Medical thermo-sensitive hydrogel dressing and preparation method thereof

A temperature-sensitive hydrogel and hydrogel technology, used in medical science, bandages, absorbent pads, etc., can solve the problems of intractable wounds, obvious foreign body sensation, no antibacterial properties, etc., and achieve good antibacterial repair effect. , Not easy to secondary damage, strong plasticity effect

Inactive Publication Date: 2016-02-03
SOUTHWEST UNIVERSITY
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, sterile gauze is easy to adhere to the wound, which often damages the new epithelial and granulation tissue when changing the dressing, and the patient suffers from unbearable pain.
At the same time, the sterile gauze itself has no antibacterial properties, and in the wound care, the patient often sweats, and the gauze shifts due to moisture in the adhesive tape, which needs to be replaced repeatedly. Too many closed adhesive tapes can easily cause skin allergies, itching, and blisters; when the temperature is low (such as winte

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medical thermo-sensitive hydrogel dressing and preparation method thereof
  • Medical thermo-sensitive hydrogel dressing and preparation method thereof
  • Medical thermo-sensitive hydrogel dressing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A medical temperature-sensitive hydrogel dressing, comprising the following raw material components in percentage by weight:

[0019]

[0020] The balance is water.

[0021] A preparation method of a medical thermosensitive hydrogel dressing, comprising the following steps: weighing 1% of acetic acid, 2% of chitosan and 6% of hydroxypropyl methylcellulose in the percentage by weight of raw materials, adding 30.5% by weight of water, stirring and dissolving in a water bath at 70-90°C for 10-20 minutes, cooling and stirring in an ice-water bath to prepare a viscous solution, taking 0.5% by weight of raw materials and adding sodium carbonate to the viscous The solution is stirred while being added to make the pH of the viscous solution 6.5-7.5, defoaming, and after standing still, continue to add glycerin which accounts for 60% by weight of the raw material and stir evenly to obtain a hydrogel dressing.

Embodiment 2

[0023] A medical temperature-sensitive hydrogel dressing, comprising the following raw material components in percentage by weight:

[0024]

[0025] The balance is water.

[0026] A preparation method of a medical temperature-sensitive hydrogel dressing, comprising the following steps: taking 2% acetic acid, 3% chitosan and 9% hydroxypropyl methylcellulose in weight percent of raw materials, adding 35% by weight of water, stirring and dissolving in a water bath at 70-90°C for 10-20 minutes, cooling and stirring in an ice-water bath to prepare a viscous solution, taking 1% by weight of raw materials and adding sodium carbonate to the viscous solution In the solution, the viscous solution has a pH value of 6.5-7.5, defoaming, and after standing still, continue to add glycerin which accounts for 50% by weight of raw materials and stir evenly to obtain a hydrogel dressing.

Embodiment 3

[0028] A medical temperature-sensitive hydrogel dressing, comprising the following raw material components in percentage by weight:

[0029]

[0030] The balance is water.

[0031] A preparation method of a medical thermosensitive hydrogel dressing, comprising the following steps: weighing 1% of acetic acid, 2% of chitosan and 6% of hydroxypropyl methylcellulose in the percentage by weight of raw materials, adding 26.5% by weight of water, stirring and dissolving in a water bath at 70-90°C for 10-20 minutes, cooling and stirring in an ice-water bath to prepare a viscous solution, taking 0.5% by weight of raw materials and adding sodium carbonate to the viscous solution, stirring while adding, so that the pH of the viscous solution is 6.5-7.5, defoaming, after standing still, continue to add glycerin, 2% collagen hyaluronic acid, 1% Vitamin E and 1% phenoxyethanol were stirred evenly to obtain a hydrogel dressing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of medical products, and particularly relates to a medical thermo-sensitive hydrogel dressing and a preparation method thereof. The medical thermo-sensitive hydrogel dressing comprises the following raw materials by weight: 2 to 3 percent of chitosan, 6 to 9 percent of hydroxypropyl methyl cellulose, 50 to 60 percent of glycerin, 1 to 2 percent of acetic acid, 0.5 to 1 percent of sodium carbonate, and the balance of water. The medical thermo-sensitive hydrogel dressing is liquid in storage state at room temperature, can cover a whole wound surface in a spraying manner and then jellify, and is high in plasticity and fitting property, similar to skin in modulus of elasticity, low in secondary harm possibility, suitable for trauma wounds of any shape and various types, and excellent in bacterium resisting and repairing effects on the wounds.

Description

technical field [0001] The invention belongs to the technical field of medical products, and in particular relates to a medical temperature-sensitive hydrogel dressing and a preparation method thereof. Background technique [0002] Wound healing is a complex process, which is affected by many factors, such as infection, wound pollution, autoimmunity, etc. Among them, infection is the most common factor, and infection is the main reason affecting wound healing. Therefore, it is very necessary to create a good environment for wound healing and prevent wound infection. Currently, local external application of "antibacterial drugs" and "dressings" are used for clinical treatment. "Antibacterial drugs" lead to more and more serious clinical drug resistance problems and "dressings" have no clear antibacterial effect, which makes wounds prone to infection, slow healing and scar formation. Traditional medicine clinically treats various skin injuries such as burns, wounds, scalds an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L15/28A61L15/42A61L15/44A61L26/00
Inventor 汪涛陈丽慢吴大洋
Owner SOUTHWEST UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap