Sound-insulation bamboo-plastic foaming composite door and window material capable of removing formaldehyde and preparation method thereof

A technology for bamboo-plastic and doors and windows is applied in the field of bamboo-plastic foamed composite door and window materials and their preparation, which can solve the problems of restricting the application of bamboo-plastic foaming composite materials, the mechanical strength needs to be improved, the functionalization of composite materials is not perfect, and the like. Formaldehyde adsorption efficiency, increasing formaldehyde adsorption efficiency, improving affinity and fluidity

Inactive Publication Date: 2016-10-12
安徽三乐节能科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In "The Effect of Titanate Coupling Agent on the Properties of Bamboo-plastic Foamed Composite Materials", Zhou Xingxing prepared a bamboo-plastic foamed composite material by using bamboo powder, polypropylene, and high-melt strength polypropylene, but its The mechanical strength needs to be improved, and the functionalization of the composite material is not perfect enough, which limits the application of bamboo-plastic foam composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0016] A sound-insulating and formaldehyde-removable bamboo-plastic foam composite door and window material is characterized in that it is made of the following raw materials in parts by weight:

[0017] Tencel fiber 2, isotactic polypropylene 70, polyester fiber 2, high melt strength polypropylene 15, bamboo powder 40, activated carbon 15, polypropylene fiber 2, corundum powder 2, Cu(NO 3 ) 2 25, stearic acid 3, calcium stearate 3, foaming agent AC1601 3, zinc stearate 15, NaOH solution 60, polyacrylate emulsion 3;

[0018] The particle diameter of described bamboo powder is 90-350 μ m, and NaOH solution concentration is 1mol / L, and Cu(NO 3 ) 2 The concentration is 0.1 mol / L, and the solid content of the polyacrylate emulsion is 40-50%.

[0019] The preparation method of a kind of sound insulation and formaldehyde-removable bamboo-plastic foam composite door and window material is characterized in that it is made by the following steps:

[0020] a. Add activated carbon a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
bending strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a sound-insulation bamboo-plastic foaming composite door and window material capable of removing formaldehyde and a preparation method thereof. The sound-insulation bamboo-plastic foaming composite door and window material is characterized by being prepared from, by weight, 1-2 parts of tencel fibers, 60-70 parts of isotactic polypropylene, 1-2 parts of polyester fibers, 10-15 parts of high-melt-strength polypropylene, 30-40 parts of bamboo powder, 10-15 parts of activated carbon, 1-2 parts of polypropylene fibers, 1-2 parts of corundum powder, 20-25 parts of Cu(NO3)2, 1-3 parts of stearic acid, 1-3 parts of calcium stearate, 1-3 parts of foaming agent AC1601, 10-15 parts of zinc stearate, 50-60 parts of a NaOH solution and 1-3 parts of polyacrylate emulsion. The activated carbon and the diamond are modified with polyacrylate and the Cu(NO3)2, and supporting of the Cu(NO3)2 in surfaces and pore channels of the activated carbon and the diamond is promoted. Due to the fact that the cooperative tencel fibers and the like are added, the sound-insulation properties are endowed to the composite material.

Description

technical field [0001] The invention relates to a bamboo-plastic composite material, in particular to a sound-insulating and formaldehyde-removable bamboo-plastic foam composite door and window material and a preparation method thereof. Background technique [0002] Bamboo-plastic foam composites have attracted much attention recently because they can overcome the defects of high density and brittleness of bamboo-plastic composites. Bamboo-plastic composite materials mainly include polyvinyl chloride and polyolefin plastics. Polyvinyl chloride-based composite materials will pollute the environment during manufacture, use and disposal. Polyvinyl chloride-based composite materials have low rigidity and maximum service temperature, and are not easy to degrade. Therefore, polypropylene (PP) wood-plastic foam composites have become a recent research hotspot. Bamboo-plastic foam composite materials have a wide range of applications, involving the automobile industry and transpor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L97/02C08L67/02C08K13/06C08K9/04C08K9/02C08K3/04C08K3/22C08J9/10
CPCC08L23/12C08J9/103C08J2203/04C08J2323/12C08J2423/12C08K2201/014C08L2203/14C08L2205/025C08L2205/035C08L2205/16
Inventor 陈学军吴珍梅徐琼琼曹蕾沈中
Owner 安徽三乐节能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products