A production process of modified high-strength rubber wood floor

A rubber wood, high-strength technology, used in wood processing appliances, wood treatment, manufacturing tools, etc., can solve problems such as poor environmental protection, and achieve the effects of stable size, beautiful color, and environmentally friendly process

Active Publication Date: 2017-10-03
石家庄朗宁体育用品科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after being treated with resin, the environmental protection is much worse
Treatment with boric acid does not solve the problem of large strength loss of rubber wood after heat treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A production process of modified high-strength rubber wood floor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A method for producing high-strength heat-modified rubber wood flooring, comprising the steps of:

[0024] (1) Timber preparation: sawing rubber wood logs into squares or blanks;

[0025] (2) Vacuum impregnation treatment: put the wooden side or billet stack into the vacuum treatment tank, use boric acid and acetic acid aqueous solution as the treatment solution for vacuum pressure impregnation; wherein the treatment solution is, according to the mass percentage, boric acid 4%, Acetic acid 1.5%; the vacuum degree of the vacuum treatment tank is 0.05, the pressurization pressure is 1.5MPa, and the pressurization time is 10min;

[0026] (3) Pre-drying: drying the wood or billets after the vacuum impregnation treatment to a moisture content of 35%;

[0027] (4) Thermal modification treatment: put the pre-dried wood or billets into the carbonization treatment equipment, use 0.2% trehalose solution as the superheated steam heat transfer medium and protective gas, and heat u...

Embodiment 2

[0031] A method for producing high-strength heat-modified rubber wood flooring, comprising the steps of:

[0032] (1) Timber preparation: sawing rubber wood logs into squares or billets;

[0033] (2) Vacuum impregnation treatment: put the wooden side or billet stack into the vacuum treatment tank, use boric acid and acetic acid aqueous solution as the treatment solution for vacuum pressure impregnation; wherein the treatment solution is, according to the mass percentage, boric acid 5%, acetic acid 1%; the vacuum degree of the vacuum treatment tank is 0.08, the pressurization pressure is 1MPa, and the pressurization time is 15min;

[0034] (3) Pre-drying: drying the wood or billets after the vacuum impregnation treatment to a moisture content of 25%;

[0035] (4) Thermal modification treatment: put the pre-dried wood or billets into the carbonization treatment equipment, use 0.3% trehalose solution as the superheated steam heat transfer medium and protective gas, and heat up a...

Embodiment 3

[0039] A method for producing high-strength heat-modified rubber wood flooring, comprising the steps of:

[0040] (1) Timber preparation: sawing rubber wood logs into squares or billets;

[0041] (2) Vacuum impregnation treatment: put the wooden side or billet stack into the vacuum treatment tank, use boric acid and acetic acid aqueous solution as the treatment solution for vacuum pressure impregnation; wherein the treatment solution is, according to the mass percentage, boric acid 4%, Acetic acid 1.4%; the vacuum degree of the vacuum treatment tank is 0.06, the pressurization pressure is 1.3MPa, and the pressurization time is 11min;

[0042] (3) Pre-drying: drying the wood or billets after the vacuum impregnation treatment to a moisture content of 30%;

[0043] (4) Thermal modification treatment: put the pre-dried wood or billets into the carbonization treatment equipment, use 0.2% trehalose solution as the superheated steam heat transfer medium and protective gas, and heat ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method for high-strength thermally-modified rubber wood floor. The production method comprises the following steps: sawing rubber logs into laminated timbers or blank; putting the laminated timbers or blank into a vacuum treatment tank, and carrying out impregnation in vacuum by taking boric acid and an acetic acid aqueous solution as a treating fluid; drying the laminated timbers or blank subjected to impregnation in vacuum until moisture content is 25-35%; stacking and putting the pre-dried laminated timbers or blank into carbonization treatment equipment, taking a 0.2-0.3% mycose solution as a superheated steam heat-transfer medium and a protective gas, increasing the temperature to 60-80 DEG C at a rate of 5-8 DEG C / min, and preserving the temperature for 2-3 hours, then heating the timers to 220-240 DEG C at a rate of 5-8 DEG C / min and preserving the temperature for 1-1.5 hours, stopping heating and cooling, and spraying steam to regulate humidity; and finally, preparing the wood floor. According to the production method, the process is environmentally-friendly, and hazardous substances such as resin and the like are not contained; and the obtained rubber wood floor is high in strength, good in termite resistance, stable in dimension and durable.

Description

technical field [0001] The invention relates to a production process of a modified high-strength rubber wood floor, which belongs to the field of wood processing. Background technique [0002] Heat Modified Wood (Heat Modified Wood), also commonly known as deep carbonized wood in my country. It refers to the use of 160-230 degrees (commonly used 180-215 degrees) to heat the wood to improve the quality of the wood and reduce the moisture absorption and water absorption of the wood. It improves dimensional stability, biological decay resistance and weather resistance, thus making a wood product with excellent performance, beautiful color and environmental friendliness. Through the control of different media and different temperatures in the production process, curing, coloring, surface burning and other treatments, various products with slightly different properties can be obtained. Thermally modified wood is a real green product, although it has anti-corrosion and insect-proof...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B27M3/04B27K3/10B27K5/04B27K5/00
Inventor 蒋美琴
Owner 石家庄朗宁体育用品科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com