Polyurethane thermal-insulation composite board

A thermal insulation composite board, polyurethane technology, applied in the field of board, can solve problems such as hazards, and achieve the effects of improving crosslinking density, excellent strength, and improving flame retardant performance

Inactive Publication Date: 2016-08-17
ANHUI GUANGYAN NEW MATERIAL TECH
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the rigid polyurethane foam used for insulation boards has a porous structure, which makes it easier to ignite than ordinary plastics, and releases a large amount of toxic gases such as hydrogen cyanide, CO, and NO during the combustion process, causing great potential hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A polyurethane thermal insulation composite board proposed by the present invention comprises a polyurethane thermal insulation layer and a backing layer arranged on the inner and outer surfaces of the polyurethane thermal insulation layer, the polyurethane thermal insulation layer is made of high-performance polyurethane rigid foam material, and the high The raw materials of performance polyurethane rigid foam include by weight: 100 parts of polyester polyol, 65 parts of diphenylmethane diisocyanate, 30 parts of hexamethylene diisocyanate, 20 parts of polyacrylate, 10 parts of styrene-butadiene rubber, 3 parts of cyclohexylamine, 0.5 parts of triethylenediamine, 1 part of stannous octoate, 3 parts of foaming agent, 5 parts of hydroxyl silicone oil, 2 parts of flame retardant, 40 parts of expanded perlite, 10 parts of attapulgite, 10 parts of pentaerythritol part, 1 part of sorbitol;

[0020] Wherein, the raw materials of the flame retardant include by weight: 10 parts ...

Embodiment 2

[0022] A polyurethane thermal insulation composite board proposed by the present invention comprises a polyurethane thermal insulation layer and a backing layer arranged on the inner and outer surfaces of the polyurethane thermal insulation layer, the polyurethane thermal insulation layer is made of high-performance polyurethane rigid foam material, and the high The raw materials of performance polyurethane rigid foam include by weight: 100 parts of polyester polyol, 35 parts of diphenylmethane diisocyanate, 65 parts of hexamethylene diisocyanate, 4 parts of polyacrylate, 30 parts of styrene-butadiene rubber, 1 part of cyclohexylamine, 3 parts of triethylenediamine, 0.1 part of stannous octoate, 10 parts of foaming agent, 1 part of hydroxyl silicone oil, 10 parts of flame retardant, 20 parts of expanded perlite, 25 parts of attapulgite, 2 parts of pentaerythritol part, 5 parts of sorbitol;

[0023] Wherein, the raw materials of the flame retardant include by weight: 2 parts of...

Embodiment 3

[0025] A polyurethane thermal insulation composite board proposed by the present invention comprises a polyurethane thermal insulation layer and a backing layer arranged on the inner and outer surfaces of the polyurethane thermal insulation layer, the polyurethane thermal insulation layer is made of high-performance polyurethane rigid foam material, and the high The raw materials of performance polyurethane rigid foam include by weight: 100 parts of polyester polyol, 52 parts of diphenylmethane diisocyanate, 40 parts of hexamethylene diisocyanate, 16 parts of polyacrylate, 19 parts of styrene-butadiene rubber, 2.1 parts of cyclohexylamine, 1.2 parts of triethylenediamine, 0.68 parts of stannous octoate, 6.2 parts of foaming agent, 3.4 parts of hydroxyl silicone oil, 6.3 parts of flame retardant, 36 parts of expanded perlite, 14 parts of attapulgite, 6.2 parts of pentaerythritol part, 2.3 parts of sorbitol;

[0026] Wherein, the thickness of the backing layer located on the inn...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Functional group degreeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyurethane thermal-insulation composite board which comprises a polyurethane thermal-insulation layer and back lining layers arranged on the inner and lower surfaces of the polyurethane thermal-insulation layer, wherein the polyurethane thermal-insulation layer is prepared from a high-performance polyurethane rigid foam material. The high-performance polyurethane rigid foam material is prepared from polyester polyol, diphenylmethane diisocyanate, hexamethylene diisocyanate, polyacrylate, styrene-butadiene rubber, cyclohexylamine, triethylenediamine, stannous octoate, a foaming agent, hydroxy silicone oil, a flame retardant, expanded perlite, attapulgite, pentaerythritol and sorbitol. The flame retardant is prepared from red phosphorus, nano magnesium hydroxide, ammonium polyphosphate, aluminum diethyl hypophosphite, piperazidine pyrophosphate and hexametapol. The polyurethane thermal-insulation composite board disclosed by the invention has the advantages of high strength, favorable impact resistance, excellent flame retardancy and long service life.

Description

technical field [0001] The invention relates to the technical field of boards, in particular to a polyurethane thermal insulation composite board. Background technique [0002] Polyurethane insulation composite board is composed of two layers of waterproof color-coated steel plates or other metal panels, and the middle is injected with flame-retardant polyurethane rigid foam. It is the best heat insulation material recognized in the world today. It can be used for large industrial plants, The roofs and walls of various buildings such as warehouses, exhibition halls, gymnasiums, cold storages, and purification workshops are integrated with heat preservation, heat insulation, load-bearing, and waterproof, and have the characteristics of rich colors and beautiful shapes. dominate the material market. However, the rigid polyurethane foam used for insulation boards has a porous structure, which makes it easier to ignite than ordinary plastics, and releases a large amount of toxi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/06C08L33/04C08L9/06C08L83/06C08K13/04C08K7/26C08K3/34C08K3/02C08K3/22C08K3/32C08K5/5313C08K5/3462C08K5/5399C08G18/76C08G18/73C08G18/66C08G18/42C08G18/32C08J9/14C08J9/08B32B27/06B32B27/18C08G101/00
CPCB32B27/06B32B27/18B32B2250/03B32B2307/304B32B2307/3065B32B2419/06B32B2607/00C08G18/6644C08G18/724C08G18/73C08G18/7671C08J9/08C08J9/141C08J9/142C08J2203/02C08J2203/12C08J2203/14C08J2203/204C08J2375/06C08J2433/04C08K2201/011C08L75/06C08L2201/02C08L2201/08C08L2203/14C08L2205/035C08G2110/0025C08L33/04C08L9/06C08L83/06C08K13/04C08K7/26C08K3/346C08K2003/026C08K2003/2224C08K2003/323C08K5/5313C08K5/3462C08K5/5399
Inventor 夏正忠
Owner ANHUI GUANGYAN NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap