Polypropylene microcellular foam composite material and preparation method thereof

A composite material, polypropylene technology, applied in the field of polypropylene micro-foamed composite material and its preparation, can solve problems such as poor mechanical properties and complex production processes, achieve superior mechanical properties, enhance nucleation efficiency, and increase roughness Effect

Inactive Publication Date: 2016-09-07
GUANGZHOU JUZHU GENERAL TECH INST CO LTD
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The invention provides a polypropylene micro-foaming composite material and a preparation method thereo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene microcellular foam composite material and preparation method thereof
  • Polypropylene microcellular foam composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0029] Example 1

[0030] A polypropylene micro-foamed composite material, which is made of the following parts by weight of raw materials: 90 parts by weight of polypropylene, 6 parts of carbon fiber, and 4 parts of foaming masterbatch. The foaming masterbatch is based on parts by weight and is made of the following raw materials Composition: 60 parts of polyethylene, 25 parts of foaming agent, 3 parts of nucleating agent, 0.5 parts of zinc oxide, 0.5 parts of titanate coupling agent NDZ-201, 4 parts of PE wax and 0.7 parts of zinc stearate. The foaming agent is calculated in parts by weight, including 65 parts of foaming agent TA-220; 35 parts of PP foaming multifunctional masterbatch and 5 parts of TA1000 foaming agent. The nucleating agent, in parts by weight, includes 20 parts of talc, 15 parts of calcium citrate and 65 parts of nano calcium carbonate.

[0031] The preparation method includes the following steps:

[0032] (1) Carbon fiber surface treatment: The carbon fiber is...

Example Embodiment

[0037] Example 2

[0038] A polypropylene micro-foamed composite material, made of the following parts by weight of raw materials: 85 parts by weight of polypropylene, 5 parts of carbon fiber, and 5 parts of a foaming masterbatch. The foaming masterbatch is based on parts by weight and is made of the following raw materials Composition: 65 parts of polyethylene, 30 parts of foaming agent, 4 parts of nucleating agent, 1.5 parts of zinc oxide, 0.8 parts of titanate coupling agent NDZ-201, 3 parts of PE wax and 0.5 parts of zinc stearate. The foaming agent is calculated in parts by weight, including 60 parts of foaming agent TA-220; 40 parts of PP foaming multifunctional masterbatch and 3 parts of TA1000 foaming agent. The nucleating agent, in parts by weight, includes 25 parts of talc, 20 parts of calcium citrate and 60 parts of nano calcium carbonate.

[0039] The preparation method includes the following steps:

[0040] (1) Carbon fiber surface treatment: The carbon fiber is surfac...

Example Embodiment

[0045] Example 3

[0046] A polypropylene micro-foamed composite material, which is made of the following parts by weight of raw materials: 95 parts by weight of polypropylene, 8 parts of carbon fiber, and 4 parts of foaming masterbatch. : 70 parts of polyethylene, 20 parts of foaming agent, 5 parts of nucleating agent, 1 part of zinc oxide, 1 part of titanate coupling agent NDZ-201, 5 parts of PE wax and 1 part of zinc stearate. The foaming agent is calculated in parts by weight, including 70 parts of foaming agent TA-220, 30 parts of PP foaming multifunctional masterbatch and 4 parts of TA1000 foaming agent. The nucleating agent, in parts by weight, includes 30 parts of talc, 10 parts of calcium citrate and 70 parts of nano calcium carbonate.

[0047] The preparation method includes the following steps:

[0048] (1) Carbon fiber surface treatment: The carbon fiber is surface-treated carbon fiber. The surface treatment steps are as follows: First, remove the oil on the surface, ta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a polypropylene microcellular foam composite material and a preparation method thereof. The polypropylene microcellular foam composite material is prepared from, by weight, 85-95 parts of polypropylene, 5-10 parts of carbon fibers and 3-5 parts of foaming masterbatch, wherein the foam masterbatch is prepared from, by weight, 60-70 parts of polyethylene, 20-30 parts of a foaming agent, 3-5parts of a nucleating agent, 0.5-1.5 parts of zinc oxide, 0.5-1 part of a titanate coupling agent NDZ-201, 3-5 parts of PE wax and 0.5-1 part of zinc stearate. According to the polypropylene microcellular foam composite material prepared through the method, the mechanical property is superior, the tensile strength reaches 35.9 MPa, the impact strength reaches 56.1 kJ/m<2>, and the bending modulus reaches 1,620 MPa.

Description

technical field [0001] The invention relates to a polypropylene composite material, in particular to a polypropylene microfoam composite material and a preparation method thereof. Background technique [0002] In the first ten years of the 21st century, the research and development of new energy and new materials in China and other economies around the world have reached a new and higher level. The development of the material field provides a new starting point, a new opportunity, and the requirements for polymers tend to be multi-functional. In the 1980s, the new technology of micro-foaming polymers proposed by the Massachusetts Institute of Technology has significantly improved the performance of materials. At the same time, endowing polymers with excellent new properties has become a new field and new direction for many researchers. Generally speaking, the diameter of microcellular foamed materials is relatively small, about 1 μm to 100 μm. The holes are evenly distribut...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/06C08K13/06C08K9/02C08K9/04C08K7/06C08K3/22C08K5/098C08K3/34C08K3/26C08J9/10C08J9/08
CPCC08L23/12C08J9/08C08J9/10C08J2203/02C08J2203/04C08J2205/044C08J2323/12C08J2423/06C08K2201/011C08K2201/014C08L2203/14C08L2205/025C08L2205/035C08L2205/24C08L23/06C08K13/06C08K9/02C08K9/04C08K7/06C08K2003/2296C08K5/098C08K3/34C08K2003/265
Inventor 不公告发明人
Owner GUANGZHOU JUZHU GENERAL TECH INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap