A high-temperature-resistant coating and high-temperature-resistant filler technology, which is applied in the direction of fireproof coatings, polyester coatings, polyurea/polyurethane coatings, etc., can solve the problems of poor drying at room temperature, poor adhesion and corrosion resistance of coatings, and achieve high paint film Adhesion, superior high temperature resistance, and the effect of solving solid waste problems

Active Publication Date: 2016-08-17
NANJING INST OF PROD QUALITY INSPECTION
View PDF6 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although silicone high-temperature resistant coatings have excellent high-temperature resistance; however, due to the different pigments and fillers and formulas selected, the coatings have problems such as poor drying at room temperature (generally requiring drying), poor mechanical strength, adhesion and corrosion resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Improved high-temperature resistant paint
  • Improved high-temperature resistant paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Example 1 300°C high temperature resistant coating

[0054] Recipe one:

[0055] Select the following components in mass percentage: 8810 modified silicone resin (acrylic resin modified silicone resin) 30% (Shanghai Longxu Chemical Co., Ltd.), alkyd resin 28% (Jiangsu Champion Paint Technology Group), xylene 7.8% (Sinopec Yangzi Petrochemical Co., Ltd.), AF300 organic soil 1% (Zhejiang Shunfu Clay Chemical Co., Ltd.), carbon black 2% (Tianjin Baochi Chemical Co., Ltd.), ceramic black 1% (Shanghai Furui Chemical Co., Ltd. company), sericite powder 15% (Lingshou County Yaotai Mica Powder Factory), 1250R brand talc powder 15% (Changxing Dajing New Material Technology Co., Ltd.), silicone defoamer 0.2% (Hangzhou Zhuoli Chemical Co., Ltd. ).

[0056] Formula two (replacing the sericite powder and talcum powder of formula one with slag fine powder of the present invention):

[0057] Select the following components in mass percentage: 8810 modified silicone resin (acrylic r...

Embodiment 2

[0065] Example 2 400°C high temperature resistant coating

[0066] Recipe three:

[0067] Select the following components in mass percentage: 8810 modified silicone resin (acrylic resin modified silicone resin) 40% (Shanghai Longxu Chemical Co., Ltd.), polyurethane resin 18% (Amway Material Technology Co., Ltd.), xylene 7.8% (Sinopec Yangzi Petrochemical Co., Ltd.), AF300 organic soil 1% (Zhejiang Shunfu Clay Chemical Co., Ltd.), carbon black 2% (Tianjin Baochi Chemical Co., Ltd.), ceramic black 1% (Shanghai Furui Chemical Co., Ltd. company), sericite powder 15% (Lingshou County Yaotai Mica Powder Factory), 1250R brand talc powder 15% (Changxing Dajing New Material Technology Co., Ltd.), silicone defoamer 0.2% (Hangzhou Zhuoli Chemical Co., Ltd. ).

[0068] Formula four (replacing the sericite powder and talcum powder of formula three with the slag powder of the present invention): select the following components in mass percentage): 8810 modified silicone resin (acrylic res...

Embodiment 3

[0077] Performance tests were performed on the high-temperature-resistant coatings of formula 1 and formula 2 in Example 1, and the high-temperature-resistant coatings of formula 3 and formula 4 in Example 2, and the results are shown in Table 1 and Table 2. The result shows that the high temperature resistant coating of the present invention has superior high temperature resistance, salt resistance, alkali resistance, salt spray resistance performance compared with the high temperature resistant coating that uses traditional high temperature resistant filler such as mica powder, talcum powder, and has higher Paint film adhesion, paint film hardness.

[0078] Table 1

[0079]

[0080] Table 2

[0081]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses improved high-temperature resistant paint. The improved high-temperature resistant paint comprises solvent, organic silicon resin and / or modified organic silicon resin and high-temperature filler which is superfine slag powder. The high-temperature resistant paint is excellent in high temperature resistance, salt resistance, alkali resistance and salt spray resistance and has larger paint film adhesive force, higher paint film hardness and higher market application value.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to an improved high-temperature-resistant coating. Background technique [0002] High temperature-resistant coatings generally refer to coatings that do not change color or fall off when the temperature is above 200°C, and can still maintain appropriate physical and mechanical properties. High temperature resistant coatings are generally composed of high temperature resistant resins, pigments and fillers, solvents and additives. Since the industrial production of organosilicon, the high-temperature-resistant coatings formulated with its products have been widely used in high-temperature motors, high-temperature reactors, high-temperature pipelines, and electrical insulation. Although silicone high-temperature-resistant coatings have excellent high-temperature resistance; however, due to the different pigments and fillers and formulas selected, the coatings have problems such as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D183/04C09D175/04C09D5/18C09D7/12
CPCC08L2201/08C09D5/18C09D7/61C09D167/08C09D183/04C08L83/04C08K13/02C08K2003/2206C08K2003/222C08K2003/2227C08K3/36C08K2003/2262C08K2003/2241C08L75/04
Inventor 黄祝华毛敏明李安平梁峙顾建华杨杰姜振军黄臻黄舒雯乔玲
Owner NANJING INST OF PROD QUALITY INSPECTION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap