Epoxy resin based high-adhesion butyl acrylate sealant for storage batteries and manufacturing method of epoxy resin based high-adhesion butyl acrylate sealant

A technology of butyl acrylate and epoxy resin, applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of damage to the battery shell and high bonding strength, and achieve increased curing speed and The effect of bonding efficiency

Inactive Publication Date: 2016-09-28
哈尔滨永淇化工有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003]With the increasing market demand for batteries year by year, more and more attention has been paid to the disposal of used batteries and the maintenance of batteries, and the key to battery maintenance is to open the sealing cover Can not damage the battery shell, if some existing sealants have high bonding strength, the battery shell will be damaged because the sealant is difficult to peel off when the sealing cover is opened, and the high bonding strength that is easy to peel off is relatively low, how to ensure Good bonding strength and no damage to the battery casing when the sealing cover is opened is a difficult problem to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy resin based high-adhesion butyl acrylate sealant for storage batteries and manufacturing method of epoxy resin based high-adhesion butyl acrylate sealant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of butyl acrylate strong viscous battery sealant based on epoxy resin, it is characterized in that: comprising A components and B components; the A components by N- β-hydroxyethylethylenediamine, PVC- Polyvinyl chloride, benzoyl peroxide, chlorosulfonated polyethylene; B Components are made of epoxy resin, butyl acrylate, neoprene, Nickel acetylacetonate , dioctyl phthalate, defoamer, paraffin composition; where the A Components include: 15-25 of N- β-hydroxyethylethylenediamine, 15-25 of PVC- PVC, 2-6 parts of benzoyl peroxide, 10-25 Parts of chlorosulfonated polyethylene composition; the B Components include: 60-80 part epoxy resin, 10-20 parts of butyl acrylate, 5-15 parts neoprene, 3-15 of Nickel acetylacetonate ， 10-25 parts of dioctyl phthalate, 10-15 parts of defoamer, 0.1-5 parts of paraffin.

[0018] said A Components include: 20 of N- β-hydroxyethylethylenediamine, 20 o...

Embodiment 2

[0026] A kind of butyl acrylate strong viscous battery sealant based on epoxy resin, it is characterized in that: comprising A components and B components; the A components by N- β-hydroxyethylethylenediamine, PVC- Polyvinyl chloride, benzoyl peroxide, chlorosulfonated polyethylene; B Components are made of epoxy resin, butyl acrylate, neoprene, Nickel acetylacetonate , dioctyl phthalate, defoamer, paraffin composition; where the A Components include: 15-25 of N- β-hydroxyethylethylenediamine, 15-25 of PVC- PVC, 2-6 parts of benzoyl peroxide, 10-25 Parts of chlorosulfonated polyethylene composition; the B Components include: 60-80 part epoxy resin, 10-20 parts of butyl acrylate, 5-15 parts neoprene, 3-15 of Nickel acetylacetonate ， 10-25 parts of dioctyl phthalate, 10-15 parts of defoamer, 0.1-5 parts of paraffin.

[0027] said A Components at temperature 36-66 ℃， 10pa Mixing under air pressure, B Components at tempera...

Embodiment 3

[0032] The preferred version of the present invention is: said A Components include: 20 of N- β-hydroxyethylethylenediamine, 20 of PVC- PVC, 4 parts of benzoyl peroxide, 15 Parts of chlorosulfonated polyethylene composition; the B Components include: 70 part epoxy resin, 15 parts of butyl acrylate, 10 parts neoprene, 8 of Nickel acetylacetonate ， 15 parts of dioctyl phthalate, 12 parts of defoamer, 3 parts of paraffin.

[0033] A Components at temperature 40 ℃ ， B Components at temperature 45 ℃ ， 10pa Under air pressure conditions, respectively Will A components, B The raw materials in the components are mixed evenly according to the ratio and then put aside for packaging. When using, directly put A components, B After the components are evenly mixed according to the weight ratio, the potting operation can be carried out.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an epoxy resin based high-adhesion butyl acrylate sealant for storage batteries and a manufacturing method of the epoxy resin based high-adhesion butyl acrylate sealant. The epoxy resin based high-adhesion butyl acrylate sealant comprises a component A and a component B; the component A comprises N-beta hydroxyethylenediamine, PVC (polyvinyl chloride), benzoyl peroxide and chlorosulfonated polyethylene; the component B comprises epoxy resin, butyl acrylate, chloroprene rubber, nickel acetylacetonate, dioctyl phthalate, an antifoaming agent and paraffin. Curing speed and adhesion efficiency of the sealant are increased through heat generated in use of the sealant, and heat resistance, acid resistance and adhesion performance of the sealant are superior to those of other types of sealants for the storage batteries. In addition, strict control of proportion in mixing of the two components is not required, heat curing is avoided, and accordingly storage battery production process is simplified, and storage battery production cost is reduced.

Description

technical field [0001] The invention relates to the technical field of chemical industry, in particular to an epoxy resin-based butyl acrylate strong viscous battery sealant and a production method for sealing batteries. Background technique [0002] With the rapid development of China's battery industry, the performance of the battery sealant, which is directly related to the quality of the battery, has attracted more and more attention from experts in the industry and various industries at home and abroad. The main components of sealing adhesives widely used in the battery industry are Amine or modified amine-cured epoxy system or polyurethane system adhesives, epoxy system adhesives require a long curing time at room temperature, sometimes even heat curing, and are relatively brittle, so this system is used as lead The sealing materials for poles and tank covers of acid batteries are still unsatisfactory; polyurethane adhesives can meet the requirements of lead-acid batte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/06C09J4/02C09J11/06C09J11/08
CPCC09J4/06C09J11/06C09J11/08C08F283/10
Inventor 刘振亭
Owner 哈尔滨永淇化工有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com