70-DEG C protective-layer soft polyvinyl chloride plastic

A soft polyvinyl chloride and polyvinyl chloride technology, which is applied in the field of soft polyvinyl chloride plastics at 70 degrees Celsius, can solve the problems of cross-linking of main materials, low strength and wear resistance, affecting the use of wires and cables, etc. Effects with pore structure, increased strength, increased capacity

Inactive Publication Date: 2016-08-17
ANHUI YANGTIAN PLASTIC IND TECH
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In wire and cable, the maximum allowable working temperature of the wire core is 70°C, and it is often made of soft materials such as polyvinyl chloride plastic. However, the strength and wear resistance of these materials are generally low, and the added reinforcing filler materials are not very good. Ground and main material cross-linking, which further affects the use of wire and cable, has become a bottleneck restricting the development of the wire and cable industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of soft polyvinyl chloride plastic with a 70-degree Celsius protective layer proposed by the present invention, its raw materials include by weight: 50 parts of polyvinyl chloride, 22 parts of polystyrene, 8 parts of nitrile rubber, 6 parts of acrylate rubber, toluene diisocyanate 3.6 parts, 2.2 parts of stearic acid, 17 parts of super-dispersed graphene reinforcing filler, 7 parts of light calcium carbonate, 8 parts of titanium dioxide, 1.1 parts of paraffin, 1.1 parts of sulfur, 1.4 parts of accelerator CZ, and 2 parts of accelerator TMTD. 3 parts, coumarone 1.3 parts, antioxidant TNP 1.2 parts, antioxidant DLTP 1.2 parts.

[0025] Wherein, the preparation process of hyperdisperse graphene reinforcing filler comprises:

[0026] S1, 3 parts of graphite, 4 parts of potassium nitrate, and 10 parts of potassium permanganate are dropped into 12 parts of mass fraction by weight in the sulfuric acid solution of 40wt%, and ultrasonic treatment obtains solution A, and t...

Embodiment 2

[0030]A kind of soft polyvinyl chloride plastic with a 70-degree Celsius protective layer proposed by the present invention, its raw materials include by weight: 45 parts of polyvinyl chloride, 25 parts of polystyrene, 15 parts of nitrile rubber, 9 parts of acrylate rubber, toluene diisocyanate 3.2 parts, 2.5 parts of stearic acid, 14 parts of super-dispersed graphene reinforcing filler, 10 parts of light calcium carbonate, 5 parts of titanium dioxide, 1.4 parts of paraffin, 0.8 parts of sulfur, 1.7 parts of accelerator CZ, 2 parts of accelerator TMTD 1.6 parts of coumarone, 0.8 parts of antioxidant TNP, and 1.5 parts of antioxidant DLTP.

[0031] Wherein, the preparation process of hyperdisperse graphene reinforcing filler comprises:

[0032] S1, 1 part of graphite, 6 parts of potassium nitrate, and 8 parts of potassium permanganate are dropped into 15 parts of mass fraction by weight in the sulfuric acid solution of 35wt%, and ultrasonic treatment obtains solution A, and the...

Embodiment 3

[0036] A kind of soft polyvinyl chloride plastic with a 70-degree Celsius protective layer proposed by the present invention, its raw materials include by weight: 48 parts of polyvinyl chloride, 23 parts of polystyrene, 17 parts of nitrile rubber, 7 parts of acrylate rubber, toluene diisocyanate 3.5 parts, 2.3 parts of stearic acid, 16 parts of super-dispersed graphene reinforcing filler, 8 parts of light calcium carbonate, 7 parts of titanium dioxide, 1.2 parts of paraffin, 1 part of sulfur, 1.5 parts of accelerator CZ, 2.2 parts of accelerator TMTD 1.4 parts of coumarone, 1.7 parts of antioxidant TNP, and 1.3 parts of antioxidant DLTP.

[0037] Wherein, the preparation process of hyperdisperse graphene reinforcing filler comprises:

[0038] S1, 2.5 parts of graphite, 4.5 parts of potassium nitrate, and 9.6 parts of potassium permanganate are dropped into 13 parts of mass fraction by weight in the sulfuric acid solution of 39wt%, and ultrasonic treatment obtains solution A. T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses 70-DEG C protective-layer soft polyvinyl chloride plastic. The plastic is prepared from, by weight, 45-50 parts of polyvinyl chloride, 22-25 parts of polystyrene, 15-18 parts of butadiene-acrylonitrile rubber, 6-9 parts of acrylic rubber, 3.2-3.6 parts of toluene diisocynate, 2.2-2.5 parts of stearic acid, 14-17 parts of super-dispersive graphene-reinforced filler, 1.4-1.7 parts of accelerant CZ, 2-2.3 parts of accelerant TMTD, 1.3-1.6 parts of coumarone, 0.8-1.2 parts of antioxidant TNP and 1.2-1.5 parts of antioxidant DLTP.

Description

technical field [0001] The invention relates to the technical field of polyvinyl chloride plastics, in particular to a soft polyvinyl chloride plastic with a 70-degree Celsius protective layer. Background technique [0002] Wires and cables have become an important supporting industry for my country's economic construction because they can be applied to various fields of the national economy. Wires and cables are indispensable materials for transmitting electric energy, transmitting information, and manufacturing various automobiles, electrical appliances, and industrial equipment, especially in electric power. Industry and communication industry occupy a very high output value; in the world, my country is also the leading producer of wire and cable. In wire and cable, the maximum allowable working temperature of the wire core is 70°C, and it is often made of soft materials such as polyvinyl chloride plastic. However, the strength and wear resistance of these materials are ge...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L25/06C08L9/02C08L33/04C08L91/06C08L45/02C08K13/06C08K9/02C08K3/04C08K3/34C08K5/29C08K5/09C08K3/26C08K3/22C08K3/06H01B3/44
CPCC08L27/06C08L2201/08C08L2203/202C08L2205/035C08L2312/00H01B3/443C08L25/06C08L9/02C08L33/04C08L91/06C08L45/02C08K13/06C08K9/02C08K3/04C08K3/346C08K5/29C08K5/09C08K2003/265C08K2003/2241C08K3/06
Inventor 巫后凡叶明周章琼焕
Owner ANHUI YANGTIAN PLASTIC IND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com