Long-chain branched high-density polyethylene material resistant to environmental stress cracking and preparation method thereof

A high-density polyethylene and environmental stress-resistant technology, applied in the field of polymer materials, can solve the problems of limiting the application range of high-density polyethylene, easy grain slippage, environmental stress cracking, etc., and achieve excellent environmental stress cracking resistance , Improve environmental stress cracking resistance and prolong life

Active Publication Date: 2018-11-27
KANGMINGYUAN GUIZHOU SCI & TECH DEV CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the simple linear molecular chain structure of high-density polyethylene, it is easy to produce environmental stress cracking under stress. This shortcoming greatly limits the application range of high-density polyethylene, because the highly crystalline unmodified The molecular chain of HDPE is a linear structure, and there are few connecting molecules between crystal grains and wafers. Under stress, it is easy to cause slippage between crystal grains.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Long-chain branched high-density polyethylene material resistant to environmental stress cracking and preparation method thereof
  • Long-chain branched high-density polyethylene material resistant to environmental stress cracking and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1 of the present invention: long-chain branched high-density polyethylene material resistant to environmental stress cracking, calculated in parts by mass, including 100 parts of high-density polyethylene (brand name: HD5218EA, MFR: 20), 0.05 parts of dimethyl Zinc dithiocarbamate, 1 part of neopentyl glycol diacrylate, 0.03 part of dicumyl peroxide and 0.05 part of antioxidant B215.

[0018] The preparation method of the long-chain branched high-density polyethylene material resistant to environmental stress cracking comprises high-density polyethylene, neopentyl glycol diacrylate, zinc dimethyl dithiocarbamate, over After dicumyl oxide and antioxidant B215 are fully mixed and uniform, they are added to a Φ65 twin-screw extruder for melt blending. The main engine speed is 400r / min, the reaction time is 2min, the temperature is 170°C, and the product is granulated. Some samples were taken for performance testing, and the results are shown in Table 1.

Embodiment 2

[0019] Example 2 of the present invention: long-chain branched high-density polyethylene material resistant to environmental stress cracking, calculated in parts by mass, including 100 parts of high-density polyethylene (brand name HD5218EA, MFR: 20), 0.15 parts of diisobutylene Dithiocarbamate zinc salt, 1 part of neopentyl glycol diacrylate, 0.05 part of dicumyl peroxide and 0.1 part of antioxidant B215.

[0020] The preparation method of the long-chain branched high-density polyethylene material resistant to environmental stress cracking comprises high-density polyethylene, neopentyl glycol diacrylate, zinc diisobutyldithiocarbamate, After dicumyl peroxide and antioxidant B215 are fully mixed, they are added to a Φ60 single-screw extruder for melt blending. The main engine speed is 60r / min, the reaction time is 4min, the temperature is 180°C, and the product is granulated. Some samples were taken for performance testing, and the results are shown in Table 1.

Embodiment 3

[0021] Example 3 of the present invention: long-chain branched high-density polyethylene material resistant to environmental stress cracking, calculated in parts by mass, including 100 parts of high-density polyethylene (grade 5000S, MFR: 1.2), 0.1 part of dimethyl Zinc dithiocarbamate, 1 part of neopentyl glycol diacrylate, 0.1 part of dicumyl peroxide and 0.2 part of antioxidant 1010.

[0022] The preparation method of the long-chain branched high-density polyethylene material resistant to environmental stress cracking comprises high-density polyethylene, neopentyl glycol diacrylate, zinc dimethyl dithiocarbamate, over After dicumyl oxide and antioxidant 1010 are fully mixed and uniform, they are added to a Φ65 single-screw extruder for melt blending. The main engine speed is 80r / min, the reaction time is 3min, the temperature is 170°C, and the product is granulated. . Some samples were taken for performance testing, and the results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a long-chain branched high-density polyethylene material resisting environmental stress cracking and a preparation method thereof. According to the preparation method, long-chain branched modification is conducted on high-density polyethylene by selecting a melting reaction processing method to improve the environmental stress cracking resisting property of the material, branching generation is promoted by adding two-functionality-degree graft monomers, acrylic ester double bonds are adopted to stabilize the macromolecular free radicals and improve the branching efficiency, and meanwhile an efficient free radical regulating agent is added to regulate and control the activity of the macromolecular free radicals to inhibit crosslinking side reaction; the prepared long-chain branched high-density polyethylene has the low gel fraction, and long-branch-chain high-density polyethylene of which the branch chain length meets the stress cracking resisting requirement is obtained. The long-chain branched high-density polyethylene prepared through the preparation method has the excellent environmental stress cracking resisting property and the good comprehensive mechanical property.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a long-chain branched high-density polyethylene material resistant to environmental stress cracking and a preparation method thereof. Background technique [0002] High-density polyethylene is a non-polar linear thermoplastic resin with high crystallinity. It has good physical and mechanical properties, high service temperature and good weather resistance. It is widely used in various plastic processing products. Capacity and demand continue to climb every year. However, due to the simple linear molecular chain structure of high-density polyethylene, it is easy to produce environmental stress cracking under stress. This shortcoming greatly limits the application range of high-density polyethylene, because the highly crystalline unmodified The molecular chain of HDPE is a linear structure, and there are few connecting molecules between crystal grains and wafers. Under stress, it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F255/02C08F222/14C08F2/40C08F4/34
CPCC08F2/40C08F4/34C08F255/02C08F222/14
Inventor 罗筑魏江涛
Owner KANGMINGYUAN GUIZHOU SCI & TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com