nano-eggshell powder with a particle size of 40nm, 7 parts of aluminum tripolyphosphate, and 3 parts of tetraethylamine tetrafluoroborate , 4 parts of talcum powder, 6 parts of iron oxide pigment slurry, and 22 parts of water; the above-mentioned components are put into a high-speed mixing tank according to the proportion and mixed at high speed, and then extruded by a screw extruder to obtain an antibacterial powder coating.

Embodiment 3

[0022] The metal antirust coating described above is made of the following materials in parts by weight: 45 parts of water-based acrylic modified epoxy resin, 8 parts of benzotriazole, 7 parts of polyorganosiloxane, ferricyanate 10 parts, 12 parts of styrene, 12 parts of aluminum powder, 1 part of nano-silver with a particle size of 20nm, 35 parts of nano-eggshell powder with a particle size of 35nm, 8 parts of aluminum tripolyphosphate, 4 parts of tetraethylamine tetrafluoroborate , 6 parts of talcum powder, 8 parts of iron oxide pigment slurry, and 25 parts of water; the above-mentioned components are put into a high-speed mixing tank according to the proportion and mixed at high speed, and then extruded by a screw extruder to obtain an antibacterial powder coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Adhesionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a metal antirust paint, belonging to the technical field of paints. The metal antirust paint is prepared from the following substances in parts by weight: 40-50 parts of water-based acrylic acid modified epoxy resin, 5-10 parts of benzotriazole, 4-9 parts of polyorganosiloxane, 5-12 parts of ferricyanate, 6-15 parts of styrene, 8-15 parts of aluminum powder, 0.5-1.5 parts of nano silver with the particle size of 20-25nm, 30-40 parts of nano egg-shell meal with the particle size of 30-40nm, 6-9 parts of aluminum tripolyphosphate, 2-5 parts of tetraethylamine tetrafluoborate, 3-7 parts of talcum powder, 5-10 parts of iron oxide pigment slurry and 20-30 parts of water. The metal antirust paint is reasonable in component proportioning. The coating has the advantages of compact texture, low temperature resistance, favorable adhesiveness, favorable waterproof effect, corrosion resistance, discoloration resistance, wear resistance, favorable punching performance and favorable antimicrobial effect.

Description

technical field [0001] The invention belongs to the technical field of coatings, in particular to a metal antirust coating. Background technique [0002] Metal coatings are coatings with a metallic texture. Most of them require some form of pretreatment on the metal surface to improve the surface condition, so as to improve the adhesion of the coating and enhance the anti-corrosion protection effect on the metal substrate. Similar to traditional paint coating, before metal coating, some form of pretreatment is required on the metal surface to improve the surface condition, so as to improve the adhesion of the coating and enhance the anti-corrosion protection effect on the metal substrate. Existing metal materials have the problem of easy corrosion, and the surface is easy to be stained, which affects the appearance; it needs to be protected by coating, and the existing metal coatings have general corrosion resistance, which cannot meet the market demand for metal coatings. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/10C09D7/12C09D5/08
Inventor 龚重勇
Owner 湖州大周高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com