PVC cable material formula

A technology of cable material and PVC resin, which is applied in the direction of plastic/resin/wax insulators, organic insulators, etc. It can solve the problem that the hardness, tensile strength and elongation are not perfect, the heat resistance and cold resistance cannot be unified, and the flame retardant and other problems, to achieve the effect of improving heat resistance, improving low temperature resistance, and good weather resistance

Inactive Publication Date: 2015-11-25
HEFEI XUANMING INFORMATION TECH
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, it is generally used as the insulation layer of low-voltage (≤1KV) and medium-high voltage (6~10KV) cables. PVC plastic is also widely used due to its flame retardant, oil resistance, corona resistance, chemical corrosion resistance and good water resistance. As the sheath material of wires and cables, heat-resistant (105°C), cold-resistant, oil-resistant, flame-retardant, extra-soft an

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A kind of PVC cable material formula, by weight ratio by the suspension method loose type PVC resin of 98, the calcium carbonate stabilizer of 3.6, the dioctyl adipate plasticizer of 18, the content of plasticizer is 50PHR, the calcining of 5 Clay filler, 17 chlorinated paraffin lubricant, chlorinated paraffin content 0.8 PHR, 1 lead stearate and calcium stearate mixture antioxidant and 4 tribasic calcium sulfate and dibasic phosphorous acid Mixture colorant composition.

[0015] As a further improvement, the dioctyl adipate is replaced with dioctyl phthalate.

[0016] As a further improvement, trioctyl trimellitate is added to the plasticizer.

[0017] As a further improvement, the content of the chlorinated paraffin is between 0.8PHR-1.2PHR.

[0018] As a further improvement, the mixture of lead stearate and calcium stearate is replaced by bisphenol A

Embodiment 2

[0020] Carry out embodiment 1 by described formula, difference is: a kind of PVC cable material formula, by weight ratio by the suspension method loose type PVC resin of 100, the calcium carbonate stabilizer of 4, the dioctyl adipate of 20 Plasticizer, plasticizer content is 55PHR, calcined clay filler of 6, chlorinated paraffin lubricant, content of chlorinated paraffin is 1PHR, lead stearate and calcium stearate mixture antioxidant of 1.2 and 5 tribasic calcium sulfate and dibasic phosphorous acid mixture colorants.

Embodiment 3

[0022] Carry out embodiment 1 by described formula, difference is: a kind of PVC cable material formula, by the suspension method loose type PVC resin of 102, the calcium carbonate stabilizer of 4.4, the dioctyl phthalate of 22 The content of fat plasticizer and plasticizer is 60PHR, the calcined clay filler of 7, the chlorinated paraffin lubricant of 19, the content of chlorinated paraffin is 1.2PHR, the mixture of lead stearate and calcium stearate of 1.4 is resistant to Oxygen agent and 6 tribasic calcium sulfate and dibasic phosphorous acid mixture colorant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of cables and concretely relates to a PVC cable material formula. The PVC cable material formula comprises, by weight, 98-102 parts of PVC resin, 3.6-4.4 parts of a stabilizing agent, 18-22 parts of a plasticizer, 5-7 parts of a filler, 17-19 parts of a lubricant, 1-1.4 parts of an anti-oxidant and 4-6 parts of a coloring agent. The PVC resin is loose PVC resin obtained by a suspension method. The stabilizing agent is calcium carbonate. The plasticizer is dioctyl adipate. The filler is calcined clay. The lubricant is chlorinated paraffin. The anti-oxidant is a mixture of lead stearate and calcium stearate. The coloring agent is a mixture of tribasic calcium sulfate and dibasic phosphorous acid. The PVC cable material formula improves low temperature resistance of a cable material. Through a mixture of lead stearate and calcium stearate, low temperature resistance of the cable material is improved, weatherability is good and hardness, tensile strength and elongation are greatly improved.

Description

technical field [0001] The invention belongs to the field of cables, and more specifically, the invention relates to a PVC cable material formula. Background technique [0002] The withstand voltage and insulation resistance of PVC cable material are relatively high, but the dielectric constant and dielectric loss are relatively large. Therefore, it is generally used as the insulation layer of low-voltage (≤1KV) and medium-high voltage (6~10KV) cables. PVC plastic is also widely used due to its flame retardant, oil resistance, corona resistance, chemical corrosion resistance and good water resistance. As the sheath material of wires and cables, heat-resistant (105°C), cold-resistant, oil-resistant, flame-retardant, extra-soft and non-toxic PVC can be produced by adding special performance additives or modifiers. Cable materials to meet the needs of special wire and cable products; however, heat resistance and cold resistance cannot be unified, and generally in order to ensu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08K13/02C08K3/26C08K5/11C08K3/34C08K5/098C08K5/12H01B3/44
Inventor 马爱琳方贤军
Owner HEFEI XUANMING INFORMATION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap