Silver wear-resisting powder coating and manufacturing and using methods thereof

A powder coating, silver technology, applied in the direction of powder coating, polyester coating, epoxy resin coating, etc., can solve the problems of poor scratch resistance and poor gloss, and achieve the effect of improved performance and good gloss

Inactive Publication Date: 2015-10-07
苏州普勒新材料有限公司
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Existing silver powder coatings have poor scratch resistance and poor gloss

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Silver wear-resistant powder coating of the present invention, comprises component and the mass percent of component is: epoxy resin 28, polyester resin 42, leveling agent 1, wetting agent 0.7, benzoin 0.5, barium sulfate 24, increaser Hardener 0.3, Charger 0.4, Silver Powder Alignment Agent 0.6, Titanium Dioxide 2, Carbon Black 0.02.

[0021] The preparation method of described silver wear-resistant powder coating, comprises the following steps:

[0022] ①Weigh according to the proportion of the formula of the silver wear-resistant powder coating, and pre-mix for 5 minutes;

[0023] ②Extrusion by extruder, in which the temperature of zone I of the extruder is 120°C, the temperature of zone II is 125°C, and the speed of the main engine is 30HZ; the premixed raw materials in ① are extruded through the extruder;

[0024] ③Flour milling, wherein the main milling speed of the milling machine is 50HZ, the auxiliary milling speed is 28HZ, and the mesh size of the screen is 1...

Embodiment 2

[0030] The silver wear-resistant powder coating of the present invention comprises components and the mass percentages of components are: epoxy resin 30, polyester resin 40, leveling agent 1.2, wetting agent 0.7, benzoin 0.6, barium sulfate 23.485, Hard agent 0.4, charging agent 0.3, silver powder alignment agent 0.8, titanium dioxide 2.5, carbon black 0.015.

[0031] The preparation method of described silver wear-resistant powder coating, comprises the following steps:

[0032] ①Weigh according to the proportion of the formula of the silver wear-resistant powder coating, and pre-mix for 5 minutes;

[0033] ②Extrusion by extruder, in which the temperature of zone I of the extruder is 120°C, the temperature of zone II is 125°C, and the speed of the main engine is 30HZ; the premixed raw materials in ① are extruded through the extruder;

[0034] ③Flour milling, wherein the main milling speed of the milling machine is 50HZ, the auxiliary milling speed is 28HZ, and the mesh size ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a silver wear-resisting powder coating. The silver wear-resisting powder coating comprises, by mass, 25-30 parts of epoxy resin, 40-50 parts of polyester resin, 0.5-1.5 parts of flatting agent, 0.5-0.8 part of wetting agent, 0.3-0.6 part of benzoin, 20-25 parts of barium sulfate, 0.3-0.5 part of hardening agent, 0.2-0.5 part of charging additive, 0.5-0.8 part of silver powder directional alignment agent, 2-3 parts of titanium dioxide and 0.01-0.03 part of carbon black. The surface of the silver wear-resisting powder coating can be as hard as Zhonghua pencils 5H in use, the scratch resistance of the surface is improved greatly, and meanwhile, surface glossiness is high.

Description

technical field [0001] The invention relates to a silver wear-resistant powder coating capable of improving the anti-scratch performance of the silver surface and a method for making and using the same. Background technique [0002] Paint is a material that is applied to the surface of the object to be coated and can form a firmly adhered continuous film. [0003] The invention relates to a powder coating, which is a coating containing 100% solid content, and has the characteristics of no solvent, no pollution, saving energy and resources, reducing labor intensity and high mechanical strength of the coating film. [0004] Powder coatings are widely used in: 1. Decorative protective coating, used for housings and parts of household appliances, metal furniture, automobiles, instruments, bicycles, sewing machines, electromechanical equipment, light industrial equipment, agricultural machinery, construction hardware, etc. ;2. Insulation and moisture-proof coating, applied to tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D163/00C09D7/12C09D5/03B05D3/02
CPCC09D167/00B05D3/02C09D5/033
Inventor 袁文荣
Owner 苏州普勒新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com