A high-performance polyurethane pressure-sensitive adhesive

A high-performance polyurethane technology, applied in polyurea/polyurethane adhesives, adhesives, grafted polymer adhesives, etc., can solve problems such as low adhesion, low performance, and insufficient balance. Achieve the effect of solving poor performance, high performance and simple preparation

Active Publication Date: 2018-06-05
新图美(台山)标签材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polyurethane pressure-sensitive adhesive is non-toxic, does not pollute the environment, and saves energy. However, the current polyurethane pressure-sensitive adhesive has low performance, low adhesion and poor balance. Therefore, we propose a high-performance polyurethane pressure-sensitive adhesive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A high-performance polyurethane pressure-sensitive adhesive, comprising the following raw materials in parts by weight: 70 parts of neoprene, 60 parts of methyl methacrylate, 60 parts of hydroxyl polysiloxane, 30 parts of xylene resin, 30 parts of polyisocyanate, and 20 parts of carbon fiber 20 parts of vinyl resin, 10 parts of azo compound blowing agent, 10 parts of rosin resin, 9 parts of triethylamine, 5 parts of methylpentynol, 5 parts of polybutadiene, 1 part of dibutyltin dilaurate, 0.5 parts of N-methylolacrylamide;

[0019] Its preparation method comprises the following steps:

[0020] S1, take 70 parts of chloroprene, 60 parts of methyl methacrylate, 60 parts of hydroxy polysiloxane, 30 parts of xylene resin, and 30 parts of polyisocyanate according to the proportion of the parts, add them to the reactor, and raise the temperature of the reactor Up to 60°C and fully stirred for 1 hour to obtain component A;

[0021] S2, weigh 20 parts of carbon fiber, 20 part...

Embodiment 2

[0025] A high-performance polyurethane pressure-sensitive adhesive, comprising the following raw materials in parts by weight: 75 parts of neoprene, 65 parts of methyl methacrylate, 65 parts of hydroxyl polysiloxane, 35 parts of xylene resin, 35 parts of polyisocyanate, 25 parts of carbon fiber Parts, vinyl resin 25 parts, azo compound foaming agent 12 parts, rosin resin 12 parts, triethylamine 11 parts, methyl pentynol 6 parts, polybutadiene 6 parts, dibutyltin dilaurate 1.25 parts, 0.6 parts of N-methylolacrylamide;

[0026] Its preparation method comprises the following steps:

[0027] S1, weigh 75 parts of chloroprene, 65 parts of methyl methacrylate, 65 parts of hydroxypolysiloxane, 35 parts of xylene resin, and 35 parts of polyisocyanate according to the proportioning ratio, add them to the reactor, and raise the temperature of the reactor to Up to 65°C and fully stirred for 1.25h to obtain component A;

[0028] S2, weigh 25 parts of carbon fiber, 25 parts of vinyl res...

Embodiment 3

[0032] A high-performance polyurethane pressure-sensitive adhesive, comprising the following raw materials in parts by weight: 80 parts of neoprene, 70 parts of methyl methacrylate, 70 parts of hydroxyl polysiloxane, 40 parts of xylene resin, 40 parts of polyisocyanate, and 30 parts of carbon fiber Parts, vinyl resin 30 parts, azo compound foaming agent 14 parts, rosin resin 14 parts, triethylamine 13.5 parts, methyl pentynol 7.5 parts, polybutadiene 7.5 parts, dibutyltin dilaurate 1.5 parts, 0.75 parts of N-methylolacrylamide;

[0033] Its preparation method comprises the following steps:

[0034] S1, weigh 80 parts of chloroprene, 70 parts of methyl methacrylate, 70 parts of hydroxy polysiloxane, 40 parts of xylene resin, and 40 parts of polyisocyanate according to the proportioning ratio, add to the reactor, and raise the temperature of the reactor to Up to 70°C and fully stirred for 1.5h to obtain component A;

[0035] S2, weigh 30 parts of carbon fiber, 30 parts of viny...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-performance polyurethane pressure-sensitive adhesive. The polyurethane pressure-sensitive adhesive is prepared from the following raw materials in parts by weight: 70-90 parts of neoprene, 60-80 parts of methyl methacrylate, 60-80 parts of hydroxy terminated polydimethylsiloxane, 30-50 parts of xylene resin, 30-50 parts of polyisocyanate, 20-40 parts of carbon fibers, 20-40 parts of olefine resin, 10-18 parts of azo-compound foaming agent, 10-18 parts of rosin resin, 5-10 parts of triethylamine, 5-10 parts of methylpentynol, 5-10 parts of polybutadiene, 4-8 parts of triethylamine, 1-2 parts of dibutyltin dilaurate and 0.5-1 part of N-hydroxymethyl acrylamide. The preparation method comprises the following steps: S1, weighing 70-90 parts of neoprene, 60-80 parts of methyl methacrylate, 60-80 parts of hydroxy terminated polydimethylsiloxane, 30-50 parts of xylene resin and 30-50 parts of polyisocyanate according to the weight proportion, adding into a reaction kettle, heating the reaction kettle to 60-80 DEG C, and sufficiently stirring. The high-performance polyurethane pressure-sensitive adhesive is simple in preparation, has good performance and environmental friendliness, and is suitable for large-scale production.

Description

technical field [0001] The invention relates to the technical field of polyurethane pressure-sensitive adhesives, in particular to a high-performance polyurethane pressure-sensitive adhesive. Background technique [0002] Pressure-sensitive adhesives and their products are widely used in the fields of office, packaging, electrical engineering, electrical appliances, etching, paint and home decoration, and are closely related to people's lives. Pressure-sensitive adhesives are used in consumer goods and are used in large quantities in various industries. Ordinary pressure-sensitive tape and label technology is very mature, and its output exceeds demand, but the pressure-sensitive adhesive used in the automotive, electronic industry and other fields requires good cohesion and adhesion. The adhesive layer will not be damaged when the force is cut, and the adhesive force ensures that the pressure-sensitive adhesive has a high peel strength. The balance between the cohesive forc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J151/04C09J175/04C09J161/18C09J11/08C08F279/02C08F220/14C08G18/61
CPCC08F279/02C08G18/61C08L2205/035C09J11/08C09J151/04C09J2301/302C08L75/04C08L61/18C08L93/04C08K7/06C08F220/14
Inventor 黄佑想
Owner 新图美(台山)标签材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com