Processless thermal sensitive plate used for direct printing on printer

A treatment-free, heat-sensitive technology, which is applied in the direction of photosensitive materials used in optomechanical equipment, and can solve the problems of poor developing ability and printing durability of plates

Active Publication Date: 2016-03-02
LUCKY HUAGUANG GRAPHICS +1
View PDF6 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The purpose of the present invention is to solve the shortcomings of poor developing ability and printing durability of the plate existing in the existing process-free thermal CTP plate technology. The present invention designs a process-free thermal plate that can be directly printed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processless thermal sensitive plate used for direct printing on printer
  • Processless thermal sensitive plate used for direct printing on printer
  • Processless thermal sensitive plate used for direct printing on printer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0074] Example 1 (copolymer P01)

[0075] Add 333.3g of methyl ethyl ketone and 10g (10% by weight) of example compound D2 (n about 60) into a 1000ml four-necked flask equipped with temperature-controlled heating, mechanical stirring, reflux and nitrogen protection device, heat and stir evenly, and add dropwise at 90°C 70g (70% by weight) St (styrene), 10g (10% by weight) AN (acrylonitrile), 10g (10% by weight) example compound C2, 0.7g benzoyl peroxide BPO, adding time 20 minutes, and then After 7.5 hours of reaction, add 0.3g of benzoyl peroxide BPO, and continue to react for another 12 hours before ending. See attached table 1 for performance.

Embodiment 2

[0076] Embodiment 2 (copolymer P02)

[0077] Add 344.8g of methyl ethyl ketone and 10g (10% by weight) of the exemplary compound D4 (n about 50) into a 1000ml four-necked flask with temperature-controlled heating, mechanical stirring, reflux and nitrogen protection device, heat and stir evenly, and add dropwise at 80°C 60g (60% by weight) St (styrene), 20g (20% by weight) AN (acrylonitrile), 10g (10% by weight) of example compound C3, 0.7g of AIBN (azobisisobutyronitrile), and the addition time was 20 minutes After another 7.5 hours of reaction, 0.3g of AIBN (azobisisobutyronitrile) was added, and the reaction was continued for another 12 hours.

Embodiment 3

[0078] Embodiment 3 (copolymer P03)

[0079] Add 384.6g of methyl ethyl ketone and 10g (10% by weight) of example compound D4 (n about 40) into a 1000ml four-necked flask equipped with temperature-controlled heating, mechanical stirring, reflux and nitrogen protection device, heat and stir evenly, and add dropwise at 80°C 50g (50% by weight) St (styrene), 30g (30% by weight) AN (acrylonitrile), 10g (10% by weight) of example compound C2, 0.7g of AIBN (azobisisobutyronitrile), adding time 20 minutes After another 7.5 hours of reaction, 0.3g of AIBN (azobisisobutyronitrile) was added, and the reaction was continued for another 12 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thermal decomposition temperatureaaaaaaaaaa
Average roughnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a processless thermal sensitive plate used for direct printing on a printer. The processless thermal sensitive plate comprises a support body, a thermal sensitive layer and a protective layer, wherein the thermal sensitive layer mainly comprises 30-70% of water soluble thermo-crosslinking polymer, 1-15% of cross-linking agent, 10-30% of polyfunctional group monomer, 1-20% of thermal sensitive initator and 1-20% of infrared light radiation absorbing dye according to percentage by weight based on the composition solid total weight. The shortcomings of low plate developing capacity and bad printing durability in the existing processless thermal sensitive CTP (computer to plate) technology are solved.

Description

technical field [0001] The invention belongs to the technical field of lithographic printing, and relates to a heat-sensitive plate that can be directly printed on a machine without processing. Background technique [0002] Lithographic printing technology has moved from traditional laser phototypesetting film copying PS plate technology to computer-to-plate technology (CTP technology for short), and CTP plate materials are gradually becoming popular. There are many types of CTP plates, and the more popular ones include silver salt diffusion CTP plates, UV-CTP plates, purple laser polymerization CTP plates, thermal CTP plates, etc. The most widely used one is thermal CTP plate. [0003] CTP plate making technology requires a development process with a developer containing a variety of toxic organic substances or strong alkalis, and there are environmental problems caused by the treatment of toxic and harmful waste liquids. At present, the development of a new generation of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G03F7/004
Inventor 宋小伟张刚高峰杨青海许文然李喜乐刘阳孙国敏
Owner LUCKY HUAGUANG GRAPHICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap