Preparation method of fireproof plate composite material
A composite material and fireproof board technology, which is applied in the field of fireproof building materials preparation, can solve the problems of poor compatibility, service life and fireproof performance decline, and achieve the effect of long service life and excellent fireproof performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0010] Embodiment 1: prepare the composite material of fireproof board according to the following steps
[0011] Step 1: in 100mL mass concentration be the concentrated sulfuric acid H of 85% 2 SO 4 , while stirring, slowly add 100g of titanium n-butoxide Ti(OC 4 h 9 ) 4 , 28.4g zirconium oxychloride octahydrate ZrOCl 2 ·8H 2 O, 6g magnesium chloride hexahydrate MgCl 2 ·6H 2 O, the stirring time was controlled for 2h to obtain solution A;
[0012] Step 2: In 50mL of deionized water, add 10g of surfactant sodium lignosulfonate and 5g of dispersant glucose, and stir for 2 hours to prepare solution B;
[0013] Step 3: Pour solution A into solution B, let stand and age for 24 hours, use saturated calcium hydroxide Ca(OH) 2 Adjust the pH value of the solution to neutral to obtain a composite solution C;
[0014] Step 4: In 1000mL of water, add 500g of calcium silicate, while stirring, add 75g of polypropylene fiber and 25g of starch, slowly pour into composite solution C,...
Embodiment 2
[0015] Embodiment 2: according to the following steps to prepare fireproof board composite material
[0016] Step 1: in 100mL mass concentration be the concentrated sulfuric acid H of 85% 2 SO 4 , while stirring, slowly add 100g of titanium n-butoxide Ti(OC 4 h 9 ) 4 , 56.8g zirconium oxychloride octahydrate ZrOCl 2 ·8H 2 O, 18g magnesium chloride hexahydrate MgCl 2 ·6H 2 O, the stirring time was controlled for 4h to obtain solution A;
[0017] Step 2: In 50mL of deionized water, add 20g of surfactant sodium lignosulfonate and 10g of dispersant glucose, and stir for 2 hours to prepare solution B;
[0018] Step 3: Pour solution A into solution B, let stand and age for 48 hours, use saturated calcium hydroxide Ca(OH) 2 Adjust the pH value of the solution to neutral to obtain a composite solution C;
[0019] Step 4: In 1000mL of water, add 500g of calcium silicate, while stirring, add 125g of polypropylene fiber and 50g of starch, slowly pour into composite solution C, ...
Embodiment 3
[0020] Embodiment 3: according to the following steps to prepare fireproof board composite material
[0021] Step 1: in 100mL mass concentration be the concentrated sulfuric acid H of 85% 2 SO 4 , while stirring, slowly add 100g of titanium n-butoxide Ti(OC 4 h 9 ) 4 , 40g zirconium oxychloride octahydrate ZrOCl 2 ·8H 2 O, 12g magnesium chloride hexahydrate MgCl 2 ·6H 2 O, the stirring time was controlled for 3h to obtain solution A;
[0022] Step 2: In 50mL of deionized water, add 15g of surfactant sodium lignosulfonate and 8g of dispersant glucose, and stir for 2 hours to prepare solution B;
[0023] Step 3: Pour solution A into solution B, let stand and age for 36 hours, use saturated calcium hydroxide Ca(OH) 2 Adjust the pH value of the solution to neutral to obtain a composite solution C;
[0024] Step 4: In 1000mL of water, add 500g of calcium silicate, while stirring, add 100g of polypropylene fiber and 35g of starch, slowly pour into composite solution C, add...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap