A kind of anionic liquid crystal type asphalt warm mix agent and preparation method thereof

A technology of warm mix agent and anion, which is applied in building insulation materials, building components, climate change adaptation, etc. It can solve the problems of reducing the performance of asphalt mixture, water damage of asphalt mixture, and generating a large amount of water vapor, so as to reduce energy consumption , Prevent rut damage, reduce the effect of smoke and harmful substance emissions

Active Publication Date: 2018-04-10
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is inevitable that some water will remain between the asphalt and aggregate interface during the production process, making the asphalt mixture potentially water-damaged
Moreover, if the amount of water added is too large, a large amount of water vapor will be generated or bumping will occur. If the amount of water is too small, the foaming effect will be poor.
[0007] At present, there are many warm mix asphalt additive products, such as CN101899218A, CN101831187A, CN102795801A, etc. Although these warm mix asphalt additive products can basically achieve the cooling effect and can successfully produce warm mix asphalt mixture, it is inevitable that there will be production Defects such as complicated process, high energy consumption, and reduced performance of asphalt mixture

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anionic liquid crystal type asphalt warm mix agent and preparation method thereof
  • A kind of anionic liquid crystal type asphalt warm mix agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Diisooctyl sodium sulfosuccinate: 32 parts

[0031] N-decyl alcohol: 2.5 parts

[0032] Water: 64.5 parts.

[0033] Add diisooctyl sodium sulfosuccinate and deionized water into the container according to the ratio, and stir at 30°C for 1 hour; add n-decyl alcohol, stir at a constant temperature of 30°C for 1 hour, and stand at room temperature for 3 hours to obtain anionic liquid crystal Asphalt warm mix.

Embodiment 2

[0035] Disodium lauryl succinate sulfonate: 30 parts

[0036] Lauryl alcohol: 3.6 parts

[0037] Water: 66.4 parts.

[0038] Add disodium lauryl alcohol succinate sulfonate and deionized water into the container according to the ratio, and stir at 35°C for 1 hour; add lauryl alcohol, stir at a constant temperature of 35°C for 1.5 hours, and stand at room temperature for 4 hours to obtain anionic liquid crystal pitch warm mix.

Embodiment 3

[0040] Disodium laureth succinate sulfonate: 25 parts

[0041] n-octanol: 2.5 parts

[0042] Water: 56.5 parts.

[0043] Add disodium lauryl polyoxyethylene ether succinate sulfosuccinate and deionized water into the container according to the ratio, and stir at 40°C for 1 hour; add n-octanol, stir at a constant temperature of 40°C for 1.5 hours, and stand at room temperature for 4 hours. An anionic liquid crystal asphalt warm mix agent is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anionic liquid-crystal-form asphalt warm-mixing agent and a preparation method therefor. The asphalt warm-mixing agent contains the raw materials in parts by weight: 5.5-40.6 parts of sulfosuccinate, 0.1-20 parts of fatty alcohol and 39.4-94.4 parts of water. The preparation method comprises the following steps: (1) uniformly mixing the water and the sulfosuccinate in a vessel according to a proportioning ratio; and (2) adding the fatty alcohol into a material obtained in the step (1), carrying out uniform mixing, and carrying out standing for a period of time, thereby obtaining the anionic liquid-crystal-form asphalt warm-mixing agent. The asphalt warm-mixing agent disclosed by the invention can be used for effectively lowering the high-temperature viscosity of asphalt and has the advantages that the performance is stable, the raw materials are easily acquired, the preparation method is simple and convenient, the range of application is wide, and the like.

Description

technical field [0001] The invention relates to an asphalt warm mix agent and a preparation method thereof, in particular to an anionic liquid crystal type asphalt warm mix agent and a preparation method thereof. Background technique [0002] Since asphalt was used in roads, the mature asphalt mixture is mainly hot mix asphalt mixture. However, hot mix asphalt mixture has defects such as high mixing temperature and paving temperature, high emission of harmful gases, and easy aging of asphalt mixture. , resulting in many ecological and environmental problems. [0003] Warm mix asphalt mixture is a new material that is environmentally friendly and energy-saving. It has the same or even better road performance as the corresponding hot mix asphalt mixture, but it can be mixed and paved at a lower temperature, which greatly reduces the The energy consumption and soot emission in the production process have significantly improved the economic benefits and ecological value. [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08K5/42C08K5/05C04B26/26C04B24/16C04B24/02
CPCY02A30/30
Inventor 宣根海宁爱民徐青柏陈杰石君章李志军
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap