Antirust heat treatment technology for spare parts
A kind of parts and process technology, which is applied in the field of anti-rust heat treatment process of parts, can solve the problems of high energy consumption, poor uniformity of galvanized layer thickness, insufficient surface hardness and wear resistance, etc., achieve low processing cost and improve process efficiency Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0016] In the following, the present invention will be further described in conjunction with the embodiments, and the operation steps are as follows:
[0017] (1) Part pretreatment: inspect the parts to remove burrs, iron filings, grease and other dirt on the surface of the parts;
[0018] (2) Degreasing: Use water-based metal degreasing cleaning agent to degrease the parts until the parts are completely wetted;
[0019] (3) Pickling: Place the pipe in a pickling tank to soak and remove the oxide scale on the surface of the steel pipe. The concentration of the pickling solution is 20-22% HCl, and then corrosion inhibitors are added. The temperature is controlled at 21-22°C and the pickling time is controlled. In 20-30 minutes;
[0020] (4) Rinsing: Add 0.1%-0.2% citric acid to clean water, and rinse with water;
[0021] (5) Immersion flux: put the parts into the flux tank to soak the flux, the flux is a mixed aqueous solution of ammonium chloride and zinc chloride, the concentration of...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap