Preparation method of synthetic grease dispersed vanadium boride boron carbide-carbon fiber friction material

A technology of vanadium boride, boron carbide and friction material, which is applied in the field of friction material preparation, can solve the problems of reduced friction performance and potential safety hazards, and achieve the effect of improving wear resistance and high manufacturing cost

Inactive Publication Date: 2017-12-15
SHANDONG UNIV OF TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the friction performance of C / C composite materials will be reduced in a humid environment, which will bring serious safety hazards to the use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] (1) Set the density to 1.8g / cm 3 The graphitized carbon fiber blanket is fed with a mixed gas of propane gas and nitrogen at a temperature of 900°C. The molar ratio of propane gas: nitrogen is 1:4, the flow rate is controlled at 50ml / min, and the carburizing treatment is performed for 24 hours to obtain a carburized carbon fiber blanket. ;

[0020] (2) Pass the above-mentioned carburized carbon fiber blanket into a mixed gas of boron trichloride, methane, hydrogen and argon at a temperature of 900 °C, and the molar ratio of boron trichloride: methane: hydrogen: argon is 1:1: 3:4, the flow rate is controlled at 50ml / min, and the deposited boron carbide is treated for 24 hours to obtain a deposited boron carbide carbon fiber blanket;

[0021] (3) Immerse the above-mentioned deposited boron carbide carbon fiber blanket into a grease slurry with a particle size of less than 0.3 μm and a content of 5% vanadium boride, place it in an ultrasonic cleaner and fill it with vanad...

Embodiment 2

[0025] (1) Set the density to 0.8g / cm 3 The graphitized carbon fiber blanket is fed with a mixture of propane gas and nitrogen at a temperature of 1000°C. The molar ratio of propane gas: nitrogen is 1:5, the flow rate is controlled at 350ml / min, and the carburizing treatment is performed for 18 hours to obtain a carburized carbon fiber blanket. ;

[0026] (2) Pass the above-mentioned carburized carbon fiber blanket into a mixed gas of boron trichloride, methane, hydrogen and argon at a temperature of 1000 °C, and the molar ratio of boron trichloride: methane: hydrogen: argon is 1:1.5: 4.5:5, the flow rate is controlled at 350ml / min, and the deposited boron carbide is treated for 18 hours to obtain a deposited boron carbide carbon fiber blanket;

[0027] (3) Immerse the above-mentioned deposited boron carbide carbon fiber blanket into a grease slurry with a particle size of less than 0.3 μm and a content of 12% vanadium boride, place it in an ultrasonic cleaner and fill it wit...

Embodiment 3

[0031] (1) Set the density to 0.1g / cm 3 The graphitized carbon fiber blanket is passed into a mixed gas of propane gas and nitrogen at a temperature of 1100 ° C. The molar ratio of propane gas: nitrogen is 1: 6, the flow rate is controlled at 600ml / min, and the carburizing treatment is performed for 10 hours to obtain a carburized carbon fiber blanket. ;

[0032] (2) Pass the above-mentioned carburized carbon fiber blanket into a mixed gas of boron trichloride, methane, hydrogen and argon at a temperature of 1100 °C, and the molar ratio of boron trichloride: methane: hydrogen: argon is 1:2: 6:6, the flow rate is controlled at 600 ml / min, and the deposited boron carbide is treated for 10 hours to obtain the deposited boron carbide carbon fiber blanket;

[0033] (3) Immerse the above-mentioned deposited boron carbide carbon fiber blanket into a grease slurry with a particle size of less than 0.3 μm and a content of 20% vanadium boride, place it in an ultrasonic cleaner and fill...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparing method for a synthetic fat dispersed vanadium boride boron carbide-carbon fiber friction material. The preparing method is characterized in that a graphited carbon fiber blanket with the density being 0.1-1.8 g / cm<3> is subjected to boron carbide deposition treatment after being subjected to carburizing treatment, then synthetic fat dispersed vanadium boride filling treatment is carried out, then burying siliconizing treatment is carried out, and then nitridation treatment is carried out in nitrogen atmosphere, so that the synthetic fat dispersed vanadium boride boron carbide-carbon fiber friction material is prepared. According to the method, the graphited carbon fiber blanket is adopted for being subjected to carburization, silicon carbide deposition, vanadium boride filling, burying siliconizing, nitridation and the like to prepare the friction material, and the prepared friction material is high in strength, toughness and friction performance, and capable of adapting to various weather conditions.

Description

technical field [0001] The invention relates to a preparation method of a friction material composited by carbon fiber and ceramic material, and belongs to the technical field of composite material preparation. Background technique [0002] At present, carbon fiber and carbon (C / C) composite materials are mainly used as friction materials. Since the wear resistance of C / C composite materials is relatively low, people are looking for a method for preparing friction materials with higher wear resistance. In addition, the friction performance of C / C composite materials will be reduced in a humid environment, which will bring serious safety hazards to the use. Contents of the invention [0003] The object of the present invention is to provide a method for preparing a friction material that can overcome the above-mentioned defects, achieve higher strength, higher friction performance and adapt to various climatic conditions. Its technical solution is: [0004] The preparatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/00C04B35/80C04B35/58C04B35/563C04B35/573C04B35/591C04B35/65C04B35/622C04B35/632
CPCC04B35/563C04B35/573C04B35/58064C04B35/591C04B35/622C04B35/632C04B35/806C04B38/00C04B2111/00362C04B2111/40C04B2235/46C04B2235/48C04B2235/5248C04B2235/5256C04B2235/616C04B2235/6567C04B2235/658
Inventor 唐竹兴
Owner SHANDONG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com