Manufacturing method of low-emissivity coated laminated glass capable of removing film in peripheral area and being bent by drying
A low-radiation coating and surrounding area technology, applied in the field of coated laminated glass manufacturing, can solve the problems of difficult film removal and low removal efficiency of automotive coated glass, so as to avoid film corrosion, ensure film quality, and prevent secondary pollution effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0047] Example one
[0048] Such as figure 1 As shown, a manufacturing method of bakeable low-emissivity coated laminated glass with film removal in the peripheral area includes the following steps:
[0049] 1) Original glass pretreatment: the original green float glass with a thickness of 1.8mm is sliced, loaded, cut, edged, washed and dried to obtain automotive-grade original glass, which is called "large glass";
[0050] 2) Coating: using magnetron sputtering coating equipment to coat the surface of the automotive-grade original glass obtained in step 1) with a low-emissivity film layer, which adopts the film configuration disclosed in Chinese Patent 200810071891.4;
[0051] 3) Film removal: Input the CAD graphics of the surrounding area to be removed 2 into the system control software of the CNC (Computer Numerical Control) host. According to the thickness of the film, set the laser power to 500W and the spot diameter to 5mm. The automatic cycle is started in the software, the rob...
Example Embodiment
[0057] Example 2
[0058] A manufacturing method for bakeable low-emissivity coated laminated glass with film removal in the peripheral area, the method comprising the following steps:
[0059] 1) Original glass pretreatment: the original white float glass with a thickness of 1.8mm is sliced, loaded, cut, edged, washed and dried to obtain automotive-grade original glass, which is called "large glass";
[0060] 2) Coating: Use magnetron sputtering coating equipment to coat a low-emissivity film on the surface of automotive-grade original glass. The low-emissivity film adopts the film configuration disclosed in Chinese Patent 200810071891.4;
[0061] 3) Film removal: Input the CAD graphics of the surrounding area to be removed 2 and the area to be removed 5 of the base into the system control software of the CNC (Computer Numerical Control) host, and set the laser power to 800W according to the thickness of the film, and set the spot The diameter is 8mm, the automatic cycle is started i...
Example Embodiment
[0063] Example 3
[0064] A manufacturing method for bakeable low-emissivity coated laminated glass with film removal in the peripheral area, the method comprising the following steps:
[0065] 1) Original glass pretreatment: the original transparent float glass with a thickness of 2.1mm is sliced, loaded, cut, edged, washed and dried to obtain automotive-grade original glass, which is called "large glass";
[0066] 2) Coating: Use magnetron sputtering coating equipment to coat a low-emissivity film on the surface of automotive-grade original glass. The low-emissivity film adopts the dual silver Low-E film configuration disclosed in Chinese Patent 20092007779.4;
[0067] 3) Film removal: Input the CAD graphics of the surrounding area to be removed 2 into the system control software of the CNC (Computer Numerical Control) host. According to the thickness of the film, set the working power of the laser to 1000W, and set the spot diameter to 10mm. In the system control software Start the...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap