Zirconia dental implant surface treatment method

A technology for surface treatment and dental implants, applied in the field of oral prosthetics, can solve problems such as affecting the success rate of implantation, difficult porous structure, no system formation, etc., to achieve the effect of improving interface effect, increasing roughness, and increasing roughness

Inactive Publication Date: 2016-08-17
CHENGDU BESMILE BIOTECH
View PDF6 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, zirconia ceramics are not easy to react with acid, so it is difficult to form an acid-etched porous structure on the implant surface
At the same time, after plasma spraying hydroxyapatite on the surface of the zirconia ceramic implant, due to the secondary sintering, faults will be formed on the implant surface, which affects the success rate of the implant.
At present, there is no systematic research on the surface treatment methods of zirconia ceramic implants.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1: a kind of zirconia dental implant surface treatment method, it comprises the following steps:

[0017] S1. Cleaning: The zirconia dental implant was ultrasonically cleaned with absolute ethanol and deionized water, and dried naturally; the cleaning time with absolute ethanol was 12 minutes, and the cleaning time with deionized water was 5 minutes;

[0018] S2. Sand blasting treatment: the cleaned dental implant is subjected to borax treatment with alumina particles with a diameter of 125 μm under an air pressure of 0.5 MPa; during the borax treatment, the nozzle is 0.5 cm away from the dental implant, and the nozzle is perpendicular to the tooth Spray the implant evenly for 20s;

[0019] S3. Acid etching: the dental implant treated with pulp and borax is completely immersed in an acidic solution for acid etching to obtain an acid-etched dental implant; wherein, the acidic solution is HF and HNO 3 The mixed solution, the concentration of HF is 1.5mol / L, HN...

Embodiment 2

[0022] Embodiment 2: a kind of zirconia dental implant surface treatment method, it comprises the following steps:

[0023] S1. Cleaning: The zirconia dental implant was ultrasonically cleaned with absolute ethanol and deionized water, and dried naturally; the cleaning time with absolute ethanol was 18 minutes, and the cleaning time with deionized water was 10 minutes;

[0024] S2. Sand blasting treatment: the cleaned dental implant is subjected to borax treatment with alumina particles with a diameter of 140 μm under an air pressure of 0.6 MPa; during the borax treatment, the distance between the nozzle and the dental implant is 1.5 cm, and the nozzle is perpendicular to the tooth. The implant is evenly sprayed for 40s;

[0025] S3. Acid etching: the dental implant treated with pulp and borax is completely immersed in an acidic solution for acid etching to obtain an acid-etched dental implant; wherein, the acidic solution is HF and HNO 3 The mixed solution, the concentration...

Embodiment 3

[0028] Embodiment 3: a kind of zirconia dental implant surface treatment method, it comprises the following steps:

[0029] S1. Cleaning: The zirconia dental implant was ultrasonically cleaned with absolute ethanol and deionized water, and dried naturally; the cleaning time with absolute ethanol was 14 minutes, and the cleaning time with deionized water was 7 minutes;

[0030] S2. Sand blasting treatment: the cleaned dental implant is subjected to borax treatment with alumina particles with a diameter of 130 μm under an air pressure of 0.54 MPa; during the borax treatment, the distance between the nozzle and the dental implant is 0.8 cm, and the nozzle is perpendicular to the tooth. The implant is evenly sprayed for 28s;

[0031] S3. Acid etching: the dental implant treated with pulp and borax is completely immersed in an acidic solution for acid etching to obtain an acid-etched dental implant; wherein, the acidic solution is HF and HNO 3 The mixed solution, the concentration...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
surface roughnessaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a zirconia dental implant surface treatment method which comprises the steps of cleaning, sand blasting treatment, acid etching, soaking and sintering. In the invention, the zirconia dental implant surface is dipped with a ball-milled zirconia suspension; the pore diameter of pores in the zirconia dental implant surface is controlled by use of different particle sizes of the ball-milled zirconia powder; meanwhile, due to the sand blasting and acid etching treatment before soaking, the surface roughness of false teeth is increased to certain degree; with later sintering, the surface roughness of false teeth is remarkably increased; and thus, the interfacial effect between the implant material and the host bone can be improved, the binding capacity between the implant and the bone is enhanced, and clinical success rate of dental implant is increased. The zirconia dental implant surface treatment method is simple in operation, convenient in treatment, low in cost and suitable for industrialized large-scale production.

Description

technical field [0001] The invention belongs to the technical field of oral restoration, and in particular relates to a method for treating the surface of a zirconia dental implant. Background technique [0002] With the continuous improvement of living standards and aesthetic requirements, implant denture restoration has become an important part of oral restoration. At present, titanium implants are mainly used clinically. In order to improve the ability of titanium implant-osseointegration and shorten the healing time, the surface of pure titanium implants is mostly treated. For example, the surface of the implant produced by the Swedish Nobel Company has been treated with TiUnite (titanium easy-resistant, porous titanium oxide structure), which can effectively promote the integration with the bone; the implant produced by the Swiss Straumann Company has been treated on its surface SLA (large-particle acid-etched sandblasting) treatment, and further upgraded SLActive (act...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/30A61L27/50A61L27/56C04B35/48C04B41/87
CPCA61L27/30A61L27/50A61L27/56C04B35/48C04B41/87A61L27/306A61L2430/12C04B41/009C04B41/5042
Inventor 王昌健
Owner CHENGDU BESMILE BIOTECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap