A kind of method that moso bamboo material prepares ecological board

A technology of ecological board and moso bamboo, which is applied in the field of building materials production, can solve the problems of uneven board surface, easy bulging of the surface of ecological board, and increase of product defective rate, so as to achieve the effects of simple production steps, cost saving and improved production efficiency

Active Publication Date: 2017-06-27
班尔奇(上海)家居科技有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem mainly solved by the present invention: Aiming at the fact that the surface of the ecological board produced by the three-time hot pressing process is easy to bulge, which makes the board surface uneven and increases the defective rate of the product, a method for preparing the ecological board from moso bamboo material is provided. The present invention Utilize the characteristics of moso bamboo material, that is, moso bamboo has many pores and has air permeability to make ecological boards. The ecological boards prepared by the present invention are not easy to bubble, resistant to pollution, and have no carbonization phenomenon. They can be produced in large quantities and improve production efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0016] First select 18m bamboo, cut it 5cm away from its roots, cut off the branches on the main stem of the bamboo pole, collect the bamboo leaves on the branches, and send the trimmed main stem to the chipper to cut into shavings with a length of 30mm , And put the shavings and bamboo leaves washed with water in the sun for 3 days, then send them to the drying kiln through a pipeline, and dry them to a moisture content of 8% for later use; then take out the dried bamboo leaves and crush them with airflow The machine is pulverized into bamboo leaf powder with a particle size of 0.18mm, and then stirred and mixed for 15 minutes according to the mass ratio of bamboo leaf powder and polyvinyl chloride resin at 1:1. After it is evenly mixed, it is placed in an internal mixer for mixing. 15min, set the banburying temperature to 90℃ and the speed of 30r / min. After the banburying is completed, take it out while hot and place it on a plate vulcanizer, press it under 15MPa for 10min, an...

example 2

[0018] First select 15m of moso bamboo, cut 3cm away from its roots, cut off the branches on the trunk of the bamboo pole, collect the bamboo leaves from the branches, and send the trimmed trunk to the chipper to cut into shavings with a length of 20mm , And put the shavings and bamboo leaves washed with water in the sun for 2 days, then send them to the drying kiln through a pipe, and dry them to a moisture content of 5% for later use; then take out the dried bamboo leaves and crush them with airflow The machine is pulverized into bamboo leaf powder with a particle size of 0.16mm, and then stirred and mixed for 10 minutes according to the mass ratio of bamboo leaf powder and polyvinyl chloride resin at 1:1. After it is uniformly mixed, it is placed in an internal mixer for mixing 10min, set the banburying temperature to 80℃, and the speed of 30r / min. After the banburying is completed, take it out while hot and place it on a plate vulcanizer, press it under 10MPa for 10min, and ...

example 3

[0020] First select 17m bamboo, cut it 4cm away from its roots, cut off the branches on the trunk of the bamboo pole, collect the bamboo leaves from the branches, and send the trimmed trunk to the chipper to cut into shavings with a length of 25mm , And put the shavings and bamboo leaves washed with water for 2 days in the sun, then send them to the drying kiln through a pipeline, and dry them to a moisture content of 7% for later use; then take out the dried bamboo leaves and crush them with airflow The machine is pulverized into bamboo leaf powder with a particle size of 0.17mm, and then stirred and mixed for 12 minutes according to the mass ratio of bamboo leaf powder and polyvinyl chloride resin at 1:1. After it is evenly mixed, it is placed in an internal mixer for mixing 12min, set the banburying temperature to 85℃ and rotating speed of 30r / min. After the banburying is completed, take it out while hot and place it on a plate vulcanizer, press it under 12MPa for 10min, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing an ecological board from a moso bamboo material, and belongs to the technical field of building material production. The present invention firstly collects the bamboo leaves and trunks on moso bamboo, beats the trunks into shavings, and then exposes them to the sun and dries them for later use. The dried bamboo leaves are crushed into bamboo leaf powder, stirred and mixed evenly with polyvinyl chloride resin, and Put it in an internal mixer and put it on a flat vulcanizer for hot pressing, take it out and cold press it to get the bamboo leaf resin layer, then crush the particle board into bamboo chips, mix with polyethylene resin, limestone powder and other substances, impregnate, Filtrate, wash with ethanol, dry, banbury, plasticize, cold press to obtain the middle layer of micro-foamed bamboo chips, and finally make the bamboo leaf resin layer into the upper and lower layers, and the middle layer is the middle layer of micro-foamed bamboo chips, and carry out hot pressing and cold press. Finally, the beneficial effects of the present invention are: no bubbling, pollution resistance, no carbonization phenomenon, mass production is possible, production efficiency is improved; production steps are simple, and cost is saved.

Description

Technical field [0001] The invention relates to a method for preparing ecological boards from moso bamboo materials, and belongs to the technical field of building material production. Background technique [0002] Eco-board is divided into two concepts: narrow and broad. In a broad sense, eco-board is equivalent to melamine veneer. Its full name is melamine-impregnated adhesive film paper veneer wood-based panel, which is to put paper with different colors or textures into eco-board resin Soaked in the adhesive and then dried to a certain degree of solidification, pave it on the surface of particleboard, moisture-proof board, medium density fiberboard or other hard fiberboard, and heat-press decorative board. Compared with traditional stickers, it has the advantages of high temperature resistance, acid and alkali resistance, moisture resistance, fire resistance, etc., and combines the functions of stickers and plywood into one, saving decoration costs and labor costs, and is wid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29D7/00C08J9/00
Inventor 吴安
Owner 班尔奇(上海)家居科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com