A packaging material, pearl cotton technology, applied in the field of packaging materials, can solve the problems of increasing energy consumption, etc., and achieve the effect of light weight, high strength and strong toughness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0028] A pearl cotton packaging material is made of the following raw materials in parts by weight: 80 parts of low-density polyethylene (LDPE), 15 parts of foaming agent, 10 parts of dispersant, 3 parts of antioxidant, 4 parts of active agent, 15 parts of luminous powder share. in
[0029] The foaming agent is a mixture of 3,3-disulfonyl hydrazide diphenyl sulfone, OBSH and p-toluenesulfonyl hydrazide (TSH) in a weight ratio of 1:1.5:2, and the dispersant is vinyl bishard Fatty amide, the antioxidant is butyl hydroxyanisole, dibutyl hydroxytoluene (BHT), tert-butyl hydroquinone (TBHQ) mixed in a weight ratio of 1:2.5:1, the active agent It is fatty alcohol polyoxyethylene ether, and further, the luminous powder is zinc sulfide.
[0030] The method for preparing above-mentioned pearl cotton packing material is:
[0031] 1) Put low-density polyethylene into a stirring device, heat up to 250°C, and then stir at a speed of 2500r / min for 50min to obtain melt A, which is set asi...
Embodiment 2
[0038] A pearl cotton packaging material is made of the following raw materials in parts by weight: 100 parts of low-density polyethylene (LDPE), 20 parts of foaming agent, 5 parts of dispersant, 5 parts of antioxidant, 5 parts of active agent, and 10 parts of luminous powder share. in
[0039] Described whipping agent is p-(N-methoxy formamido) benzene sulfonyl hydrazide, and described dispersant is oleic acid acyl, and described antioxidant is butyl hydroxyanisole, dibutyl hydroxy toluene (BHT) 1. Tertiary butyl hydroquinone (TBHQ) is mixed according to the weight ratio of 1.5:1.2:1, the active agent is fatty alcohol polyoxyethylene ether, and the luminous powder is zinc sulfide.
[0040] The preparation method of above-mentioned pearl cotton packing material, comprises the following steps:
[0041] 1) Put the low-density polyethylene into a stirring device, heat up to 200°C, and then stir at a speed of 3500r / min for 30min to obtain a melt A for later use;
[0042] 2) Put...
Embodiment 3
[0048] A pearl cotton packaging material is made of the following raw materials in parts by weight: 90 parts of low-density polyethylene (LDPE), 10 parts of foaming agent, 8 parts of dispersant, 5 parts of antioxidant, 1 part of active agent, 12 parts of luminous powder share. in
[0049] The blowing agent is p-toluenesulfonyl hydrazide (TSH), 2,4-toluene disulfonyl hydrazide and p-(N-methoxyformylamino) benzenesulfonyl hydrazide mixed in a weight ratio of 1.5:2.5:1 Forming, described dispersant is glyceryl tristearate, and described antioxidant is butyl hydroxyanisole, dibutyl hydroxytoluene (BHT) and tert-butyl hydroquinone (TBHQ) by 1.2:2: 1 by weight, the active agent is fatty alcohol polyoxyethylene ether, and the luminous powder is zinc sulfide.
[0050] The preparation method of above-mentioned pearl cotton packing material, comprises the following steps:
[0051] 1) Put the low-density polyethylene into a high-temperature stirring device, raise the temperature to 220°...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com