Cold resistant anti-impact modified polypropylene and preparation method thereof

A cold-resistant and impact-resistant polypropylene technology, applied in the field of plastics, to achieve the effects of improved impact toughness and molding shrinkage, excellent comprehensive performance, and improved low-temperature resistance

Inactive Publication Date: 2016-11-09
SUZHOU HAOSHUN PLASTIC RUBBER CO LTD
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The main technical problem to be solved by the present invention is to provide a cold-resistant and impact-resistant modified polypropylene and its preparation method, which can solve the above-mentioned shortcomings existing in existing polypropylene plastics and meet the requirements of the industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A cold-resistant and impact-resistant modified polypropylene, which is jointly toughened and modified by an organic modifier and an inorganic mineral modifier, and also improves its low-temperature resistance; specifically, it includes the following raw materials in parts by weight:

[0023] 70 parts of polypropylene (PP), 15 parts of ethylene / octene copolymer (POE), 10 parts of styrene / butadiene / styrene copolymer (SBS), 20 parts of mineral additives, 10 parts of silane coupling agent, anti 1 part of oxygen agent 1010, 5 parts of sodium dodecylbenzenesulfonate; wherein, the mineral additive is a mixture of modified silica fume, talcum powder and calcium carbonate in a mass ratio of 2:1:2.

[0024] The preparation method of the above-mentioned cold-resistant and impact-resistant modified polypropylene, the specific steps are as follows:

[0025] (1) Preparation of modified micro-silica powder: Take an appropriate amount of micro-silica powder and place it in a box-type r...

Embodiment 2

[0033] A cold-resistant and impact-resistant modified polypropylene, which is jointly toughened and modified by an organic modifier and an inorganic mineral modifier, and also improves its low-temperature resistance; specifically, it includes the following raw materials in parts by weight:

[0034] 80 parts of polypropylene, 10 parts of ethylene / octene copolymer, 10 parts of styrene / butadiene / styrene copolymer, 30 parts of mineral additives, 15 parts of silane coupling agent, 3 parts of antioxidant 1010, dodecane 8 parts of sodium base benzene sulfonate; Wherein, described mineral additive is the mixture that modified microsilica powder, talcum powder and calcium carbonate mix with the mass ratio of 3:1:2.

[0035] The preparation method of the above-mentioned cold-resistant and impact-resistant modified polypropylene, the specific steps are as follows:

[0036] (1) Preparation of modified micro-silica powder: Take an appropriate amount of micro-silica powder and place it in a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cold resistant anti-impact modified polypropylene (PP) and a preparation method thereof. The cold resistant anti-impact modified polypropylene comprises the following raw materials by weight: 70-80 parts of PP, 10-15 parts of POE, 5-10 parts of SBS, 20-30 parts of a mineral additive, 10-15 parts of a silane coupling agent, 1-3 parts of an antioxidant, and 5-8 parts of a dispersant. Compared with pure PP, the modified PP has tensile strength improved by 15-25%, impact strength increased by 35-45%, and molding shrinkage decreased by more than 80%. The invention uses POE, SBS, mineral raw materials and other modifiers to conduct blending modification on PP, effectively improves the low temperature resistance of PP, and endows a modified polypropylene composite material with excellent impact resistance, rigidity, aging resistance and cold resistance. Modified polypropylene can meet the impact strength requirement of automobile bumpers, can be widely applied to processing of automobile bumpers, instrument panels, body-building racks and other parts with low temperature resistance, and has excellent comprehensive performance.

Description

technical field [0001] The invention relates to the field of plastics, in particular to a cold-resistant and impact-resistant modified polypropylene and a preparation method thereof. Background technique [0002] Polypropylene (PP) is rich in sources, low in price, easy to form and process, and has excellent comprehensive performance. It has been widely used in chemical, construction, electric power, automobile, machinery, textile, medical, packaging, building materials, furniture and other industries. In addition, polypropylene is also the main raw material for the preparation of fitness equipment. However, the low-temperature resistance of polypropylene material is insufficient, and there are disadvantages such as easy embrittlement at low temperature, poor impact resistance, and low dimensional stability of the product, which cannot meet the performance of the product. Contents of the invention [0003] The main technical problem to be solved by the present invention i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L23/08C08L53/02C08K13/06C08K9/06C08K9/04C08K3/36C08K3/34C08K3/26C08K5/134
CPCC08L23/12C08L2205/02C08L2205/03C08L23/0815C08L53/02C08K13/06C08K9/06C08K9/04C08K3/36C08K3/34C08K2003/265C08K5/1345
Inventor 邹晓明
Owner SUZHOU HAOSHUN PLASTIC RUBBER CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com