High peel strength adhesive for shoes

A high peeling and adhesive technology, applied in the direction of adhesives, carboxyl rubber adhesives, non-polymer adhesive additives, etc., can solve the problems of poor water resistance, slow drying, low initial adhesion, etc., and achieve good adhesion and fracture Effects of reduced elongation and increased tensile strength

Inactive Publication Date: 2016-01-13
安徽大松树脂有限公司
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with traditional solvent-based polyurethane adhesives, it ha...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present invention proposes a high peel strength adhesive for shoes, its raw materials include by weight: 90 parts of modified polyurethane, 28 parts of carboxylated styrene-butadiene rubber, 20 parts of water-soluble chlorosulfonated polyethylene, and 35 parts of water-soluble epoxy resin , 5 parts of calcium zinc stabilizer, 8 parts of anti-aging agent, 50 parts of water.

[0022] The preparation method of the modified polyurethane is as follows: add 18 parts of graphene oxide into the mixed acid solution by weight for ultrasonic treatment, wherein the mixed acid solution is composed of concentrated sulfuric acid with a mass fraction of 95wt% and concentrated nitric acid with a mass fraction of 65wt%. The ratio is 2:1.5, the frequency of ultrasonic treatment is 70kHz, the power of ultrasonic treatment is 800W, the time of ultrasonic treatment is 3h, and the first material is obtained by drying; after mixing the first material and butanone, the temperature is raised ...

Embodiment 2

[0024] A kind of high-peeling strength shoe adhesive proposed by the present invention, its raw material comprises by weight: 105 parts of modified polyurethane, 25 parts of carboxylated styrene-butadiene rubber, 23 parts of water-soluble chlorosulfonated polyethylene, 30 parts of water-soluble epoxy resin , 10 parts of calcium zinc stabilizer, 3 parts of anti-aging agent, 80 parts of water.

[0025] The preparation method of the modified polyurethane is as follows: add 15 parts of graphene oxide by weight to the mixed acid solution for ultrasonic treatment, wherein the mixed acid solution is composed of concentrated sulfuric acid with a mass fraction of 98wt% and concentrated nitric acid with a mass fraction of 60wt%. The ratio is 3:1, the frequency of ultrasonic treatment is 75kHz, the power of ultrasonic treatment is 750W, the time of ultrasonic treatment is 6h, and the first material is obtained by drying; after mixing the first material and butanone, the temperature is rai...

Embodiment 3

[0027]The present invention proposes a high-peeling-strength adhesive for shoes, whose raw materials include by weight: 95 parts of modified polyurethane, 27 parts of carboxylated styrene-butadiene rubber, 21 parts of water-soluble chlorosulfonated polyethylene, and 34 parts of water-soluble epoxy resin , 8 parts of calcium zinc stabilizer, 6 parts of anti-aging agent, 60 parts of water.

[0028] The preparation method of the modified polyurethane is as follows: add 17 parts of graphene oxide into the mixed acid solution by weight for ultrasonic treatment, wherein the mixed acid solution is composed of concentrated sulfuric acid with a mass fraction of 96 wt% and concentrated nitric acid with a mass fraction of 64 wt%. The ratio is 2.5:1.4, the frequency of ultrasonic treatment is 72kHz, the power of ultrasonic treatment is 780W, the time of ultrasonic treatment is 4h, and the first material is obtained by drying; after mixing the first material and methyl ethyl ketone, the tem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a high peel strength adhesive for shoes, wherein the raw materials comprise, by weight, 90-105 parts of modified polyurethane, 25-28 parts of carboxy styrene-butadiene rubber, 20-23 parts of water-soluble chlorosulfonated polyethylene, 30-35 parts of a water-soluble epoxy resin, 5-10 parts of a calcium zinc stabilizer, 3-8 parts of an anti-aging agent, and 50-80 parts of water, and during the modified polyurethane preparation method, graphene oxide is subjected to acidification and ultrasound treatment, the obtained material is grafted with cyclohexanedimethylene diisocyanate to obtain modified diisocyanate, and the modified diisocyanate, an anionic hydrophilic chain extender and other materials are combined to generate the modified polyurethane. According to the present invention, the high peel strength adhesive for shoes has characteristics of excellent peel resistance, high toughness and good bonding property, and adopts water as the solvent, such that the environmental protection is good, and the high peel strength adhesive can not harm the health.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to an adhesive for shoes with high peeling strength. Background technique [0002] my country is the largest producer, consumer and exporter of footwear products in the world, with an annual output of several billion pairs of shoes, accounting for more than 50% of the total global shoe production. China consumes more than 2 billion pairs of shoes every year, surpassing the United States and ranking first in the world. There are more than 20,000 shoe-making enterprises in China, of which more than 80% of the shoes produced are adhesive shoes, and the consumption of shoe glue is more than 200,000 tons. The use of adhesives has greatly improved the production efficiency of the shoe industry. [0003] The development of shoe adhesives often uses organic solvents. Organic solvents are chemically inactive in the natural environment and are not easy to be decomposed, causing huge pollu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J175/04C09J175/06C09J113/00C09J123/34C09J163/00C09J11/04C08G18/75C08G18/66C08G18/42C08G18/44C08G18/32C08G18/34
Inventor 朱立芳
Owner 安徽大松树脂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap