A kind of glazed tile made of Suzhou soil

A technology of glazed tiles and green bodies, which is applied in the field of glazed tiles, can solve problems such as insufficiently rich and stable color rendering, insufficient product quality, and insufficient glaze gloss, and achieve optimal water absorption and air permeability, bright and bright colors, and low cost. Effect

Active Publication Date: 2017-01-04
浙江嘉苑园艺景观有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Existing glazed tiles are usually fired with a mixture of various mud materials. The glaze layer is generally thick and produces stress. The quality is heavy, and it is easy to cause cracks and cracks on the glazed surface of the product.
Not smooth enough, and the mud is prone to pollution in the production process, high cost and energy consumption, the quality of the product is not stable enough, the gloss of the glaze is not enough, and the color is not rich and stable enough. Fades easily in sunlight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A glazed tile made of Suzhou soil,

[0030] The glazed tile green body is composed as follows in parts by weight:

[0031] 110 parts of Suzhou soil; 25 parts of corundum powder; 9 parts of albite; 5 parts of quartz; 5 parts of fused magnesia; 5 parts of organic fiber; 5 parts of phenolic resin; 5 parts of starch; 5 parts of rice husk;

[0032] This glazed tile glaze composition by weight is as follows,

[0033] Iron oxide yellow 45 parts; yttrium stabilized zirconia 5 parts; feldspar powder 5 parts; nano zinc oxide 5 parts; silicon carbide 5 parts; carbon fiber 5 parts; tin dioxide 5 parts; TEOS 5 parts; polytetrafluoroethylene 5 parts;

[0034] The chemical composition of Suzhou soil is: SiO 2 48wt%, Al 2 o 3 39wt%, CaO 7%, other components 6wt%.

[0035] The particle size of corundum powder is less than 1 μm.

[0036] Its preparation method is as follows:

[0037] (1) Mixing: weighing, crushing and sieving the raw materials of the glazed tile body, adding wat...

Embodiment 2

[0043] A glazed tile made of Suzhou soil,

[0044] The glazed tile green body is composed as follows in parts by weight:

[0045] 112 parts of Suzhou soil; 26 parts of corundum powder; 8 parts of albite; 5 parts of quartz; 4 parts of fused magnesia; 5 parts of organic fiber; 4 parts of phenolic resin; 5 parts of starch; 5 parts of rice husk;

[0046] This glazed tile glaze composition by weight is as follows,

[0047] Iron oxide yellow 46 parts; yttrium stabilized zirconia 5 parts; feldspar powder 2 parts; nano zinc oxide 2 parts; silicon carbide 5 parts; carbon fiber 5 parts; tin dioxide 2 parts; TEOS 5 parts; polytetrafluoroethylene 5 parts;

[0048] The chemical composition of Suzhou soil is: SiO 2 48wt%, Al 2 o 3 39wt%, CaO 7%, other components 6wt%.

[0049] The particle size of corundum powder is less than 1 μm.

[0050] Its preparation method is as follows:

[0051] (1) Mixing: weighing, crushing and sieving the raw materials of the glazed tile body, adding wat...

Embodiment 3

[0057] A glazed tile made of Suzhou soil,

[0058] The glazed tile green body is composed as follows in parts by weight:

[0059] 109 parts of Suzhou soil; 22 parts of corundum powder; 9 parts of albite; 5 parts of quartz; 5 parts of fused magnesia; 5 parts of organic fiber; 5 parts of phenolic resin; 5 parts of starch; 5 parts of rice husk;

[0060] This glazed tile glaze composition by weight is as follows,

[0061]Iron oxide yellow 42 parts; yttrium stabilized zirconia 5 parts; feldspar powder 2 parts; nano zinc oxide 2 parts; silicon carbide 2 parts; carbon fiber 5 parts; tin dioxide 5 parts; TEOS 2 parts; polytetrafluoroethylene 2 parts;

[0062] The chemical composition of Suzhou soil is: SiO 2 48wt%, Al 2 o 3 39wt%, CaO 7%, other components 6wt%.

[0063] The particle size of corundum powder is less than 1 μm.

[0064] Its preparation method is as follows:

[0065] (1) Mixing: weighing, crushing and sieving the raw materials of the glazed tile body, adding wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a glazed tile produced from Suzhou clay. The blank of the glazed tile is composed of Suzhou clay, corundum powder, albite, quartz, fused magnesia, organic fibers, phenolic resin, starch and rice husk; and the glaze of the glazed tile is composed of iron oxide yellow, yttria-stabilized zirconia, feldspar powder, nanometer zinc oxide, silicon carbide, carbon fibers, tin dioxide, TEOS and polytetrafluoroethylene. The surface of the glazed tile is smooth and clean, and has brilliant and bright color, and the glazed tile has excellent compression, fire, acid and alkali resistance, and also has the advantages of light mass, low water absorption rate, good permeability and low cost.

Description

technical field [0001] The invention belongs to the field of glazed tiles, in particular to a glazed tile prepared from Suzhou soil. Background technique [0002] Glazed tile is an ancient and traditional ceramic material in my country. With the development of tourism, people's demand for glazed tiles is also increasing, and their requirements are also getting higher and higher. [0003] Glazed tiles, solid materials, bright colors, and smooth glaze, have always been used as traditional Chinese building components. After successive developments and quality improvements, they have been widely used in modern buildings due to their various excellent functions. [0004] Existing glazed tiles are usually made by mixing and firing various mud materials. The glaze layer is generally thick and stress is generated, and the quality is heavy, which easily leads to defects such as cracks and chipping on the glazed surface of the product. Not smooth enough, and the mud is prone to poll...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C03C8/04
Inventor 张锋超
Owner 浙江嘉苑园艺景观有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com