Modified (methyl) acrylate resin and preparation method

A technology of methyl methacrylate and acrylate, which is applied in the field of multi-curable silicone modified (meth)acrylate resin and its preparation, can solve the problems of wear resistance and poor toughness, reduce brittleness, increase Flexibility, the effect of reducing curing shrinkage

Active Publication Date: 2015-10-07
CHINA LUCKY FILM CORP +1
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The resin can maintain the hardness, gloss, chemical corrosion resistance and other properties of (meth)acrylate r

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified (methyl) acrylate resin and preparation method
  • Modified (methyl) acrylate resin and preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0067] The preparation method of resin of the present invention comprises the following steps:

[0068] (1) Preparation of (meth)acrylate, glycidyl (meth)acrylate and silicone copolymer intermediates

[0069] Under the condition of passing inert gas, heat the solvent 1 to 60°C-90°C, slowly add the mixture of monomer 1, monomer 2, initiator, molecular weight regulator, and organosilicon containing double bonds, for 1 hour- The addition is completed in 6 hours; the system is kept warm for 2 hours to 10 hours, the temperature is raised to 100°C-130°C, and the temperature is kept for 0.5-4 hours to obtain a copolymer intermediate.

[0070] (2) Preparation of modified (meth)acrylate resin

[0071] Lower the temperature of the copolymer intermediate obtained in step (1) to below 60°C, pass air or other gases containing oxygen, add monomer 3, polymerization inhibitor, catalyst, then raise the temperature to 70°C-100°C, and keep it warm for 2 hours After -10 hours, the temperature o...

Embodiment 1

[0087] Synthesis of modified (meth)acrylate resin intermediates

[0088] In the reaction device equipped with a stirrer, condenser tube, nitrogen gas introduction tube, and thermometer, nitrogen gas is passed, 300 parts of butyl acetate are added, the temperature is raised to 80°C, the air in the reaction device is fully removed, and 300 parts of pre-configured Glycidyl methacrylate (hereinafter referred to as GMA), 75 parts of methyl methacrylate (hereinafter referred to as MMA), 37 parts of γ-methacryloxypropyl trimethoxysilane, 12 parts of azobisiso A mixed solution composed of butyronitrile (hereinafter referred to as AIBN) and 1.5 parts of lauryl mercaptan (hereinafter referred to as DDM) was slowly added dropwise for 3 hours and kept warm for 5 hours. Then, the mixture in the reaction device was blown into nitrogen. Raise the temperature to 120° C., keep the temperature for 2 hours, and cool down to obtain a modified (meth)acrylate resin intermediate.

[0089] Preparati...

Embodiment 2

[0092] Synthesis of modified (meth)acrylate resin intermediates

[0093] In the reaction device equipped with a stirrer, condenser tube, nitrogen gas inlet tube, and thermometer, nitrogen gas is passed, 300 parts of butyl acetate are added, the temperature is raised to 60°C, the air in the reaction device is fully removed, and 85.7 parts of pre-configured A mixed solution composed of GMA, 226 parts of MMA, 37 parts of γ-methacryloxypropyltrimethoxysilane, 12 parts of AIBN, and 1.5 parts of DDM was slowly added dropwise for 6 hours and kept warm for 2 hours. Then, the reaction device The mixture in the mixture was heated to 130° C. under the condition of feeding nitrogen gas, kept at a temperature of 0.5 hour, and cooled to obtain a modified (meth)acrylate resin intermediate.

[0094] Synthesis of modified (meth)acrylate resin

[0095] Cool the above resin intermediate to 60°C, blow in air, add the pre-configured 10.9 parts of AA, 0.4 parts of MEHQ, 0.5 parts of TPP mixed solu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses modified (methyl) acrylate resin. The resin contains a (methyl) acrylate chain link, an unsaturated double bond and carboxylic group, an unsaturated double bond and epoxy group and an organic silicon group containing double bonds. The modified (methyl) acrylate resin can be solidified through various methods, has the characteristics of high hardness, high toughness, no adhesion, strong adhering force, good wear resistance and the like, and can be applied to fields such as coating, ink and adhesive. The invention further relates to a preparation method of the material.

Description

technical field [0001] The invention belongs to the technical field of organic polymer synthesis, and in particular relates to a multi-curable silicone-modified (meth)acrylate resin and a preparation method thereof. The resin can be applied to heat, ultraviolet light, moisture, and air-cured Coatings, adhesives, inks and other fields. Background technique [0002] In the prior art, various (meth)acrylate heat-curable and UV-curable resins have been proposed. The cured resin has fast light curing, high hardness of the coating film, good adhesion, good gloss, and chemical resistance. Corrosion and other advantages. [0003] (Meth)acrylate resins cured in two or more ways can generally achieve ideal results, but there is a problem of easy adhesion after one curing, and increasing the molecular weight will increase the viscosity and bring inconvenience to construction. An increase in the degree of crosslinking reduces the toughness. Adding a release layer can solve the above ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F220/14C08F220/18C08F220/28C08F220/06C08F220/04C08F230/08
Inventor 李娜姜伟张占国左志和滕领贞成志秀吕硕千昌富
Owner CHINA LUCKY FILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap