Method for producing wood-based artificial carbonized wood

A production method and technology of artificial charcoal, applied in the direction of manufacturing tools, charcoal burning/combustion, wood processing utensils, etc., can solve the problems of flame retardant performance, poor waterproof performance, etc., to improve waterproof performance, improve weathering resistance, and improve density. Effect

Inactive Publication Date: 2016-01-27
黄万忠
View PDF12 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the above-mentioned technical problems of artificial carbonized wood with poor flame retardancy and waterproof performance in the prior art, the technical problem to be solved by the present invention is to propose a method for producing wood artificial carbonized wood with good flame retardancy and waterproof performance and environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A method for producing wooden artificial carbonized wood, the steps are as follows:

[0035] 1. Selection: SiO of silica sol 2 The content is 40%, the particle size range is 30-70nm; the modulus of sodium silicate is 2.4; the particle size range of nano-titanium dioxide powder is 20-80nm; the mesh number of talcum powder and sodium montmorillonite is 250 mesh.

[0036] 2. Raw material processing

[0037]a) Crushing process: pine wood waste (shavings, sawn wood, wood chips, etc.) is roughly processed into 25 purpose coarse pine wood powder with a pulverizer, and then pulverized with a fine pulverizer to obtain 180 purpose fine pine wood powder;

[0038] b) Centrifugal filtration: under the state of stirring, the fine pine wood powder is dissolved in the sodium chloride solution, and after the fine pine wood powder is fully dissolved, the mixture is centrifuged, filtered, and dried, and repeated 3 times to obtain a purity rate of 95%. % fine pine wood flour;

[0039] c...

Embodiment 2

[0050] A method for producing wooden artificial carbonized wood, the steps are as follows:

[0051] 1. Selection: SiO of silica sol 2 The content is 30%, the particle size range is 20-80nm; the modulus of sodium silicate is 2.2; the particle size range of nano-titanium dioxide powder is 1-100nm; the mesh number of talcum powder and sodium montmorillonite is 200 mesh.

[0052] 2. Raw material processing

[0053] a) Crushing process: pine wood waste (shavings, sawn wood, wood chips, etc.) is roughly processed into 20 purpose coarse pine wood powder with a pulverizer, and then pulverized with a fine pulverizer to obtain 170 purpose fine pine wood powder;

[0054] b) Centrifugal filtration: under stirring state, dissolve fine pine wood powder in sodium chloride solution, after fine pine wood powder is fully dissolved, then the mixture is centrifuged, filtered, and dried, repeating 3 times to obtain a purity rate of 95.4 % fine pine wood flour;

[0055] c) Proportion stirring: a...

Embodiment 3

[0066] A method for producing wooden artificial carbonized wood, the steps are as follows:

[0067] 1. Selection: SiO of silica sol 2 The content is 50%, the particle size range is 25-75nm; the modulus of sodium silicate is 2.6; the particle size range of nano-titanium dioxide powder is 10-90nm; the mesh number of talc powder and sodium montmorillonite is 300 mesh.

[0068] 2. Raw material processing

[0069] a) Crushing process: pine wood waste (shavings, sawn wood, wood chips, etc.) is roughly processed into 30 purpose coarse pine wood powder with a pulverizer, and then pulverized with a fine pulverizer to obtain 190 purpose fine pine wood powder;

[0070] b) Centrifugal filtration: under the state of stirring, the fine pine wood powder is dissolved in the sodium chloride solution, and after the fine pine wood powder is fully dissolved, the mixture is centrifuged, filtered, and dried, and repeated 3 times to obtain a purity rate of 95%. % fine pine wood flour;

[0071] c)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for producing a wood-based artificial carbonized wood. The method comprises the following four steps: processing raw materials; carrying out hot compression molding; carbonizing; performing surface treatment. The raw materials are processed by mixing and stirring, namely, a mixture, comprising pure fine pine powder, a sodium silicate solution, silica sol, nano-titania powder, sodium lignin sulfonate, talcum powder and sodium montmorillonite based on the weight part ratio of (4-8): (2-4): (0.3-0.5): (0.1-0.3): (0.03-0.07): (0.02-0.04): (0.01-0.03), is uniformly stirred for 20 to 25min at the speed of 230-250r/min under a heating state, so as to obtain a blank with water content of 8 to 12%. The wood-based carbonized wood has the characteristics of being outstanding in flame retardant property, outstanding in waterproofing performance, and being environmental friendly; the wood-based carbonized wood is applicable to a plurality of fields, and is particularly applicable to working environments being in contact with water for a long term.

Description

technical field [0001] The invention relates to a production method of wooden artificial carbonized wood, which belongs to the technical field of wood material manufacturing. Background technique [0002] Wood is an anisotropic porous material, which not only has the characteristics of sound insulation, heat insulation, good elasticity and high strength-to-weight ratio, but also has good tactile and visual effects. Therefore, wood is often used as sound insulation materials, building construction materials and wood products. With the rapid development of economic construction and the remarkable improvement of people's living standards, people's demand for wood is increasing day by day. Although wood is a renewable resource, the speed of supply is far slower than the speed of demand, which has led to an increasingly tense contradiction between wood supply and demand. In order to alleviate the tense situation of wood, people have adopted wood-based panel measures. [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/04B27N3/12B27N1/02B27M1/06
Inventor 黄万忠
Owner 黄万忠
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap