A kind of sandwich structure chitosan/nonionic surfactant cross-linked gel film and preparation method thereof

A non-ionic surface and cross-linked gel technology, which is applied in the field of sandwich structure chitosan/non-ionic surfactant cross-linked gel film and its preparation, achieves excellent stability, good mechanical properties, improved mechanical properties and stable sexual effect

Active Publication Date: 2019-10-11
JIANGNAN UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the deficiencies of the existing gel membrane in the field of gas separation, to provide a sandwich structure chitosan / nonionic surfactant cross-linked gel membrane and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) Preparation of gel film:

[0022] Mix 10 parts of chitosan, 75 parts of 2% acetic acid aqueous solution and 15 parts of Tween 20 at 40°C, spread them on a polytetrafluoroethylene board, and dry the solvent to obtain a gel film.

[0023] (2) The surface layer of the film is re-crosslinked:

[0024] Dissolve 2 parts of isophorone diisocyanate and 2 drops of dibutyltin dilaurate in 98 parts of n-hexane to form a cross-linking agent solution, and immerse the above-mentioned gel film in the cross-linking agent solution for 0.1 hour to form a gel film surface cross-linking;

[0025] (3) Post-processing:

[0026] The cross-linked gel film was dried in the air for 24 hours, then transferred to a vacuum drying oven, and treated at 30° C. for 24 hours to obtain a sandwich-structured chitosan / nonionic surfactant cross-linked gel film.

[0027] The aforementioned sandwich-structured chitosan / nonionic surfactant cross-linked gel film was used for CO 2 / N 2 Separation, under...

Embodiment 2

[0029] (1) Preparation of gel film:

[0030] 20 parts of chitosan, 70 parts of 3% acetic acid aqueous solution and 10 parts of Triton X-114 were evenly mixed at 30°C and spread on a polytetrafluoroethylene board, and the solvent was dried to obtain a gel film.

[0031] (2) The surface layer of the film is re-crosslinked:

[0032] Dissolve 1 part of toluene diisocyanate and 1 drop of dibutyltin dilaurate in 99 parts of n-hexane to form a cross-linking agent solution, and immerse the above-mentioned gel film in the cross-linking agent solution for 6 hours to carry out cross-linking of the surface layer of the gel film ;

[0033] (3) Post-processing:

[0034] The cross-linked gel film was dried in the air for 24 hours, then transferred to a vacuum drying oven, and treated at 30° C. for 24 hours to obtain a sandwich-structured chitosan / nonionic surfactant cross-linked gel film.

[0035] The aforementioned sandwich-structured chitosan / nonionic surfactant cross-linked gel film w...

Embodiment 3

[0037] (1) Preparation of gel film:

[0038] Mix 10 parts of chitosan, 70 parts of 2% acetic acid aqueous solution and 20 parts of Span 80 at 50°C, spread them on a polytetrafluoroethylene board, and dry the solvent to obtain a gel film.

[0039] (2) The surface layer of the film is re-crosslinked:

[0040] Dissolve 3 parts of diphenylmethane diisocyanate and 2 drops of dibutyltin dilaurate in 97 parts of n-hexane to form a cross-linking agent solution, and immerse the above-mentioned gel film in the cross-linking agent solution for 0.5 hour to form a gel film surface cross-linking;

[0041] (3) Post-processing:

[0042] The cross-linked gel film was dried in the air for 24 hours, then transferred to a vacuum drying oven, and treated at 30° C. for 24 hours to obtain a sandwich-structured chitosan / nonionic surfactant cross-linked gel film.

[0043] The aforementioned sandwich-structured chitosan / nonionic surfactant cross-linked gel film was used for CO 2 / N 2 Separation, u...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of film separation and relates to a chitosan / nonionic surfactant cross-linked gel film with a sandwich structure and a preparation method thereof. The film is characterized in that the film has the sandwich structure, the upper and lower surface layers are arranged as cross-linked surfaces and a gel layer is arranged in the middle. The preparation method comprises the following steps: (1) uniformly mixing chitosan, nonionic surfactant and solvent under a certain temperature, paving on a polytetrafluoroethylene plate, and drying to remove the solvent to obtain a gel film; (2) soaking the gel film in the solution containing the cross-linking agent and catalyst for 0.1-6 hours and performing the surface cross-linking reaction on the gel film; (3) drying the cross-linked gel film in air for 24 hours, and then transferring into a vacuum drying oven, and processing for 24 hours at 30 DEG C, thereby acquiring the chitosan / nonionic surfactant cross-linked gel film with the sandwich structure. According to the preparation method provided by the invention, the upper and lower surfaces of the film are cross-linked, so that the chitosan / nonionic surfactant cross-linked gel film with the sandwich structure is formed, the nonionic surfactant is difficult to run off, the lasting stability of the physical structure and property of the film is ensured and the preparation method is fit for the separating of the carbon dioxide in the mixed gas and the recycling of the organic steam.

Description

technical field [0001] The invention belongs to the technical field of membrane separation, and in particular relates to a sandwich structure chitosan / nonionic surfactant cross-linked gel membrane and a preparation method thereof. Background technique [0002] current atmospheric CO 2 Concentrations continue to rise, and the greenhouse effect is intensifying, posing a serious threat to the ecological environment on which human beings depend. Conventional CO 2 Separation technologies, such as amine aqueous solution absorption method, cryogenic separation method and pressure swing adsorption method, are accompanied by high energy consumption, high operating costs or the possibility of secondary pollution in the process of realizing gas separation. Therefore, membrane separation technology, which has many advantages such as economy, high efficiency, and environmental protection, has received more and more attention in the field of gas separation. [0003] Gel membrane is a n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D71/74B01D67/00B01D53/22
CPCY02C20/40
Inventor 张春芳张鹏白云翔顾瑾孙余凭
Owner JIANGNAN UNIV