Fig cutting medium and preparation method thereof

A technology of cutting substrates and figs, applied in the preparation of organic fertilizers, organic fertilizers, fertilizer mixtures, etc., can solve the problems of poor effect, inconvenient fertilization management, etc., achieve the effects of improving the growth environment, solving waste disposal problems, and increasing survival rate

Inactive Publication Date: 2015-12-02
界首市地龙养殖专业合作社
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The effect of fig cuttings is inseparable from the soil or substrate. Most farmers do not pay enough attention to the quality of the cutting land, and they still use the rough method of "cutting when they see the ground" to breed, often with poor results. Fertilization management Waiting is inconvenient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A fig cutting substrate is made of the following substances by weight:

[0024] 45 parts of river mud, 28 parts of vermicompost, 17 parts of vermiculite, 12 parts of carbonized peanut shells, 8 parts of fungal dregs, 8 parts of traditional Chinese medicine dregs, 15 parts of sucrose dregs, and 12 parts of urea.

[0025] A preparation method for fig cutting matrix, comprising the steps of:

[0026] (1) Put 45 parts of river mud in the hot sun for 3 days and then crush it to 40 meshes to obtain crushed product A for later use;

[0027] (2) Grinding 12 parts of carbonized peanut shells to obtain crushed product B for later use;

[0028] (3) Put 8 parts of fungal dregs, 8 parts of traditional Chinese medicine dregs, and 15 parts of sucrose dregs into a fermentation tank after pulverization and mixing, and inoculate the fermentation broth with an amount of 0.6 kg per cubic meter of material, and control the fermentation temperature at 50-60 ℃, after 7 days of fermentation,...

Embodiment 2

[0037] A fig cutting substrate is made of the following substances by weight:

[0038] 50 parts of river mud, 25 parts of vermicompost, 18 parts of vermiculite, 15 parts of carbonized peanut shells, 8 parts of fungal dregs, 10 parts of traditional Chinese medicine dregs, 12 parts of sucrose dregs, and 12 parts of urea.

[0039] A preparation method for fig cutting matrix, comprising the steps of:

[0040] (1) Put 50 parts of river mud in the hot sun for 5 days and then crush it to 40 meshes to obtain crushed product A for later use;

[0041] (2) Grinding 15 parts of carbonized peanut shells to obtain crushed product B for later use;

[0042] (3) Put 8 parts of fungal dregs, 10 parts of traditional Chinese medicine dregs, and 12 parts of sucrose dregs into a fermentation tank after pulverization and mixing, and inoculate 1 kg of fermented bacteria liquid per cubic meter of material, and control the fermentation temperature at 50-60 °C , after 8 days of fermentation, the ferme...

experiment example 1

[0052] Select the longan variety grapes with good growth and no disease, and make 60 cuttings with a length of 10cm and a stem thickness of 0.5-0.6cm, and divide them into two groups at random, one group is planted with the cutting substrate prepared in Example 1, and the other The group is planted with common planting soil as the control group 1. Except that the cultivation substrate is different, all the other management methods are the same. After 40 days, each branch is measured and counted. The following table is the comparison result:

[0053]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fig cutting medium and a preparation method thereof. The fig cutting medium comprises the following substances in parts by weight: 40-50 parts of river mud, 25-30 parts of wormcast, 15-20 parts of vermiculite, 10-15 parts of carbonized peanut shells, 8-10 parts of fungal residues, 5-10 parts of traditional Chinese medicine residues, 10-15 parts of cane sugar residues and 12 parts of urea. Various waste materials are used as main components of the medium, through reasonable mixing and processing, not only are material resources fully utilized, but also a problem of waste treatment is solved, and the environment is protected. The prepared medium is excellent in heat preservation, moisture retention and gas permeability; per kilogram of the medium comprises 300-400 g of organic matters and 30-50 g of NPK; the pH value is 6.5-7.5, the medium is excellent in suitability and has a higher nutritional value, the rooting rate and the survival rate of cultivated cutting slips are greatly increased, and seedlings are unified and robust, and have strong root systems.

Description

technical field [0001] The invention relates to a plant culture substrate, in particular to a fig cutting substrate and a preparation method thereof. Background technique [0002] The effect of fig cuttings is inseparable from the soil or substrate. Most farmers do not pay enough attention to the quality of the cutting land, and they still use the rough method of "cutting when they see the ground" to breed, often with poor results. Fertilization management Waiting is more inconvenient. Contents of the invention [0003] In order to solve the above problems, the present invention provides a fig cutting substrate and a preparation method thereof. The prepared substrate has reasonable components, balanced nutrition, easy-to-obtain raw materials, simple method, and the bred figs have good growth and high survival rate. [0004] The present invention is realized through the following technical solutions: [0005] A fig cutting substrate is made of the following substances by ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C05G3/00C05F17/00
CPCY02W30/40
Inventor 牛灵
Owner 界首市地龙养殖专业合作社
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap