Matt glaze and fabrication process

A matte glaze and glaze technology, applied in the field of matte glaze and production technology, can solve the problems of low production efficiency, long firing time, high firing temperature, etc., and achieve short firing time, stable glaze effect, high firing The effect of low temperature

Inactive Publication Date: 2015-12-23
MYINGFA CERAMIC CO LTD DEHUA FUJIAN
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing matt glaze has complex components, and the firing time is long, the firing temperature is high, the fuel consumption for production is relatively large, the production efficiency is relatively low, and the production cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Matte glaze, composed of transparent glaze, high expansion glaze and Suzhou kaolin in a mass ratio of 1:3:3,

[0016] The transparent glaze is made of the following raw materials according to mass percentage: 52% silicon dioxide, 14% aluminum oxide, 7% potassium feldspar, 7% albite feldspar, 6% calcium carbonate, 10% borax, barium carbonate 4%;

[0017] The high expansion glaze glaze is made of the following raw materials according to mass percentage: 38% of silicon dioxide, 15% of aluminum oxide, 7% of potassium feldspar, 4% of albite feldspar, 18% of calcium carbonate, 6% of borax, carbonic acid Barium 12%.

[0018] The production process of the above matt glaze, the specific production steps are as follows:

[0019] (1) Preparation of glaze: Grind the raw materials of the transparent glaze separately, then mix them evenly and put them into a ball mill for grinding for 4 hours; grind the raw materials of the high-expansion glaze separately, then mix them evenly and ...

Embodiment 2

[0023] Matte glaze, composed of transparent glaze, high expansion glaze and Suzhou kaolin in a mass ratio of 1:4:2,

[0024] The transparent glaze glaze is made of the following raw materials according to mass percentage: 55% silicon dioxide, 10% aluminum oxide, 8% potassium feldspar, 5% albite feldspar, 7% calcium carbonate, 8% borax, barium carbonate 7%;

[0025] The high expansion glaze glaze is made of the following raw materials according to mass percentage: 35% of silicon dioxide, 20% of aluminum oxide, 6% of potassium feldspar, 6% of albite feldspar, 15% of calcium carbonate, 8% of borax, carbonic acid Barium 10%.

[0026] The production process of the above matt glaze, the specific production steps are as follows:

[0027] (1) Glaze preparation: Grind the raw materials of the transparent glaze separately, then mix them evenly and put them into a ball mill for grinding for 5 hours; grind the raw materials of the high-expansion glaze separately, then mix them evenly an...

Embodiment 3

[0031] Matte glaze, composed of transparent glaze, high expansion glaze and Suzhou kaolin at a mass ratio of 1:5:1,

[0032] The transparent glaze glaze is made of the following raw materials according to mass percentage: 58% silicon dioxide, 6% aluminum oxide, 10% potassium feldspar, 3% albite feldspar, 9% calcium carbonate, 6% borax, barium carbonate 8%;

[0033] The high-expansion glaze glaze is made of the following raw materials according to mass percentage: 32% of silicon dioxide, 25% of aluminum oxide, 5% of potassium feldspar, 8% of albite feldspar, 12% of calcium carbonate, 10% of borax, carbonic acid Barium 8%.

[0034] The production process of the above matt glaze, the specific production steps are as follows:

[0035] (1) Glaze preparation: Grind the raw materials of the transparent glaze separately, then mix them evenly and put them into a ball mill for grinding for 6 hours; grind the raw materials of the high-expansion glaze separately, then mix them evenly an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a matt glaze and a fabrication process. The matt glaze consists of transparent glaze material, high-expansion glaze material and Suzhou kaolin clay at mass ratio. Each of the transparent glaze material and the high-expansion glaze material consists of silica, alumina oxide, potassium feldspar, albite, calcium carbonate, borax and barium carbonate. The fabrication process comprises the following steps: uniformly mixing the raw materials in proportion, then mixing the mixture with water to stir, and putting the mixture into a ball mill for ball milling so as to prepare matt glaze material; spraying and coating the matt glaze material onto the surface of a ceramic body, feeding into a baking furnace for baking, and obtaining a calcined product with a matt glaze surface effect after cooling from the kiln. The matt glaze provided by the present invention is simple in composition and reasonable in formula, and the prepared matt glaze is stable in glaze surface effect, comfortable in gloss, free of glare, smooth and is high in strength. In the fabrication process, the calcining time is short, and the sintering temperature is low, so that the power consumption is reduced, the energy is saved, the environment is protected, and the production cost is reduced.

Description

technical field [0001] The invention relates to the technical field of glaze preparation, in particular to a matt glaze and a production process. Background technique [0002] Matte glaze is a special glaze between glossy glaze and matte glaze. Its glaze surface has weak reflective ability and no glassy luster on the surface, but presents a soft silky or velvet luster. After the glaze material of matt glaze is melted at high temperature, crystals are separated out in a part of the glaze components during the cooling process. The crystals are extremely small and regularly dispersed and embedded in the glass matrix, and the light source irradiates on it to produce diffuse reflection. The existing matte glaze has complex components, and the firing time is long, the firing temperature is high, the production requires more fuel, the production efficiency is relatively low, and the production cost is high. Contents of the invention [0003] The purpose of the present invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00C04B41/86
Inventor 林建华
Owner MYINGFA CERAMIC CO LTD DEHUA FUJIAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com