Highly-dispersed carbon nano-tube composite electric conduction ink

A carbon nanotube composite, conductive ink technology, applied in the direction of carbon silicon compound conductors, conductive materials, conductive materials, etc., can solve problems such as the reduction of the electrical properties of surfactants

Active Publication Date: 2015-08-26
BEIJING AGLAIA TECH DEV +1
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this way, the carbon nanoconductive film formed will reduce its electrical properties due to the non-conductivity of the surfactant.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Highly-dispersed carbon nano-tube composite electric conduction ink
  • Highly-dispersed carbon nano-tube composite electric conduction ink
  • Highly-dispersed carbon nano-tube composite electric conduction ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Modified single-walled carbon nanotube methanol solution 10ml

[0030] 1.8% PEDOT: PSS aqueous solution of conductive polymer aqueous solution 20ml

[0031] Concentrate to a volume of 15ml.

[0032] Preparation method: 0.05 g of single-walled carbon nanotubes (SWCNTs) were ultrasonically dispersed in 20 ml of methanol for 20 min to form a SWNT suspension. Put the SWCNT suspension into a UV light cleaning machine for 40 minutes to obtain SWCNT powder; put 20ml of deionized water into a single-necked flask, and then add 10ml of concentrated HNO 3 (68wt%), add 5wt% ammonium persulfate (APS) aqueous solution, mix evenly, add the purified SWCNT powder, stir with a magnet, and reflux at 120°C for 5h. The deionized water was repeatedly washed by centrifugation (7000rpm, 10min) for 3 times, and the obtained single-walled carbon nanotubes were finally ultrasonically dispersed in methanol for 20min, and then centrifuged twice, and finally 10ml of methanol dispersion of SWCNT wa...

Embodiment 2

[0035] Modified multi-walled carbon nanotube (MWCNT) ethanol solution 20ml

[0036] 1.8%PEDOT:PSS aqueous solution 20ml

[0037] Preparation method: 0.05g of MWCNT is ultrasonically dispersed in 20ml of ethanol for 20min to form a MWCNT suspension. Put this MWCNT suspension into a UV light cleaning machine for 40min. The obtained MWCNT powder was ultrasonically cleaned with 20ml of DMF and TFA mixture (9:1 / Vol) for 30-60min, centrifuged at 7000rpm, and then repeated ultrasonically for a total of 5 times. Finally, ultrasonically dispersed with ethanol for 20min, and then centrifuged , repeated twice, and finally 20ml of ethanol dispersion of MWCNT was obtained.

[0038] Mix 20ml of 1.8% PEDOT:PSS with 10ml of MWCNT ethanol dispersion evenly, and concentrate to 15ml (weighing about 15 grams), to form a uniformly dispersed MWCNT / PEDOT:PSS ink solution.

Embodiment 3

[0040] Modified SWCNT methanol 10ml

[0041] 1.8%PEDOT:PSS aqueous solution 20ml

[0042]Preparation method: 0.05 g of single SWNT is dispersed in 20 ml of methanol, and the SWNT suspension is formed after ultrasonic dispersion for 20 min. Put the SWNT suspension into a UV light cleaning machine for 40 minutes to obtain SWNT powder; take 20ml of concentrated sulfuric acid and put it into a single-necked flask, add the purified single-wall SWNT powder, stir magnetically, and swell at room temperature for 12 hours. After diluting the mixed concentrated sulfuric acid solution of SWNT with 10:1 water, the centrifugation was carried out and repeated 4 times. Finally, a single-walled SWNT powder is obtained. Put this powder into a single-necked flask, add 20ml of deionized water, and then add 10ml of concentrated HNO 3 (68wt%), add 10ml H 2 o 2 , magnetic stirring, reflux reaction at 85°C for 5h. Repeated centrifugal washing (7000rpm, 10min) with deionized water for 3 times, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A high-dispersion carbon nanotube composite conductive ink, consisting of modified carbon nanotubes, conductive polymeric material, and solvent; said modified carbon nanotubes being obtained from conventional carbon nanotubes that have been irradiated on a UV bench and then oxidized by a strong acid. Carbon nanotubes obtained via this process do not require, when preparing conductive composite ink, the addition of a surfactant to increase the dispersibility of the ink, such that the conductive layer obtained therefrom has good conductive properties, optical transmittance within the visible light range, and flexibility. The conductive properties of this flexible carbon nanotube polymeric transparent conductive film are world class, and the invention has good prospects for application.

Description

technical field [0001] The invention relates to a conductive ink added with carbon nanotubes, in particular to a composite conductive ink with highly dispersed carbon nanotubes. Background technique [0002] In liquid crystal panels, OLED panels, touch screens, electronic paper, solar cells and other display devices and photovoltaic devices, transparent electrodes are an indispensable part. Indium tin oxide (ITO) forms an ITO thin film on a glass substrate showing excellent light transmission and conductivity, so it currently occupies a dominant position in the application field of commercial transparent electrodes. However, with the development of science and technology and the diversification of transparent electrode application fields, transparent electrodes must have low square resistance, good transmittance in the visible light range, flexibility, and a simple operation process that can realize large-area fine coating and film formation. However, the inflexibility of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/52
CPCH01B1/06C09D11/52C08G2261/3223C08G2261/512C08G2261/794C08G2261/91C08G2261/95C08K3/041C08K2201/001C09D165/00H01B1/04H01B1/127H01B1/128C08L25/18C08K7/06
Inventor 郝海燕曹西亮戴雷蔡丽菲
Owner BEIJING AGLAIA TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap